Advanced Engineering Materials

Volumn 10, Issue 5, 2008, Pages 453-458

Stress Corrosion Cracking (SCC) in Mg-Al alloys studied using compact specimens

(5) Winzer, Nick a Atrens, Andrej a Dietzel, Wolfgang b Song, Guangling a Kainer, Karl U b

a UNIVERSITY OF QUEENSLAND (Australia)

b INSTITUTE OF MATERIALS RESEARCH (Germany)

Author keywords

[No Author keywords available]

Indexed keywords

ADDITION REACTIONS; ADSORPTION; ALLOYS; ALUMINUM; CORROSION; CORROSION FATIGUE; CRACK DETECTION; CRACK TIPS; CRACKING (CHEMICAL); CRACKS; GAS ADSORPTION; HELIUM; HYDROGEN; HYDROGEN EMBRITTLEMENT; MAGNESIUM PRINTING PLATES; MECHANISMS; METAL CASTINGS; METALS; NONMETALS; PIGMENTS; POWDERS; RESIDUAL STRESSES; STRESSES; TESTING;

AS-CAST; CONTROL TESTS (CT); CORROSION REACTIONS; DE COHESION; DELAYED HYDRIDE CRACKING (DHC); FATIGUE CRACKS; HYDROGEN EMBRITTLEMENT (HM); HYDROGEN-ENHANCED LOCALIZED PLASTICITY (HELP); INDUCED DISLOCATION; MG AL ALLOYS; MG ALLOYS; PRINCIPLE STRESSES; STRESS CORROSION; STRESS CORROSION CRACKING (SCC); TEST MATERIALS; TRANSGRANULAR STRESS CORROSION CRACKING (TGSCC);

STRESS CORROSION CRACKING;

EID: 45149105508 PISSN: 14381656 EISSN: 15272648 Source Type: Journal
DOI: 10.1002/adem.200700319 Document Type: Article

Times cited : (34)

References (35)

1
- 25444458037
- N. Winzer, A. Atrens, G. Song, E. Ghali, W. Dietzel, K. U. Kainer, N. Hort, C. Blawert, Adv. Eng. Mater. 2005, 8, 659.
- (2005) Adv. Eng. Mater , vol.8 , pp. 659
- Winzer, N.¹ Atrens, A.² Song, G.³ Ghali, E.⁴ Dietzel, W.⁵ Kainer, K.U.⁶ Hort, N.⁷ Blawert, C.⁸

2
- 42149154380
- DOI: 10.1007/s11661-008-9475-8
- N. Winzer, A. Atrens, W. Dietzel, G. Song, K. U. Kainer, Metall. Mater. Trans. A 2008, DOI: 10.1007/s11661-008-9475-8.
- (2008) Metall. Mater. Trans. A
- Winzer, N.¹ Atrens, A.² Dietzel, W.³ Song, G.⁴ Kainer, K.U.⁵

3
- 0004328695
- doi:10.1016/j.msea.2007.03.021
- N. Winzer, A. Atrens, W. Dietzel, G. Song, K. U. Kainer, Mater. Sci. Eng. A 2007, doi:10.1016/j.msea.2007.03.021.
- (2007) Mater. Sci. Eng. A
- Winzer, N.¹ Atrens, A.² Dietzel, W.³ Song, G.⁴ Kainer, K.U.⁵

4
- 0004328695
- doi: 10.1016/ j.msea.2007.07.070
- M. Bobby Kannan, W. Dietzel, C. Blawert, A. Atrens, P. Lyon, Mater. Sci. Eng. A 2007, doi: 10.1016/ j.msea.2007.07.070.
- (2007) Mater. Sci. Eng. A
- Bobby Kannan, M.¹ Dietzel, W.² Blawert, C.³ Atrens, A.⁴ Lyon, P.⁵

5
- 23444452376
- R. G. Song, C. Blawert, W. Dietzel, A. Atrens, Mater. Sci. Eng. 2005, 399, 308.
- (2005) Mater. Sci. Eng , vol.399 , pp. 308
- Song, R.G.¹ Blawert, C.² Dietzel, W.³ Atrens, A.⁴

