Investigation of die for pressure die-casting of Mg-alloy

Engineering Failure Analysis

Volumn 16, Issue 1, 2009, Pages 176-181

  Torkar, M ^a   Godec, M ^a   Lamut, M ^a  

^a INSTITUTE OF METALS AND TECHNOLOGY   (Slovenia)

Author keywords

Corrosion; Erosion; Failure of tool; Metallography; Nitrided layer

Indexed keywords

CALCIUM; CHROMIUM; CORROSION; DIE CASTINGS; DIES; FRACTURE; FRACTURE TOUGHNESS; MAGNESIUM PRINTING PLATES; MECHANICAL PROPERTIES; MICROSCOPIC EXAMINATION; NITRIDES; SURFACES; TOUGHNESS;

EROSION; FAILURE OF TOOL; METALLOGRAPHY; NITRIDED LAYER;

DIE CASTING;

EID: 53849140457     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2008.02.001     Document Type: Article

References (9)

1. Ratajski J., Tacikowski J., and Somers M.A.J. Development of compound layer of iron (carbo) nitrides during nitriding of steel. Surf Eng 19 4 (2003) 285-291
2. Tercelj M., Smolej A., Fajfar P., and Turk R. Laboratory assessment of wear on nitrided surfaces of dies for hot extrusion of aluminium. Tribol Int 40 (2007) 374-384
3. Karamiş M.B., and Gerçekcioǧlu E. Wear behaviour of plasma nitrided steels at ambient and elevated temperatures. Wear 243 (2000) 76-84
4. Kang H., Park I.W., Jae J.S., and Kang S.S. A study on a die wear model considering thermal softening: (I) construction of the wear model. J Mater Process Technol 96 (1999) 53-58
5. Sjöstrom J., and Bergström J. Thermal fatigue testing of chromium martensitic hot-work tool steel after different austenitizing treatments. J Mater Process Technol 153-154 (2004) 1089-1096
6. Castro G., Fernandez-Vicente A., and Cid J. Influence of the time in the wear behaviour of an AISI H13 during a crankshaft forging process. Wear 263 7-12 (2007) 1375-1385
7. Godec M. Cooling cracks on nitrided pins. Eng Fail Anal 9 6 (2002) 665-671
8. Wei Y.-h., Yin G.-s., Hou L.-f., Xu B.-s., and Ichinose H. Formation mechanism of pits on the surface of thin-wall die-casting magnesium alloy components. Eng Fail Anal 13 4 (2006) 558-564
9. Murtaza G., and Akid R. Empirical corrosion fatigue life prediction models of a high strength steel. Eng Fract Mech 67 5 (2000) 461-474