The meaning of threshold fatigue in fibre metal laminates

International Journal of Fatigue

Volumn 31, Issue 2, 2009, Pages 213-222

  Alderliesten, René ^a   Rans, Calvin ^a  

^a Delft University of Technology   (Netherlands)

Author keywords

Delamination; Fatigue crack growth; Fatigue threshold; Fibre metal laminates; Glare

Indexed keywords

CRACKING (CHEMICAL); CRACKS; FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; LAMINATES;

CONSTANT AMPLITUDES; FATIGUE CRACK GROWTH; FATIGUE THRESHOLD; FIBRE METAL LAMINATES;

PAPER LAMINATES;

EID: 55949107305     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2008.09.008     Document Type: Article

References (52)

1. Schütz W.A. History of fatigue. Eng Fract Mech 54 2 (1996) 263-300
2. Paris P.C., Tada H., and Donald J.K. Service load fatigue damage-a historical perspective. Int J Fatigue 21 (1999) S35-S46
3. Irwin G.R. The stresses and strains near the tip of a crack traversing a plate. J Appl Mech ASME (1957)
4. Paris P.C., Gomez M.P., and Anderson W.E. A rational analytic theory of fatigue. Trend Eng 13 9 (1961)
5. Elber W. Fatigue crack closure. Eng Fract Mech (1970)
6. Elber W. The significance of crack closure. ASTM/STP 486 (1971)
7. Vasudevan A.K., Sadananda K., and Louat N. Two critical stress intensities for threshold fatigue crack propagation. Scripta Metall Mater 28 (1993) 65-70
8. Sadananda K., Vasudevan A.K., and Kang I.W. Effect of superimposed monotonic fracture modes on the ΔK and the Kmax parameters of fatigue crack propagation. Acta Materiala 51 (2003) 3399-3414
9. Sadananda K., and Vasudevan A.K. Multiple mechanisms controlling fatigue crack growth. Fatigue Fract Eng Mater Struct 26 (2003) 835-845
10. Sadananda K., and Vasudevan A.K. Crack tip driving forces and crack growth representation under fatigue. Int J Fatigue 26 (2004) 39-47
11. Lang M. A model for fatigue crack growth, part I: phenomenology. Fatigue Fract Eng Mater Struct 23 (2000) 587-601
12. Lang M.A. Model for fatigue crack growth, part II: modelling. Fatigue Fract Eng Mater Struct 23 (2000) 603-617
13. 0.5 driving force parameter for crack growth in aluminium alloys. Int J Fatigue 23 (2001) 733-740
14. Borrego L.P., Ferreira J.M., Pinho da Cruz J.M., and Costa J.M. Evaluation of overload effects on fatigue crack growth and closure. Eng Fract Mech 70 (2003) 1379-1397
15. eff estimation procedures on 6061-T6 and 2024-T3 aluminium alloys. Int J Fatigue 21 (1999) S47-S57
16. Schijve J. Fatigue of structures and materials (2001), Kluwer Academic Publishers, Dordrecht, The Netherlands
17. Vlot A. GLARE; History of the development of a new aircraft material (2001), Kluwer Academic Publishers, Dordrecht
18. Alderliesten R.C. On the available relevant approaches for fatigue crack propagation prediction in Glare. Int J Fatigue 29 (2007) 289-304
19. Marissen R. Fatigue crack growth in ARALL, a hybrid aluminium-aramid composite material, crack growth mechanisms and quantitative predictions of the crack growth rate, Ph D Thesis, Delft University of Technology; 1988.
20. Guo Y.J., and Wu X.R. A theoretical model for predicting fatigue crack growth rates in fibre-reinforced metal laminates. Fatigue Fract Eng Mater Struct 21 (1998) 1133-1145
21. Guo Y.J., and Wu X.R. Bridging stress distribution in center-cracked fibre reinforced metal laminates: modelling and experiment. Eng Fract Mech 63 (1999) 147-163
22. Alderliesten RC. Fatigue crack propagation and delamination growth in Glare, Ph D Thesis, Delft University of Technology; 2005.
23. Alderliesten R.C. Analytical prediction model for fatigue crack propagation and delamination growth in Glare. Int J Fatigue 29 4 (2007) 628-646
24. Plokker H.M., Alderliesten R.C., and Benedictus R. Crack closure in fibre metal laminates. Fatigue Fract Eng Mater Struct (2007)
25. Schijve J. Some formulas for the crack opening stress level. Memorandum M-368. Delft University of Technology: Delft; 1980.
26. Alderliesten R.C. Application of the energy release rate approach for delamination growth in Glare. Eng Fract Mech 73 6 (2006) 697-709
27. Schut JE, Alderliesten RC. Delamination growth rate at low and elevated temperatures in Glare. In: Proceedings of the 25th International Congress of the Aeronautical Sciences. Hamburg; 2006.
28. Daandels D. Search for (ΔK threshold of Glare. Preliminary thesis, Delft University of Technology 2003.
29. ASTM E647-95a. Standard test method for measurement of fatigue crack growth rates. Annual Book of ASTM Standards, American Society for Testing and Materials; 1995.
