Corrosion and stress-corrosion cracking of exploited storage tank steel

Materials Science

Volumn 40, Issue 3, 2004, Pages 421-427

  Zagorski A ^a,b   Matysiak, H ^a,b   Tsyrulnyk, O ^a,b   Zvirko, O ^a,b   Nykyforchyn, H ^a,b   Kurzydlowski K ^a,b  

^a KARPENKO PHYSICOMECHANICAL INSTITUTE   (Ukraine)

^b WARSAW UNIVERSITY OF TECHNOLOGY   (Poland)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION RESISTANCE; CRACK INITIATION; DEGRADATION; FRACTURE; MAGNETIC SUSCEPTIBILITY; PLASTICS;

CORROSION ACTIVITY; HYDROGEN-INDUCED CRACKING; ST3S STEEL;

STEEL;

HYDROGEN; METAL; STEEL; WATER;

ARTICLE; CHEMICAL INTERACTION; CORROSION; DEGRADATION; PHYSICAL CHEMISTRY; STATISTICAL SIGNIFICANCE; TANK;

EID: 14944364466     PISSN: 1068820X     EISSN: None     Source Type: Journal    
DOI: 10.1007/s11003-005-0055-4     Document Type: Article

References (10)

1. A. Y. Krasowsky A. A. Dolgiy V. M. Torop 2001 Charpy testing to estimate pipeline steel degradation after 30 years of operation Proc. "Charpy Centenary Conference" 1 489 495 Poitiers
2. Z. V. Slobodyan H. M. Nykyforchyn O. I. Petrushchak 2002 Corrosion resistance of pipe steel in petroleum-water media Mater. Sci. 38 3 424 429 (translated from Fizyko-Khimichna Mekhanika Materialiv, 38, No. 3, 93-96 (2002))
3. Z. Slobodyan O. Petrushchak H. Nykyforchyn E. Łunarska 2002 Peculiarities of corrosion fracture of the inner side surface of oil pipeline Fiz.-Khim. Mekh. Mater. 3 782 785
4. H. Nykyforchyn K.-J. Kurzydłowski A. Zagórski Z. Slobodyan 2003 Corrosion and mechanical degradation of transport oil pipeline and tanks Proc. of the 3rd Internal. Conf. "Strength, Durability, and Stability of Materials and Structures" (September 2003) Kaunas Technologija, Klaipeda Lithuania 207 214 in
5. A. Zagórski H. Matysiak Z. Słobodian O. Zvirko H. Nykyforchyn K. Kurzydłowski 2004 Corrosion degradation of oil-storage tank Fiz.-Khim. Mekh. Mater. 1 437 439
6. A. Turnbul 1992 Tests methods for environment-assisted cracking British Cor. J. 27 4 271 289
7. MP 185-86: Methodical Recommendations. Strength Analyses and Tests. Testing Methods for the Evaluation of the Susceptibility of Steels and Alloys to Corrosion Cracking in Liquid Media, VNIINMASH, Moscow (1986).
8. H. Nykyforchyn, D. Slobodyan, O. Petrushchak, E. Łunarska, "Rola wodoru w korozyjnym niszczenu wewnetrznych powierzchni rurociagu naftowego, " in: Ochrona Przed Korozja̧ Wydanie Specialne (2002), pp. 445-449.
9. V. Y. Chemov V. D. Makarenko E. I. Kryzhanivs'kyi L. S. Shlapak 2002 On the causes of corrosion fracture of industrial pipelines Mater. Sci. 38 6 880 883 (translated from Fizyko-Khimichna Mekhanika Materialiv, 38, No. 6, 93-95 (2002))
10. O. I. Radkevych H. V. Chumalo 2003 Damage to the metal of industrial pipelines in a hydrogen-sulfide environment Mater. Sci. 39 4 596 600 (translated from Fizyko-Khimichna Mekhanika Materialiv, 39, No. 4, 112-114 (2003))