Stress corrosion cracking of annealed and cold worked Titanium Grade 7 and Alloy 22 in 110 °c concentrated salt environments

NACE - International Corrosion Conference Series

Volumn 2001-March, Issue , 2001, Pages

  Andresen, P L ^a   Emigh, P W ^a   Young, L M ^a   Gordon, G M ^b  

^a GE GLOBAL RESEARCH   (United States)

^b Framatome Cogema Fuels   (United States)

Author keywords

Alloy 22; Concentrated groundwater; Crack growth rate; Nuclear waste; Stress corrosion cracking; Titanium Grade 7

Indexed keywords

CONCENTRATION (PROCESS); CRACK PROPAGATION; CRACKS; GROUNDWATER; RADIOACTIVE WASTES; RESIDUAL STRESSES; TITANIUM ALLOYS;

ALLOY 22; CONCENTRATED GROUNDS; CONCENTRATED GROUNDWATER; DC POTENTIAL; LONG-TERM BEHAVIOR; PRE-CRACKING; STABLE CRACK GROWTH; STATIC LOADING;

STRESS CORROSION CRACKING;

EID: 85046754837     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (12)

1. P.L. Andresen and C.L. Briant, "Environmentally Assisted Cracking of Types 304L/316L/316NG Stainless Steel in 288 °C Water, " Corrosion, pp. 448-463, 1989.
2. P.L. Andresen, "IGSCC Crack Propagation Rate Measurement in BWR Environments: Executive Summary of a Round Robin Study", SKI Report 98:27, ISSN 1104-1374, ISRN SKI-R-98/27-SE, SKI, Stockholm, 1999.
3. P.L. Andresen, K. Gott and J.L. Nelson, "Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel in 288 °C Water: A Five Laboratory Round Robin", Proc. Ninth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, AIME, 1999.
4. D.M. Himmelblau, J Chem Eng Data 5, 10, 1960.
5. P.L. Andresen, "Effects of Testing Characteristics on Observed SCC Behavior in BWRs", Paper #98137, Corrosion/98, NACE, 1998.
6. P.L. Andresen, "SCC Testing and Data Quality Consideration", 9th Int. Syrup. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, AIME, 1999.
7. Unpublished results from P.L. Andresen and other in an EPRI sponsored, international experts "PEER" group which evaluated crack growth data for Alloy 600 and Alloy 182 weld metal, 1999.
8. P.L. Andresen, "Probabilistic Interpretation of SCC Initiation & Growth", Paper #99446, Corrosion/98, 1999.
9. J. Farmer et al, "General and Localized Corrosion of Outer Barrier of High Level Waste Container in Yucca Mountain", 2000 ASME/PVP Conference, Seattle, WA., July 23-27, 2000.
10. J. Farmer, "Waste Package Degradation Expert Elicitation Project", Rev. 1, Prepared by Geomatrix Consultants and TRW, June 1998.
11. P.L. Andresen and F.P. Ford, "Life Prediction by Mechanistic Modelling and System Monitoring of Environmental Cracking of Fe and Ni Alloys in Aqueous Systems", Matls Sci & Eng, A103, 167, 1988.
12. F.P. Ford and P.L. Andresen, "Corrosion in Nuclear Systems: Environmentally Assisted Cracking in Light Water Reactors", Corrosion Mechanisms, Ed. P. Marcus and J. Ouder, M. Dekker, 501, 1994.