30. Newman Jr. J.C., Schneider J., Daniel A., and McKnight D. Compression pre-cracking to generate near threshold fatigue-crack-growth rates in two aluminium alloys. Int J Fatigue 27 (2005) 1432-1440
31. Forth S.C., Newman Jr. J.C., and Forman R.G. On generating fatigue crack growth thresholds. Int J Fatigue 25 (2003) 912-915
32. Donald J.K. Introducing the compliance ratio concept for determining effective stress intensity. Int J Fatigue 19 1 (1997) S191-S195
33. Bucci R, James MA, Sklyut H, Heinimann MB, Ball DL, Donald JK. Advances in testing and analytical simulation methodologies to support design and structural integrity assessment of large monolithic parts, SAE Paper No. 2006-01-3179, 2006 SAE Aerospace Manufacturing and automated fastening conference, De Congrès Pierre Baudis, Toulouse, France, September 12-14; 2006.
34. Ball DL. A proposed analytical approach for the incorporation of residual stresses in the design of large forged components. In: Proceedings of the Boeing 7th industry wide unitized structure technical interchange, Dallas, USA; 2005.
35. Newman JA. The effects of load ratio on threshold fatigue crack growth of aluminium alloys. Ph D Thesis, Faculty of the Virginia Polytechnic Institute and State University; 2000.
36. Halliday M.D., Cooper C., Poole P., and Bowen P. On predicting small fatigue crack growth and fatigue life from long crack data in 2024 aluminium alloy. Int J Fatigue 25 (2003) 709-718
37. Zhang X.P., Wang C.H., Yeb L., and Maib Y.-W. A study of the crack wake closure/opening behaviour of short fatigue cracks and its influence on crack growth. Mate Sci Eng A 406 (2005) 195-204
38. Chapetti M.D. Fatigue propagation threshold of short cracks under constant amplitude loading. Int J Fatigue 25 (2003) 1319-1326
39. de Koning AU, Analysis of the fatigue crack growth behaviour of "through the thickness" cracks in fibre metal laminates. Report NLR-CR-2000-575, National Aerospace Laboratory NLR; 2000 (restricted).
40. Bouwman VP, de Koning AU, Fatigue crack growth methodology of 'through the thickness' cracks in fibre metal laminates. Report NLR-CR-2003-032, National Aerospace Laboratory NLR; 2000 (restricted).
41. Vlot A., and Ingen J.W. Delamination resistance of post-stretched fibre metal laminates. J Comp Mater 32 19 (1998) 1784-1805
42. Alderliesten RC. The influence of temperature on the fatigue crack propagation behaviour of Glare - Test report. Report TD-R-02-016, Fibre Metal Laminates Centre of Competence; 2003.
43. Alderliesten RC, Woerden HJM. Load history effects during fatigue crack propagation in Glare. In: Proceedings of the 22nd Symposium of the International Committee on Aeronautical Fatigue, Lucerne Switzerland; 2003.
44. Schwarmann L. Handbuch struktur berechnung. Fundamentals and Methods for the Design and Evaluation of Aeronautical Structures. Aerospace Technical Handbook; 1989.
45. Homan JJ. Crack growth properties of thin aluminium sheets. Issue 2, Report B2V- 01-16, Delft University of Technology, Delft; 2002 (restricted).
46. Thibault-Liboiron K, Alderliesten RC, Benedictus R, Bocher Ph. Off-axis crack propagation and delamination growth in FML's. 6th Canadian-international composites conference, Winnipeg, Manitoba, Canada, August 14-17; 2007.
47. Alderliesten R.C., Campoli G., and Benedictus R. Modelling cyclic shear deformation of fibre/epoxy layers in fibre metal laminates. Comp Sci Technol 67 11-12 (2007) 2545-2555
48. Stanzl S.E. The influence of air humidity on near-threshold fatigue crack growth of 2024-T3 aluminium alloy. Mater Sci Eng A147 (1991) 45-54
49. Newman Jr. JC. Analyses of fatigue crack growth and closure near threshold conditions for large-crack behavior. NASA report NASA/TM-1999-209133; 1999.
50. Newman JA. The effects of load ratio on threshold fatigue crack growth of aluminium alloys. Ph D thesis, Faculty of the Virginia Polytechnic Institute and State University; 2000.
51. Holper B., Mayer H., Vasudevan A.K., and Stanzl-Tschegg S.E. Near threshold fatigue crack growth in aluminium alloys at low and ultrasonic frequency: influences of specimen thickness, strain rate, slip behaviour and air humidity. Int J Fatigue 25 (2003) 397-411
52. Holper B., Mayer H., Vasudevan A.K., and Stanzl-Tschegg S.E. Near threshold fatigue crack growth at positive load ratio in aluminium alloys at low and ultrasonic frequency: influences of strain rate slip behaviour and air humidity. Int J Fatigue 26 (2004) 27-38