Preparation and characterization of continuous high-temperature resistant Si-Al-C fibers by one-step method

Science in China, Series E: Technological Sciences

Volumn 51, Issue 9, 2008, Pages 1425-1432

  Zheng, ChunMan ^a   Li, XiaoDong ^a   Wang, Hao ^a   Zhao, DaFang ^a   Hu, TianJiao ^a  

^a NATIONAL UNIVERSITY OF DEFENSE TECHNOLOGY   (China)

Author keywords

Continuous Si Al C fibers; High temperature resistant; One step method; Polymer derived technology

Indexed keywords

ALUMINUM; CURING; DRYING; FIBERS; SILICON; SILICON CARBIDE; SINTERING; SULFATE MINERALS;

AVERAGE DIAMETER; CHEMICAL FORMULAE; CONTINUOUS SI-AL-C FIBERS; HIGH TEMPERATURES; HIGH-TEMPERATURE RESISTANT; MELT-SPINNING; ONE STEP METHOD; ONE-STEP METHODS; POLYALUMINOCARBOSILANE; POLYMER-DERIVED TECHNOLOGY;

SPINNING (FIBERS);

EID: 49249132203     PISSN: 10069321     EISSN: 1862281X     Source Type: Journal    
DOI: 10.1007/s11431-008-0106-9     Document Type: Article

References (20)

1. Johnson D W, Evans A G, Goettler R W. Ceramic Fibers and Coatings: Advanced Materials for the Twenty-First Century. Publication NMAB-494, Washington D C: National Academy Press, 1998. 1-49
2. Yajima S, Hayashi J, Omori M, et al. Development of a SiC fiber with high tensile strength. Nature, 1976, 262: 683-685
3. Laine R M, Babonneau F. Preceramic polymer routes to silicon carbide. Chem Mater, 1993, 5: 260-279
4. Sacks M D. Effect of composition and heat treatment conditions on the tensile strength and creep resistance of SiC-based fibers. J Europ Ceram Soc, 1999, 19(10): 2305-2315
5. Toreki W, Batich C D, Sacks M D, et al. Polymer-derived silicon carbide fibers with low oxygen content and improved thermomechanical stability. Comp Sci Technol, 1994, 51(2): 145-159
6. Kakimoto K I, Shimoo T, Okamura K. Oxidation-induced microstructural change of Si-Ti-C-O fibers. J Am Ceram Soc, 1998, 81(2): 409-412
7. Kumagawa K, Yamaoka H, Shibuya M, et al. Thermal stability and chemical corrosion resistance of newly developed continuous Si-Zr-C-O Tyranno fiber. Ceram Eng Sci Proc, 1997, 18(3): 113-118
8. Lipowitz J, Barnard T, Bujalski D, et al. Fine-diameter polycrystalline SiC fibers. Comp Sci Technol, 1994, 51(2): 167-171
9. Ishikawa T, Kohtoku Y, Kumagawa K, et al. High-strength alkali-resistant sintered SiC fiber stable able to 2200°C. Nature, 1998, 391: 773-774
10. Cao F, Li X D, Peng P, et al. Structural evolution and associated properties on conversion from Si-C-O-Al ceramic fibers to Si-C-Al fibers by sintering. J Mater Chem, 2002, 12(3): 606-610
11. Zheng C M, Li X D, Yu Y X, et al. Preparation of high temperature resistance Si-Al-C-O fibers by polymer-derived method (in Chinese). J Mater Eng, 2004, 259(12): 25-28
12. Wang Y D, Feng C X, Song Y C. Study on process of continuous SiC fibers (in Chinese). Aerospace Mater Technol, 1997, 27(2): 21-25
13. Vahlas C. Thermodynamic approach to the oxidation of Hi-Nicalon™ fiber. J Am Ceram Soc, 1999, 82(9): 2514-2516
14. Suzuki K, Kumagawa K, Kamiyama T, et al. Characterization of the medium-range structure of Si-Al-C-O, Si-Zr-C-O, and Si-Al-C Tyranno fibers by small angle X-ray scattering. J Mater Sci, 2002, 37(5): 949-953
15. Du T F. Modern Instrument and Analysis (in Chinese). Changsha: National University of Defense Technology Press, 1994. 250-273
16. Hartman J S, Richardson M F, Sherriff B L, et al. Magic angle spinning NMR studies of silicon carbide polytypes, impurities, and highly inefficient spin-lattice relaxation. J Am Chem Soc, 1987, 109(20): 6059-6067
17. 13C in β-Silicon carbides. J Phy Chem, 1989, 93(13): 5061-5064
18. Yang N R, Yue W H. The Handbook of Inorganic Metalloid Materials Atlas (in Chinese). Wuhan: Wuhan Industry University Press, 2000. 608-609
19. Babonneau F, Soraru G D, Thorne K J, et al. Chemical characterization of Si-Al-C-O precursor and its pyrolysis. J Am Ceram Soc, 1991, 74(7): 1725-1728
20. Li X D, Edirisinghe M J. Evolution of the ceramic structure during thermal degradation of a Si-Al-C-O precursor. Chem Mater, 2004, 16(6): 1111-1119