Effect of shot-peening treatment on high cycle fatigue property of ductile cast iron

International Journal of Fatigue

Volumn 23, Issue 5, 2001, Pages 441-448

  Ochi, Yasuo ^a   Masaki, Kiyotaka ^a   Matsumura, Takashi ^a   Sekino, Takeshi ^a  

^a UNIVERSITY OF ELECTRO COMMUNICATIONS   (Japan)

Author keywords

Ductile cast iron; Fracture origin; High cycle fatigue; Residual stress; Shot peening

Indexed keywords

BENDING (DEFORMATION); DUCTILITY; FATIGUE OF MATERIALS; RESIDUAL STRESSES; SHOT PEENING;

DUCTILE CAST IRON;

CAST IRON;

EID: 0035342172     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(00)00110-9     Document Type: Article

References (17)

1. Structure-property relationship in graphite cast iron
2. Comparison of fatigue properties of nodular cast iron production and Y-block castings
3. Fatigue life assessment of nodular cast iron containing cast iron containing casting defects
4. Effects of shot peening on fatigue strength of austempered ductile iron
5. Gigacycle fatigue of ferrous alloys
6. Fatigue behavior in very long life region of austempered spheroidal graphite ductile iron
7. Factors influencing the mechanism of superlong fatigue failure in steels
8. The effect of atmosphere on fatigue properties of high strength steel
9. Stepwise S-N diagrams and fish-eye failure in gigacycle fatigue
10. Effect of shot peening on residual stress and fatigue life of a spring steel
11. Effect of residual stress on fatigue strength on induction hardened nodular cast iron
12. Experimental evidence of duplex S-N characteristics in wide life region for high strength steels
13. Effect of shot-peening on suppression of scatter of fatigue strength in Ti-6Al-4V alloy
14. The fatigue limit and its elimination
15. Subsurface fatigue crack initiation behavior and S-N diagrams characteristic in high carbon-chromium steel
16. Initiation and propagation behaviors of surface fatigue cracks and their statistical properties in ferrite-base spheroidal graphite cast iron
17. Initiation and propagation behaviors of surface fatigue crack in pearlitic spheroidal graphite cast iron