Volumn , Issue , 2007, Pages 281-287

Effects of shot peening treatment on very high cycle fatigue property in austempered ductile cast iron

Author keywords

Austempered ductile cast iron; Residual stress intemal fracture; Shot peening; Very high cycle fatigue

Indexed keywords

BENDING TESTS; DUCTILE FRACTURE; FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE; LIFE CYCLE; METAL CASTING; RESIDUAL STRESSES; SHOT PEENING; STRENGTH OF MATERIALS; STRESS CONCENTRATION; SURFACE TREATMENT; TENSILE STRENGTH;

EID: 58349109466     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper
Times cited : (3)

References (9)
  • 1
    • 0005486194 scopus 로고
    • Structure-property relationship in graphite cast iron
    • P.A.Blackmore and K.Morthon, "Structure-property relationship in graphite cast iron", Int. J. Fatigue, 4(1982), 149-155.
    • (1982) Int. J. Fatigue , vol.4 , pp. 149-155
    • Blackmore, P.A.1    Morthon, K.2
  • 2
    • 0023138996 scopus 로고
    • Comparison of fatigue properties of nodular cast iron production and Y-block castings
    • F.D.Grisword, Jr., R.I.Stephens, "Comparison of fatigue properties of nodular cast iron production and Y-block castings", Int. J. Fatigue, 9(1987), 3-10.
    • (1987) Int. J. Fatigue , vol.9 , pp. 3-10
    • Grisword Jr., F.D.1    Stephens, R.I.2
  • 3
    • 0032633680 scopus 로고    scopus 로고
    • Fatigue life assessment of nodular cast iron containing casting defects
    • Y.Nadot, et al., "Fatigue life assessment of nodular cast iron containing casting defects", Fatigue Fract. Engng. Mater. Struct., 22(1999), 289-300.
    • (1999) Fatigue Fract. Engng. Mater. Struct , vol.22 , pp. 289-300
    • Nadot, Y.1
  • 4
    • 0035342172 scopus 로고    scopus 로고
    • Effects of shot-peening treatment on high cycle fatigue property of ductile cast iron
    • Y.Ochi et al., "Effects of shot-peening treatment on high cycle fatigue property of ductile cast iron", Int. J. Fatigue, 23(2001), 441-448.
    • (2001) Int. J. Fatigue , vol.23 , pp. 441-448
    • Ochi, Y.1
  • 5
    • 0033177737 scopus 로고    scopus 로고
    • Gigacycle fatigue of ferrous alloys
    • Q.Y.Wang et al., "Gigacycle fatigue of ferrous alloys", Fatigue Fract. Engng. Mater. Struct., 22 (1999), 667-672.
    • (1999) Fatigue Fract. Engng. Mater. Struct , vol.22 , pp. 667-672
    • Wang, Q.Y.1
  • 6
    • 0005513325 scopus 로고
    • Fatigue behavior in very long life region of austempered sheroidal graphite ductile iron
    • 93
    • S.Doi et al., "Fatigue behavior in very long life region of austempered sheroidal graphite ductile iron", Proc. of the inter. Conf. on Mechanical Behavior of Ductile Cast iron(ICDI'93), 1(1993)91-92.
    • (1993) Proc. of the inter. Conf. on Mechanical Behavior of Ductile Cast iron(ICDI , Issue.1 , pp. 91-92
    • Doi, S.1
  • 7
    • 0032664906 scopus 로고    scopus 로고
    • Factors influencing the mechanism of superlong fatigue failure in steels
    • Y.Murakami, T.Nomoto and T.Ueda, "Factors influencing the mechanism of superlong fatigue failure in steels", Fatigue Fract. Engng. Mater. Struct., 22(1999), 581-590.
    • (1999) Fatigue Fract. Engng. Mater. Struct , vol.22 , pp. 581-590
    • Murakami, Y.1    Nomoto, T.2    Ueda, T.3
  • 8
    • 58349108006 scopus 로고    scopus 로고
    • Y.Ochi et al., Effects of micro-defects on high cycle fatigue property in ductile cast irons, Proc. of the 7th Fracture mechanics Symposium, 1 (1993) 31-358 (in Japanese).
    • Y.Ochi et al., Effects of micro-defects on high cycle fatigue property in ductile cast irons", Proc. of the 7th Fracture mechanics Symposium, 1 (1993) 31-358 (in Japanese).
  • 9
    • 0031249962 scopus 로고    scopus 로고
    • Y.Ochi et al., Initiation and propagation life distributions of fatigue cracks and the life evaluation in high cycle fatigue of ADI, J. of the Soc. Of Mater. Sci., Japan, 46 (1997), 1155-1160 (in Japanese).
    • Y.Ochi et al., "Initiation and propagation life distributions of fatigue cracks and the life evaluation in high cycle fatigue of ADI", J. of the Soc. Of Mater. Sci., Japan, 46 (1997), 1155-1160 (in Japanese).


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.