6
- 44049096006
- DOI: 10.1016/ j.msea.2007.11.064
- N. Winzer, A. Atrens, W. Dietzel, V. S. Raja, G. Song, K. U. Kainer, Mater. Sci. Eng. A 2008, DOI: 10.1016/ j.msea.2007.11.064.
- Mater. Sci. Eng. A , vol.2008
- Winzer, N.¹ Atrens, A.² Dietzel, W.³ Raja, V.S.⁴ Song, G.⁵ Kainer, K.U.⁶

7
- 34447275029
- N. Winzer, A. Atrens, W. Dietzel, G. Song, K. U. Kainer, Mater. Sci. Eng. A - Struct 2007, 466, 18.
- (2007) Mater. Sci. Eng. A - Struct , vol.466 , pp. 18
- Winzer, N.¹ Atrens, A.² Dietzel, W.³ Song, G.⁴ Kainer, K.U.⁵

8
- 0033196585
- G. Song, A. Atrens, Adv. Eng. Mater. 1999, 1, 11.
- (1999) Adv. Eng. Mater , vol.1 , pp. 11
- Song, G.¹ Atrens, A.²

9
- 1342283923
- G. Song, A. Atrens, Adv. Eng. Mater. 2003, 5, 837.
- (2003) Adv. Eng. Mater , vol.5 , pp. 837
- Song, G.¹ Atrens, A.²

10
- 33947626062
- G. Song, A. Atrens, Adv. Eng. Mater. 2007, 9, 177.
- (2007) Adv. Eng. Mater , vol.9 , pp. 177
- Song, G.¹ Atrens, A.²

11
- 34248192408
- A. Atrens, W. Dietzel, Adv. Eng. Mater. 2007, 9, 292.
- (2007) Adv. Eng. Mater , vol.9 , pp. 292
- Atrens, A.¹ Dietzel, W.²

12
- 0023964602
- S. P. Lynch, P. Trevena, Corrosion 1988, 44,113.
- (1988) Corrosion , vol.44 , pp. 113
- Lynch, S.P.¹ Trevena, P.²

13
- 0021226322
- E. I. Meletis, R. F. Hochman, Corrosion 1984, 40, 39.
- (1984) Corrosion , vol.40 , pp. 39
- Meletis, E.I.¹ Hochman, R.F.²

14
- 0016921482
- D. G. Chakrapani, E. N. Pugh, Metall. Trans. A 1976, 7, 173.
- (1976) Metall. Trans. A , vol.7 , pp. 173
- Chakrapani, D.G.¹ Pugh, E.N.²

15
- 0642328286
- Materials Society, London
- A. J. Bursle, E. N. Pugh, in Mech. of Environment Sensitive Cracking of Mater, Materials Society, London 1977, 471.
- (1977) Mech. of Environment Sensitive Cracking of Mater , pp. 471
- Bursle, A.J.¹ Pugh, E.N.²

16
- 0027643116
- G. L. Makar, J. Kruger, K. Sieradzki, Corros. Sci. 1993, 34, 1311.
- (1993) Corros. Sci , vol.34 , pp. 1311
- Makar, G.L.¹ Kruger, J.² Sieradzki, K.³

17
- 45149093997
- S. P. Lynch, Ada. Metall. 1988, 34, 2639.
- (1988) Ada. Metall , vol.34 , pp. 2639
- Lynch, S.P.¹

18
- 4544298704
- TMS, Warrendale
- S. P. Lynch, in Hydrogen Effects on Mater. Behavior and Corrosion Deformation Interactions, TMS, Warrendale 2003, 449.
- (2003) Hydrogen Effects on Mater. Behavior and Corrosion Deformation Interactions , pp. 449
- Lynch, S.P.¹

19
- 0004896788
- TMS, Warrendale
- H. K. Birnbaum, in Hydrogen Effects on Mater. Behavior, TMS, Warrendale 1990, 639.
- (1990) Hydrogen Effects on Mater. Behavior , pp. 639
- Birnbaum, H.K.¹

20
- 0016564695
- J. K. Tien, R. J. Richards, Scr. Metall. Mater. 1975, 9, 1097.
- (1975) Scr. Metall. Mater , vol.9 , pp. 1097
- Tien, J.K.¹ Richards, R.J.²

21
- 84974904217
- L. Fairman, H. J. Bray, Brit. Corros. J. 1971, 6, 170.
- (1971) Brit. Corros. J , vol.6 , pp. 170
- Fairman, L.¹ Bray, H.J.²

