Volumn 46, Issue 13, 2009, Pages 2659-2668

Nonlinear interface shear fracture of end notched flexure specimens

Author keywords

Analytical solution; Arbitrary nonlinear cohesive laws; Bonded joint; Cohesive zone model (CZM); Composites; ENF; Interface shear fracture; Mode II

Indexed keywords

ANALYTICAL SOLUTION; ARBITRARY NONLINEAR COHESIVE LAWS; BONDED JOINT; COHESIVE ZONE MODEL (CZM); COMPOSITES; ENF; INTERFACE SHEAR FRACTURE; MODE II;

EID: 63349088668     PISSN: 00207683     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijsolstr.2009.02.011     Document Type: Article
Times cited : (65)

References (29)
  • 1
    • 0018432859 scopus 로고
    • Stress singularities and fracture mechanics
    • Atkinson C. Stress singularities and fracture mechanics. Applied Mechanics Review 32 2 (1979) 123-135
    • (1979) Applied Mechanics Review , vol.32 , Issue.2 , pp. 123-135
    • Atkinson, C.1
  • 3
    • 0009231269 scopus 로고
    • The formation of equilibrium cracks during brittle fracture. General ideas and hypothesis. Axisymmetrical cracks
    • English Translation
    • Barenblatt G.I. The formation of equilibrium cracks during brittle fracture. General ideas and hypothesis. Axisymmetrical cracks. Journal of Applied Mathematics and Mechanics (PMM) 23 3 (1959) 622-636 English Translation
    • (1959) Journal of Applied Mathematics and Mechanics (PMM) , vol.23 , Issue.3 , pp. 622-636
    • Barenblatt, G.I.1
  • 4
    • 0038500752 scopus 로고    scopus 로고
    • The use of a cohesive zone model to study the fracture of fibre composites and adhesively-bonded joints
    • Blackman B.R.K., Hadavinia H., Kinloch A.J., and Williams J.G. The use of a cohesive zone model to study the fracture of fibre composites and adhesively-bonded joints. International Journal of Fracture 119 (2003) 25-46
    • (2003) International Journal of Fracture , vol.119 , pp. 25-46
    • Blackman, B.R.K.1    Hadavinia, H.2    Kinloch, A.J.3    Williams, J.G.4
  • 6
    • 0342803672 scopus 로고    scopus 로고
    • Experimental aspects of mode I and mode II fracture toughness testing of fibre-reinforced polymer-matrix composites
    • Brunner A.J. Experimental aspects of mode I and mode II fracture toughness testing of fibre-reinforced polymer-matrix composites. Computer Methods in Applied Mechanics and Engineering 185 (2000) 161-172
    • (2000) Computer Methods in Applied Mechanics and Engineering , vol.185 , pp. 161-172
    • Brunner, A.J.1
  • 9
    • 0022810345 scopus 로고
    • On the analysis and design of the end notched flexure (ENF) specimen for mode II testing
    • Carlsson L.A., Gillespie J.W., and Pipes R.B. On the analysis and design of the end notched flexure (ENF) specimen for mode II testing. Journal of Composite Materials 20 (1986) 594-604
    • (1986) Journal of Composite Materials , vol.20 , pp. 594-604
    • Carlsson, L.A.1    Gillespie, J.W.2    Pipes, R.B.3
  • 10
    • 27144475407 scopus 로고    scopus 로고
    • Effects of friction, geometry and fixture compliance on the perceived toughness from three and four point bended notched flexure tests
    • Davidson B.D., and Sun X. Effects of friction, geometry and fixture compliance on the perceived toughness from three and four point bended notched flexure tests. Journal of Reinforced Plastic Composites 4 15 (2005) 1611-1628
    • (2005) Journal of Reinforced Plastic Composites , vol.4 , Issue.15 , pp. 1611-1628
    • Davidson, B.D.1    Sun, X.2
  • 11
    • 34248639858 scopus 로고    scopus 로고
    • Influences of friction, geometric nonlinearities, and fixture compliance on experimentally observed toughnesses from three and four-point bend end-notched flexure tests
    • Davidson B.D., Sun X., and Vinciquerra A. Influences of friction, geometric nonlinearities, and fixture compliance on experimentally observed toughnesses from three and four-point bend end-notched flexure tests. Journal of Composite Materials 41 10 (2007) 1177-1196
    • (2007) Journal of Composite Materials , vol.41 , Issue.10 , pp. 1177-1196
    • Davidson, B.D.1    Sun, X.2    Vinciquerra, A.3
  • 14
    • 0032311897 scopus 로고    scopus 로고
    • The impact-induced delamination of laminated composites: a 2D simulation
    • Geubelle P.H., and Baylor J.S. The impact-induced delamination of laminated composites: a 2D simulation. Composites Part B: Engineering 29 (1998) 589-602
