Crack-growth behavior of epoxy adhesives modified with liquid rubber and cross-linked rubber particles under mode I loading

International Journal of Adhesion and Adhesives

Volumn 29, Issue 1, 2009, Pages 45-55

  Imanaka, Makoto ^a   Motohashi, Satoshi ^a   Nishi, Kazuaki ^a   Nakamura, Yoshinobu ^b   Kimoto, Masaki ^c  

^a OSAKA KYOIKU UNIVERSITY   (Japan)

^b OSAKA INSTITUTE OF TECHNOLOGY   (Japan)

^c OSAKA MUNICIPAL TECHNICAL RESEARCH INSTITUTE   (Japan)

Author keywords

A. Epoxy; M. Double cantilever beam specimen; M. Fracture mechanics

Indexed keywords

ADHESIVES; CANTILEVER BEAMS; CRACKS; DISTRIBUTED PARAMETER NETWORKS; EPITAXIAL GROWTH; FRACTURE FIXATION; FRACTURE TOUGHNESS; PAINTING; PHOTORESISTS; SURFACE ROUGHNESS; VOID FRACTION;

A. EPOXY; CRACK-GROWTH RESISTANCE; CROSS-LINKED RUBBER; DOUBLE-CANTILEVER BEAM; EPOXY ADHESIVES; FRACTURE SURFACES; GROWTH BEHAVIOR; GROWTH SIMULATIONS; GURSON'S MODELS; LOADING CONDITIONS; M. DOUBLE CANTILEVER BEAM SPECIMEN; M. FRACTURE MECHANICS; MODIFIED EPOXY; R-CURVES; SINGLE-EDGE NOTCH; TWO TYPES;

RUBBER;

EID: 50449090767     PISSN: 01437496     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijadhadh.2007.11.004     Document Type: Article

References (23)

1. Hunston D.L., Kinloch A.J., and Wang S.S. Micromedianics of fracture in structural adhesive bonds. J Adhes 28 (1989) 103-114
2. Daghyni H.R., Ye L., and Mai Y.-W. Mode I fracture behavior of adhesive joints, Part I. Relationship between fracture energy and bond thickness. J Adhes 53 (1995) 149-162
3. Rakestraw M.D., Taylor M.W., Dillard D.A., and Cheng T. Time dependent crack growth and loading effect on interfacial and cohesive fracture of adhesive joints. J Adhes 55 (1995) 123-149
4. Sue H.-J., Meitin E.I.G., Pickelman D.M., and Bott C.J. Fracture mechanisms inrigid core-shell particle modified high performance epoxies. Colloid Polym Sci 274 (1996) 342-349
5. Qian J.Y., Person R.A., Dimonie V.L., Shaffer O.L., and EI-Aasser M.S. The role of dispersed phase morphology on toughening on epoxies. Polymer 38 (1997) 21-30
6. Ormatxea M., Forcada J., Mugika F., Valea A., Martin M.D., Marieta C., et al. Ultimate properties of rubber and core-shell modified epoxy matrices with different chain flexibilities. J Mater Sci 36 (2001) 845-852
7. Fan L., Cantwell W.J., and Kausch H.H. The role of cavitation and debonding in the toughening of core-shell rubber modified epoxy systems. J Mater Sci 32 (1997) 3055-3059
8. Yan C., Xiao K., and Mai Y.-W. Numerical and experimental studies on the fracture behavior of rubber-toughened epoxy in bulk specimen and laminated composites. J Mater Sci 37 (2002) 921-927
9. Imanaka M., Nakamura Y., Nishimura A., and Iida T. Fracture toughness of rubber-modified epoxy adhesives: effect of plastic deformability of matrix phase. Comp Sci Tech 63 (2003) 41-51
10. Du J., Thouless M.D., and Yee A.F. Development of a process zone in rubber-modified epoxy polymers. Int J Fract 92 (1998) 271-285
11. Blackman B.P.K., Hadavinia H., Kinloch A.J., Parasch M., and Williams J.G. The calculation of adhesive fracture energies in mode I: revisiting the tapered double cantilever beam (TDCB) test. Eng Fract Mech 70 (2003) 233-248
12. 1C, of structural adhesive joints: an effective crack length approach. Eng Fract Mech 72 (2005) 897-977
13. ASTM Designation: E-1820-99a, standard test method for measurement of fracture toughness. In: Annual book of ASTM standard, section 3, vol. 03.01.2000.
14. Cotterell B., and Mai Y.-W. Fracture mechanics of cementitious materials (1996), Blackie Academic & Professional, London
15. Daghyani H.R., Ye L., and Mai Y.-W. Effect of thermal residual stress on the crack path in adhesively bonded joints. J Mater Sci 31 (1996) 2523-2529
16. Lee D.-B., Ikeda T., Miyazaki N., and Choi N.-S. J Mater Sci Lett 22 (2003) 229-233
17. Gurson A.L. Continumm theory of ductile rupture by void nucleation and growth, Part 1. Yield and flow rule for porous ductile media. J Eng Mater Tech 99 (1977) 2-15
18. Tvergaard V. Influence of void nucleation on ductile shear fracture at free surface. J Mech Phys Solids 30 (1982) 399-425
19. Lazzeri A, Bucknall CB. Recent developments in the modeling of dilational yielding in toughened plastics. In: Person RA, Sue H-J, Tee AF, editors. Symposium series #759 on toughening of plastics, American Chemical Society, Washington, DC; 2000. p. 86-96.
20. Ikeda T, Mano J, Ikemoto D, Lee DB, Miyazaki N. Constraint effect of the fracture of adhesive joint (2nd Report, Failure analysis around a crack tip using Gurson's model). Trans Jpn Soc Mech Eng 2003;69:210-7 (in Japanese).
21. Tverrgard V. On localization in ductile materials containing spherical voids. Int J Fract 18 (1982) 237-252
22. Imanaka M., and Suzuki Y. Yield behavior of rubber-modified epoxy adhesives under multiaxial stress condition. J Adhes Sci Technol 11 (2002) 1687-1700
23. Xia L., Shih C.F., and Hutchinson J.H. A computational approach to ductile crack growth under large scale yielding conditions. J Mech Solids 43 (1995) 389-413