Dehydration of Ca3Al2(SiO4)y(OH)4(3-y) (0 < y < 0.176) studied by neutron thermodiffractometry

Journal of the European Ceramic Society

Volumn 28, Issue 9, 2008, Pages 1737-1748

  Rivas Mercury, J M ^a   Pena, P ^b   de Aza, A H ^b   Turrillas, X ^c  

^a FEDERAL INSTITUTE OF EDUCATION   (Brazil)

^b INSTITUTO DE CERÁMICA Y VIDRIO   (Spain)

^c INSTITUTO DE CIENCIAS DE LA CONSTRUCCIÓN EDUARDO TORROJA   (Spain)

Author keywords

Calcium aluminates; Neutron powder diffraction; Refractories; Thermal expansion; Thermal treatment; X ray methods

Indexed keywords

ANNEALING; CALCIUM COMPOUNDS; DECOMPOSITION; DEHYDRATION; HYDRATION; NEUTRON POWDER DIFFRACTION; QUENCHING; SILICA; THERMAL EXPANSION;

HYDROGARNET; KATOITE; THERMAL DEHYDRATION; TRICALCIUM ALUMINUM OXIDE;

REFRACTORY MATERIALS;

ANNEALING; CALCIUM COMPOUNDS; DECOMPOSITION; DEHYDRATION; HYDRATION; NEUTRON POWDER DIFFRACTION; QUENCHING; REFRACTORY MATERIALS; SILICA; THERMAL EXPANSION;

EID: 41549155891     PISSN: 09552219     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.jeurceramsoc.2007.12.038     Document Type: Article

References (23)

1. Lee W.E., Viera W., Zang S., Ahai K.G., Sarpoolaky H., and Parr C. Castable refractory concretes. Int. Mater. Rev. 46 3 (2001) 145-167
2. 4-humo de sílice. Bol. Soc. Esp. Ceram. Vidr. 46 6 (2007) 280-288
3. Rivas-Mercury J.M., de Aza A.H., Turrillas X., and Pena P. Calcium aluminate cements hydration. Part II: effect of silica and alumina additions. Bol. Soc. Esp. Ceram. Vidr. 42 6 (2003) 361-368
4. 2 at temperatures below 90 °C. J. Solid State Chem. 179 10 (2006) 2988-2997
5. Turrillas X., Convert P., Hansen T., De Aza A.H., Pena P., Rodriguez M.A., et al. Dehydration of calcium aluminate hydrates investigated by neutron thermodiffractometry. In: Mangabhai R.J., and Glasser F.P. (Eds). Proceedings of the International Conference on Calcium Aluminate Cements (2001), Edinburgh 517-531
6. 6 from soft mechanochemically activated precursors studied by time-resolved neutron diffraction up to 1000 °C. J. Solid State Chem. 177 (2004) 866-874
7. Program Origin Version 7.0. Microcal Software Inc., Northampton, MA, USA; 2004.
8. Program NOeSYS. Version 1.2. Research Systems Inc. (Kodak Company), Sterling, VA 20164, USA; 1998. http://www.rsinc.com/.
9. Outokumpu HSC Chemistry for Windows Version 1.10. Outokumpu Research Oy, Pori, Finland; 1993.
10. Rodríguez-Carvajal J. Satellite Meeting on Powder Diffraction of the XV IUCr Congress, 127 (1990)
11. Accelrys Materials Studio v. 4.0. Accelrys, Cambridge, CB4 0WN, UK; 2005.
12. Pawley G.S. Unit-cell refinement from powder diffraction scans. J. Appl. Cryst. 14 (1981) 357
13. Engel G.E., Wilke S., Harris K.D.M., and Leusen F.J.J. PowderSolve-a complete package for crystal structure solution from powder diffraction patterns. J. Appl. Cryst. 32 (1999) 1169-1179
14. 3. Am. Mineral. 72 (1987) 756-765
15. McCusker L.B., Von Dreele R., Cox B., Louer D.E., and Scardi D.P. Rietveld refinement guidelines. J. Appl. Crystallogr. 32 (1999) 36-50
16. 29Si NMR investigation on Si-substituted hydrogarnets. Acta Mater. 55 (2007) 1183-1191
17. 3). Neues Jahrb Mineral Montas. (1970) 547-552
18. Fujita S., Suzuki K., Ohkawa M., Shibasaki Y., and Mori T. Reaction of hydrogrossular with hydrogen chloride gas at high temperature. Chem. Mater. 13 8 (2001) 2523-2527
19. 2(2-) radicals. Chem. Mater. 15 1 (2003) 255-263
20. Fenq Q.L., Glasser F.P., Howie R.A., and Lachowski E.E. Acta Crystalogr. C44 (1988) 589-590
21. 3 prepared via solid-state reactions. Inorg. Chem. 26 8 (1987) 1192-1195
22. Fujita S., Ohkawa M., Suzuki K., Nakano H., Mori T., and Masuda H. Controlling the quantity of radical oxygen occluded in a new aluminum silicate with nanopore. Chem. Mater. 15 26 (2003) 4879-4881
23. 2. J. Am. Ceram. Soc. 42 12 (1959) 644-645