    • (1998) Composites Part B: Engineering , vol.29 , pp. 589-602
    • Geubelle, P.H.1    Baylor, J.S.2
  • 15
    • 0004725612 scopus 로고
    • Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements
    • Hillerborg A., Modéer M., and Petersson P.E. Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements. Cement and Concrete Research 6 (1976) 773-782
    • (1976) Cement and Concrete Research , vol.6 , pp. 773-782
    • Hillerborg, A.1    Modéer, M.2    Petersson, P.E.3
  • 16
    • 0033875372 scopus 로고    scopus 로고
    • Mechanics of materials: top-down approaches to fracture
    • Hutchinson J.W., and Evans A.G. Mechanics of materials: top-down approaches to fracture. Acta Materialia 48 (2000) 125-135
    • (2000) Acta Materialia , vol.48 , pp. 125-135
    • Hutchinson, J.W.1    Evans, A.G.2
  • 18
    • 0023410904 scopus 로고
    • A continuum model for void nucleation by inclusion debonding
    • Needleman A. A continuum model for void nucleation by inclusion debonding. ASME Journal of Applied Mechanics 54 (1987) 525-531
    • (1987) ASME Journal of Applied Mechanics , vol.54 , pp. 525-531
    • Needleman, A.1
  • 20
    • 65349178501 scopus 로고    scopus 로고
    • Local damage evolution of DCB specimens during crack initiation process: A natural boundary condition based method
    • in press
    • Ouyang, Z., Li, G., in press. Local damage evolution of DCB specimens during crack initiation process: a natural boundary condition based method. ASME Journal of Applied Mechanics.
    • ASME Journal of Applied Mechanics
    • Ouyang, Z.1    Li, G.2
  • 21
    • 58249141762 scopus 로고    scopus 로고
    • Cohesive zone model based analytical solutions for adhesively bonded pipe joints under torsional loading
    • Ouyang Z., and Li G. Cohesive zone model based analytical solutions for adhesively bonded pipe joints under torsional loading. International Journal of Solids and Structures 46 5 (2009) 1205-1217
    • (2009) International Journal of Solids and Structures , vol.46 , Issue.5 , pp. 1205-1217
    • Ouyang, Z.1    Li, G.2
  • 22
  • 23
    • 65349143992 scopus 로고    scopus 로고
    • Russell, A.J., Street, K.N. 1982. Factors affecting the interlaminar fracture energy of graphite/epoxy laminates. In: ICCM-IV, Tokyo, Japan, 1982.
    • Russell, A.J., Street, K.N. 1982. Factors affecting the interlaminar fracture energy of graphite/epoxy laminates. In: ICCM-IV, Tokyo, Japan, 1982.
  • 24
    • 0012242835 scopus 로고
    • Materials Report 82-0, Defence Research, Establishment Pacific, Victoria, British Columbia, Canada
    • Russell, A.J., 1982. On the measurement of mode II interlaminar fracture energies. Materials Report 82-0, Defence Research, Establishment Pacific, Victoria, British Columbia, Canada.
    • (1982) On the measurement of mode II interlaminar fracture energies
    • Russell, A.J.1
  • 25
    • 0034250054 scopus 로고    scopus 로고
    • Evaluation of the accuracy of the four-point bend end-notched flexure test for the mode II delamination toughness determination
    • Schuecker C., and Davidson B.D. Evaluation of the accuracy of the four-point bend end-notched flexure test for the mode II delamination toughness determination. Composite Science and Technology 60 (2000) 2137-2146
    • (2000) Composite Science and Technology , vol.60 , pp. 2137-2146
    • Schuecker, C.1    Davidson, B.D.2
  • 26
    • 0025449007 scopus 로고
    • Effect of fibre debonding in a whisker-reinforced metal
    • Tvergaard V. Effect of fibre debonding in a whisker-reinforced metal. Materials Science and Engineering A 125 (1990) 203-213
    • (1990) Materials Science and Engineering A , vol.125 , pp. 203-213
    • Tvergaard, V.1
  • 27
    • 44049109778 scopus 로고
    • The relation between crack growth resistance and fracture process parameters in elastic-plastic solids
    • Tvergaard V., and Hutchinson J.W. The relation between crack growth resistance and fracture process parameters in elastic-plastic solids. Journal of the Mechanics and Physics of Solids 40 (1992) 1377-1397
    • (1992) Journal of the Mechanics and Physics of Solids , vol.40 , pp. 1377-1397
    • Tvergaard, V.1    Hutchinson, J.W.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.