Effect of simulated groundwater chemistry on stress corrosion cracking of alloy 22

Corrosion

Volumn 63, Issue 10, 2007, Pages 940-950

  Chiang, K T ^a   Dunn, D S ^a   Cragnolino, G A ^a  

^a SOUTHWEST RESEARCH INSTITUTE   (United States)

Author keywords

Alloy 22; Simulated concentrated water; Slow strain rate test; Stress corrosion cracking

Indexed keywords

CORROSION; CRACKS; GROUNDWATER; HYDROCHEMISTRY; IONS; NITRATES; RESIDUAL STRESSES; SODIUM BICARBONATE; STRAIN RATE;

ALLOY 22; CHLORIDE ION CONCENTRATION; CHLORIDE SOLUTIONS; SATURATED CALOMEL ELECTRODE; SIMULATED GROUND WATER; SLOW STRAIN RATE TESTS; SODIUM NITRATE SOLUTION; SYNERGISTIC EFFECT;

STRESS CORROSION CRACKING;

EID: 54249110027     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278312     Document Type: Article

References (26)

1. U.S. Department of Energy, "Yucca Mountain Science and Engineering Report," U.S. Department of Energy, Office of Civilian Radioactive Waste Management, DOE/RW-539-1, Las Vegas, Nevada, February 2002.
2. G.M. Gordon, Corrosion 58, 10 (2002): p. 811-825.
3. J.C. Estill, G.A. Hust, R.B. Rebak, "Long-Term Corrosion Potential Behavior of Alloy 22 in Yucca Mountain Relevant Environments," CORROSION/2003, paper no. 03688 (Houston, TX: NACE International, 2003).
4. J.H. Lee, T. Summers, R.B. Rebak, "A Performance Assessment Model for Localized Corrosion Susceptibility of Alloy 22 in Chloride-Containing Brines for High-Level Nuclear Waste Disposal Container," CORROSION/ 2004, paper no. 04692 (Houston, TX: NACE, 2004).
5. D.S. Dunn, L.T. Yang, Y.-M. Pan, G.A. Cragnolino, "Localized Corrosion Susceptibility of Alloy 22," CORROSION/2003, paper no. 03697 (Houston, TX: NACE, 2003).
6. D.S. Dunn, G.A. Cragnolino, Y.-M. Pan, L.T. Yang, "Effect of Fabrication Processes on Alloy 22 Corrosion Resistance," CORROSION/ 2004, paper no. 04698 (Houston, TX: NACE, 2004).
7. P.L. Andresen, P.W. Emigh, L.M. Young, G.M. Gordon, "Stress Corrosion Cracking Growth Rate Behavior of Alloy 22 (UNS N06022) in Concentrated Groundwater," CORROSION/2003, paper no. 03683 (Houston, TX: NACE, 2003).
8. J.C. Estill, K.J. King, D.V. Fix, D.G. Spurlock, G.A. Hust, S.R. Gordon, R.D. McCright, R. Rebak, "Susceptibility of Alloy 22 to Environmentally Assisted Cracking in Yucca Mountain Relevant Environments," CORROSION/2002, paper no. 02535 (Houston, TX: NACE, 2002).
9. K.J. King, J.C. Estill, R. B. Rebak, "Characterization of the Resistance of Alloy 22 to Stress Corrosion Cracking," 2002 ASME Pressure Vessels and Piping Codes and Standards, ed. M.D. Rana, vol. 449, paper no, 03E-02 (New York, NY: ASME International, 2002).
10. D.V. Fix, J.C. Estill, G.A. Hust, K.J. King, S.D. Day, R.B. Rebak, "Influence of Environmental Variables in the Susceptibility of Alloy 22 to Environmentally Assisted Cracking," CORROSION/2003, paper no. 03542 (Houston, TX: NACE, 2003).
11. K.J. King, L.L. Wong, J.C. Estill, R.B. Rebak, "Slow Strain Rate Testing of Alloy 22 in Simulated Concentrated Groundwaters," CORROSION/2004, paper no. 04548 (Houston, TX: NACE, 2004).
