Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)

Journal of Solid State Electrochemistry

Volumn 13, Issue 7, 2009, Pages 1091-1099

  Elboujdaini, M ^a   Revie, R W ^a  

^a NATURAL RESOURCES CANADA   (Canada)

Author keywords

Hydrogen induced cracking (HIC); Metallurgical factors; Nonmetallic inclusions; Stress corrosion cracking (SCC)

Indexed keywords

ACID CORROSIONS; ANODIC REACTIONS; ATOM SOURCES; CATHODIC REACTIONS; EXTERNAL SURFACES; HYDROGEN IONS; HYDROGEN-INDUCED CRACKING (HIC); INHOMOGENEITIES; INTERNAL DELAMINATIONS; LINE PIPE STEELS; LOCALIZED CORROSIONS; METALLURGICAL FACTORS; NONMETALLIC INCLUSIONS; PIPE SURFACES; PITTING CORROSIONS; STRESS CORROSION CRACKING (SCC); STRESS-CORROSION CRACKS;

ATOMS; CORROSION RESISTANCE; CRACK DETECTION; CRACKING (CHEMICAL); DEFECTS; HYDROGEN; INCLUSIONS; METALLURGY; PIPE; PIPELINES; PITTING; RESIDUAL STRESSES; STEEL; SURFACES;

STRESS CORROSION CRACKING;

EID: 67349211202     PISSN: 14328488     EISSN: None     Source Type: Journal    
DOI: 10.1007/s10008-009-0799-0     Document Type: Article

References (26)

1. National Energy Board, Calgary, Alberta, Stress Corrosion Cracking on Canadian Oil and Gas Pipelines, Report No. MH-2-95, 1996
2. JM Sutcliffe RR Fessler WK Boyd RN Parkins 1972 Stress corrosion cracking of carbon steel in carbonate solutions Corrosion 28 313 (Pubitemid 18561530)
3. Beavers JA, Harle BA (1996) Mechanisms of high-pH and near-neutral-pH SCC of underground pipelines. ASME International Pipeline Conference, Calgary, Alberta, June
4. EA Charles RN Parkins 1995 Generation of stress corrosion cracking environments at pipeline surfaces Corrosion 51 518
5. RN Parkins WK Blanchard BS Delanty 1994 Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near-neutral-pH Corrosion 50 394 (Pubitemid 289929)
6. BS Delanty JO Beirne 1992 Major field study compares pipeline SCC with coatings Oil Gas J 90 39
7. Wang Y-Z, Revie RW, Shehata MT, Parkins RN (1998) Early stages of stress corrosion crack development of X-65 pipeline steel in near-neutral pH solution, materials for resource recovery and transport. Metallurgical Society of CIM 1998, 71
8. Beavers JA, Johnson JT (1998) Annual Report on Effects of Pressure Fluctuations on SCC Propagation", Prepared for Line Pipe Research Supervisory Committee of PRC International, CC Technologies, Dublin, Ohio, May 1999
9. RN Parkins 1988 Mater Sci Eng A 103 143
10. TK Christman 1990 Corrosion 46 450
11. JM Silcock 1982 Corrosion 38 144
12. BF Brown CD Beachem 1965 Corros Sci 5 745
13. M Yasuda F Weinberg D Tromans 1990 J Electrochem Soc 137 12
14. Issacs HS, Newman RC (1987) Local electrochemistry of pitting corrosion in stainless steels. Corrosion chemistry within pits, crevices, and cracks. HMSO, London
15. Dolphin AS, Turnbull A (1987) Experimental determination of the electrochemistry in corrosion-fatigue cracks in structural steel in marine environments. Corrosion chemistry within pits, crevices, and cracks. HMSO, London
16. Jonas O (1997) Molecular modeling of corrosive environments in cracks. Effects of the environment on the initiation of crack growth: ASTM STP 1298. ASTM, Philadelphia
17. RN Parkins 1984 Metals Technol 9 122
18. RN Parkins 1985 Mater Sci Technol 1 480
19. Elboujdaini M, Wang Y-Z, Revie RW, Shehata M, de Silveira G, Parkins RN (2001) Initiation of stress corrosion cracking in pipeline steel. GRI report no. GRI 05-0005
20. Elboujdaini M, Li J, Gertsman V, Gu G, Revie W, Gao M, Katz DC (2004) Stress corrosion cracking: microstructural and material properties for crack initiation of 16" X-52 line pipe steel. Corrosion 2004, Paper 04553, NACE, Houston, TX
21. Parkins RN, Delanty BS (1996) The initiation and early stages of growth of stress corrosion cracks in pipeline steels exposed to a dilute, near neutral pH Solution. Ninth Symposium on Pipeline Research, AGA Catalog No. L 51746, pp. 19-1 to 9-14
22. Elboujdaini M, Wang Y-Z, Revie RW, Parkins RN, Shehata MT (2000) Stress corrosion crack initiation processes: pitting and microcrack coalescence. Corrosion 2000, Paper 00379, NACE, Houston, TX
23. W Chen F King E Vokes 2002 Characteristics of near-neutral pH stress corrosion cracks in an X-65 pipeline Corrosion 58 267 (Pubitemid 34294809)
24. Elboujdaini M, Shehata MT, Revie RW (1998) Performance of pipeline steels in sour service. Proc. 37th Int Symp Materials for Resource Recovery and Transport, Conf of Metallurgists, CIM, Calgary, August
25. Standard Test Method TM-0284 - Test Method Evaluation of Pipeline Steels for Resistance to Stepwise Cracking - NACE International, Houston, TX, 1996
26. RA Oriani PH Josephic 1980 Met Trans A 11 1809