22
- 25444525694
- W. M. Pardue, F. H. Beck, M. G. Fontana, Trans. of the Am. Soc.for Met. 1961, 54, 539.
- (1961) Trans. of the Am. Soc.for Met , vol.54 , pp. 539
- Pardue, W.M.¹ Beck, F.H.² Fontana, M.G.³

23
- 0004184893
- ASM International, USA
- W. K. Miller, in Stress Corrosion Cracking: Mater. Performance and Evaluation, ASM International, USA 1992, 251.
- (1992) Stress Corrosion Cracking: Mater. Performance and Evaluation , pp. 251
- Miller, W.K.¹

24
- 0018547359
- W.-Y. Chu, C.-M. Hsiao, S.-Q. Li, Scr. Met. 1979, 13, 1063.
- (1979) Scr. Met , vol.13 , pp. 1063
- Chu, W.-Y.¹ Hsiao, C.-M.² Li, S.-Q.³

25
- 0345982296
- N. N. Kinaev, D.R. Cousens, A. Atrens, J. Mater. Sci. 1999, 34, 4909.
- (1999) J. Mater. Sci , vol.34 , pp. 4909
- Kinaev, N.N.¹ Cousens, D.R.² Atrens, A.³

26
- 0346613580
- N. N. Kinaev, D. R. Cousens, A. Atrens, J. Mater. Sci. 1999, 34, 4921.
- (1999) J. Mater. Sci , vol.34 , pp. 4921
- Kinaev, N.N.¹ Cousens, D.R.² Atrens, A.³

27
- 0038711084
- N. N. Kinaev, D. R. Cousens, A. Atrens, J. Mater. Sci. 1999, 34, 4931.
- (1999) J. Mater. Sci , vol.34 , pp. 4931
- Kinaev, N.N.¹ Cousens, D.R.² Atrens, A.³

28
- 45149104719
- J. K. Tien, O. Buck, R. C. Bates, S. Nair, Scr. Metall. Mater. 1980, 14, 583.
- (1980) Scr. Metall. Mater , vol.14 , pp. 583
- Tien, J.K.¹ Buck, O.² Bates, R.C.³ Nair, S.⁴

29
- 25444505910
- R. I. Stephens, C. D. Schrader, D. L. Goodenberger, K. B. Lease, V. V. Ogarevic, S. N. Perov, Soc. of Automotive Eng. 1993, 930752.
- (1993) Soc. of Automotive Eng , pp. 930752
- Stephens, R.I.¹ Schrader, C.D.² Goodenberger, D.L.³ Lease, K.B.⁴ Ogarevic, V.V.⁵ Perov, S.N.⁶

30
- 0002780761
- M. O. Speidel, M. J. Blackburn, T. R. Beck, J. A. Feeney, Mech. and Microstruct. NACE-2, 1972, 324.
- (1972) Mech. and Microstruct , vol.NACE-2 , pp. 324
- Speidel, M.O.¹ Blackburn, M.J.² Beck, T.R.³ Feeney, J.A.⁴

31
- 0023833967
- K. Ebtehaj, D. Hardie, R. N. Parkins, Corros. Sci. 1993, 28, 811.
- (1993) Corros. Sci , vol.28 , pp. 811
- Ebtehaj, K.¹ Hardie, D.² Parkins, R.N.³

32
- 0016520094
- D. G. Chakrapani, E. N. Pugh, Metall. Trans. A 1975, 6, 1155.
- (1975) Metall. Trans. A , vol.6 , pp. 1155
- Chakrapani, D.G.¹ Pugh, E.N.²

33
- 0004564631
- W. R. Wearmouth, G. P. Dean, R. N. Parkins, Corrosion 1973, 29, 251.
- (1973) Corrosion , vol.29 , pp. 251
- Wearmouth, W.R.¹ Dean, G.P.² Parkins, R.N.³

34
- 0028375179
- S. Q. Shi, M. P. Puls, J. Nucl. Mater. 1994, 208, 232.
- (1994) J. Nucl. Mater , vol.208 , pp. 232
- Shi, S.Q.¹ Puls, M.P.²

35
- 4344637668
- C. Yan, L. Ye, Y.-W. Mai, Mater. Lett. 2004, 58, 3219.
- (2004) Mater. Lett , vol.58 , pp. 3219
- Yan, C.¹ Ye, L.² Mai, Y.-W.³

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.