12. P.L. Andresen, P.W. Emigh, L.M. Young, G.M. Gordon, "Stress Corrosion Cracking of Annealed and Cold-Worked Titanium Grade 7 and Alloy 22 in 110°C Concentrated Salt Environments," CORROSION /2001, paper no. 01130 (Houston, TX: NACE, 2001).
13. P.L. Andresen, P.W. Emigh, G.M. Gordon, "SCC Growth Rate Studies on Welded and Aged Alloy 22 in Concentrated Groundwater," CORROSION /2004, paper no. 04695 (Houston, TX: NACE, 2004).
14. G.A. Cragnolino, D. S. Dunn, Y.-M. Pan, "Effects of Potential and Environment on the Stress Corrosion Cracking Susceptibility of Nickel-Chromium-Molybdenum Alloys," CORROSION/2003, paper no. 03541 (Houston, TX: NACE, 2003).
15. ASTM G5-94, "Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements," in Annual Book of Standards, vol. 3.02: Wear and Erosion - Metal Corrosion (West Conshohocken, PA: ASTM International, 2003).
16. OLI Systems, Inc., StreamAnalyzer, ver. 1.2, Morris Plains, OLI System, Inc., New Jersey, 2002.
17. ASTM G129, "Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking," in Annual Book of Standards, vol. 3.02: Wear and Erosion--Metal Corrosion (West Conshohocken, PA: ASTM International, 2003).
18. ASTM B575-04a, "Standard Specification for Low-Carbon Nickel-Molybdenum-Chromium, Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, Low-Carbon Nickel-Chromium-Molybdenum-Tantalum, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Plate, Sheet, and Strip," In Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 2004).
19. N.D. Rosenberg, G.E. Gdowski, K.G. Knauss, Appl. Geochem. 16 (2001): p. 1,231-1,240.
20. K.T. Chiang, D.S. Dunn, G.A. Cragnolino, "The Combined Effect of Bicarbonate and Chloride Ions on the Stress Corrosion Cracking Susceptibility of Alloy 22," CORROSION/2006, paper no. 06506 (Houston, TX: NACE, 2006).
21. G.A. Cragnolino, D.S. Dunn, Y.-M. Pan, "Evaluation of Corrosion Processes Affecting the Performance of Alloy 22 as a Proposed Waste Package Material," Scientific Basis for Nuclear Waste Management XXVII, Symp. Proc., vol. 807, eds. V.M. Oversby, L.O. Werme (Warrendale, PA: Materials Research Society, 2004), p. 435-440.
22. B.A. Kehler, G.O. Ilevbare, J.R. Scully, Corrosion 57, 12 (2001): p. 1,042-1,065.
23. D.S. Dunn, L. Yang, C. Wu, G.A. Cragnolino, "Effect of inhibiting Oxyanions on the Localized Corrosion Susceptibility of Waste Package Container Materials," Scientific Basis for Nuclear Waste Management XXVIII, Symp. Proc., vol. 824, eds. J.M. Hanchar, S. Stroes-Gascoyne, L. Browning (Warrendale, PA: Materials Research Society, 2004), p. 33-38.
24. N. Sridhar, G.A. Cragnolino, "Stress-Corrosion Cracking of Nickel-Base Alloys," in Stress Corrosion Cracking - Materials Performance and Evaluation, ed. R.H. Jones (Materials Park, OH: ASM International, 1992), p. 131-179.
25. R.D. McCright, "Engineered Materials Characterization: Corrosion Data and Modeling - Update for the Viability Assessment," Lawrence Livermore National Laboratory, Report no. UCRL-ID-1 19564, vol. 3, rev. 1.1, 1998.
26. D.S. Dunn, Y.-M. Pan, K.T. Chiang, G.A. Cragnolino, "Surface Analysis of Alloy 22 Under Conditions that Promote Stress Corrosion Cracking," CORROSION/2006, paper no. 06509 (Houston, TX: NACE, 2006).