The determination of the mode II adhesive fracture resistance, GIIC, of structural adhesive joints: An effective crack length approach

Engineering Fracture Mechanics

Volumn 72, Issue 6 SPEC. ISS., 2005, Pages 877-897

  Blackman, B R K ^a   Kinloch, A J ^a   Paraschi, M ^a  

^a IMPERIAL COLLEGE LONDON   (United Kingdom)

Author keywords

Adhesive joints; Corrected beam theory; Effective crack length; End loaded split test; Fracture mechanics; Microcracking; Mode II

Indexed keywords

ADHESION; BONDING; COMPOSITE MATERIALS; CRACK PROPAGATION; EPOXY RESINS; MICROCRACKS; SUBSTRATES;

BEAM THEORY ANALYSES; CRACK LENGTH; END-LOADED SPLIT (ELS); FRACTURE RESISTANCE;

JOINTS (STRUCTURAL COMPONENTS);

FRACTURE MECHANICS;

EID: 11044229008     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2004.08.007     Document Type: Article

References (24)

1. IC, of structural adhesive joints: The results of an International round-robin Int. J. Adhes. Adhes. 23 2003 293-305
2. IC, of structural adhesives using the double cantilever beam (DCB) and tapered double cantilever beam (TDCB) specimens; 2001. BS 7991
3. A.J. Kinloch Adhesion & adhesives: Science & technology 1987 Chapman Hall London & New York p. 441
4. R.H. Martin B.D. Davidson Mode II fracture toughness evaluation using four point bend, end notched flexure test Plastics Rubber Compos. 28 8 1999 401-406
5. P. Qiao J. Wang J.F. Davalos Analysis of tapered ENF specimen and characterization of bonded interface fracture under Mode II loading Int. J. Solids Struct. 40 2003 1865-1884
6. F.C. Edde Y. Verreman Nominally constant strain energy release rate specimen for the study of mode II fracture and fatigue in adhesively bonded joints Int. J. Adhes. Adhes. 15 1995 29-32
7. P. Davies et al. Comparison of test configurations for determination of mode II interlaminar fracture toughness results from international collaborative test programme Plastics Rubber Compos. 28 9 1999 432-437
8. L.A. Carlsson J.W. Gillespie R.B. Pipes On the analysis and design of the end notched flexure (ENF) specimen form mode II testing J. Compos. Mater. 20 1986 594-604
9. Russel AJ, Street KN. Factors affecting the interlaminar fracture energy of graphite/epoxy laminates. In: ICCM-IV, Tokyo, Japan, 1982
10. G. Fernlund J.K. Spelt Mixed-mode fracture characterisation of adhesive joints Compos. Sci. Technol. 50 1994 441-449
11. C. Schuecker B.D. Davidson Effect of friction on the perceived mode II delamination toughness from three and four point bend end-notched flexure tests P. Grant C.Q. Rousseau Composites structures: Theory and practice 2000 American Society of Testing and Materials West Conshohocken 334-344
12. C. Schuecker B.D. Davidson Evaluation of the accuracy of the four-point bend end-notched flexure test for the mode II delamination toughness determination Compos. Sci. Technol. 60 2000 2137-2146
13. P. Davies Influence of ENF specimen geometry and friction on the mode II delamination resistance of cardon/PEEK J. Thermoplast. Compos. Mater. 10 1997 353-361
14. B.R.K. Blackman J.G. Williams On the mode II testing of carbon-fibre polymer composites ECF12 fracture from defects 1998 EMAS Publishing Sheffield, UK
15. A.J. Brunner Experimental aspects of mode I and mode II fracture toughness testing of fibre-reinforced polymer-matrix composites Comput. Methods Appl. Mech. Eng. 185 2000 161-172
16. IC delamination tests on fibre composites. Compos Sci Technol, accepted for publication 2005
17. IC tests on fibre composites Fracture of polymers, composites and adhesives II 2002 Elsevier Science Ltd Les Diablerets, Switzerland
18. S. Hashemi A.J. Kinloch J.G. Williams The analysis of interlaminar fracture in uniaxial fibre-polymer composites Proc. R. Soc. London A427 1990 173-199
19. Y. Wang J.G. Williams Corrections for mode II fracture toughness specimens of composite materials Compos. Sci. Technol. 43 1992 251-256
20. P. Davies B.R.K. Blackman A.J. Brunner Mode II delamination D.R. Moore A. Pavan J.G. Williams Fracture mechanics testing methods for polymers adhesives and composites 2001 Elsevier Amsterdam, London, New York 307-334
21. Paraschi M. A fracture mechanics approach to the failure of adhesive joints. Department of Mechanical Engineering, Imperial College, University of London, London 2002
22. ASTM, Determination of flexural properties of plastics and reinforced plastics, 1990
23. IIC: Shear measurement or sheer myth? In: Composite materials: Fatigue and fracture, 1998. p. 3-18
24. S.M. Lee Mode II delamination failure mechanisms of polymer matrix composites J. Mater. Sci. 32 1997 1287-1295