Prediction of time to crack initiation in reinforced concrete exposed to chloride

Construction and Building Materials

Volumn 22, Issue 6, 2008, Pages 1100-1107

  Yüzer, Nabi ^a   Aköz, Fevziye ^a   Kabay, Nihat ^a  

^a YILDIZ TECHNICAL UNIVERSITY   (Turkey)

Author keywords

Accelerated corrosion; Corrosion; Cracking (fracturing); Internal chlorides; Reinforced concrete; Silica fume

Indexed keywords

CHLORINE COMPOUNDS; CRACK INITIATION; DAMAGE DETECTION; NEGATIVE IONS; REINFORCED CONCRETE; SILICA FUME;

ACCELERATED CORROSIONS; CONCRETE INGREDIENTS; CORROSION TESTS; INTERNAL CHLORIDES;

CORROSION RATE;

EID: 40949144493     PISSN: 09500618     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.conbuildmat.2007.03.011     Document Type: Article

References (21)

1. Rodriguez P., Ramirez E., and Gonzalez J.A. Methods for studying corrosion in reinforced concrete. Mag Concrete Res 46 (1994) 81-90
2. Akman M.S. Concrete technology in marine structures (1992), I.T.U. Publishing House, Istanbul Turkey p. 188-94
3. Liong M.T., Wang K.L., and Liang C.H. Service life prediction of reinforced concrete structures. Cement Concrete Res 29 (1999) 1411-1418
4. Martin-Perez B., Zibara H., Hooton R.D., and Thomas M.D.A. A study of the effect of chloride binding on service life predictions. Cement Concrete Res 30 (2000) 1215-1223
5. Khatri R.P., and Sirivivatnanon. Characteristic service life for concrete exposed to marine environments. Cement Concrete Res 34 (2004) 745-752
6. Kirkpatrick T.J., Weyers R.E., Anderson-Cook C.M., and Sprinkel M.M. Probabilistic model for the chloride-induced corrosion service life of bridge decks. Cement Concrete Res 32 (2002) 1943-1960
7. Uomoto T., and Misra S. Behavior of concrete beams and columns in marine environment when corrosion of reinforcing bars takes place. II International conference on performance of concrete in marine environment (1988), New Brunswick, Canada 127-146
8. Andrade C., Alonso C., and Molina F.J. Cover cracking as a function of bar corrosion: part I - experimental test. Mater Struct 26 (1993) 453-464
9. ASM Handbook. Corrosion, 4th ed. vol. 13. ASM International; 1992. p. 212-3.
10. Andrade C., Alonso C., Rodriguez J., and Garcia M. Cover cracking and amount of rebar corrosion:Importance of the current applied accelerated tests. Concrete repair, rehabilitation and protection (1996), E and FN Spon, London p. 263-73
11. Khedr A., and Idriss A.F. Resistance of silica fume concrete to corrosion-related damage. J Mater Civil Eng 7 2 (1995) 102-107
12. Pech-Canul M.A., and Castro P. Corrosion measurements of steel reinforcement in concrete exposed to a tropical marine atmosphere. Cement Concrete Res 32 (2002) 495-498
13. APHA. Standard method for the examination of water and waste, 17th ed. AWWA, WPEF: Washington; 1989. p. 4.67-4.70.
14. Angi L, Baoyu L, Guoping H, Yeibo C, Guolian S. Study on corrosion prevention in reinforced concrete containing condensed silica fume and its application. In: II. CANMET/ACI international conference on durability of concrete. Canada: Montreal; 1991. p. 499-509.
15. Lorentz T., and French C. Corrosion on reinforcing steel in concrete: Effects of materials, mix composition, and cracking. ACI Mater J 92 2 (1995) 181-190
16. Wiens U, Breit W, Schiessl P. Influence of high silica fume and high fly ash contents on alkalinity of pore solution and protection of steel against corrosion. In: V. CANMET/ACI international conference on fly ash, silica fume, slag and natural pozzolans in concrete. USA: Milwaukee; 1995. p. 741-61.
17. Kayali{dotless} O., and Zhu B. Corrosion performance of medium-strength and silica fume high-strength reinforced concrete in a chloride solution. Cement Concrete Comp 27 (2005) 117-124
18. Mehta P.K. Concrete, structure properties and materials (1986), Prentice-Hall, USA p. 152-8
19. Gonzalez J.A., Andrade C., Alonso C., and Feliu S. Comparison of rates of general corrosion and maximum pitting penetration on concrete embedded steel reinforcement. Cement Concrete Res 25 2 (1995) 257-264
20. Rasheeduzzafar, Hussain S.E., and Al-Gahtani A.S. Pore solution composition and reinforcement corrosion characteristics of microsilica blended cement concrete. Cement Concrete Res 21 (1991) 1035-1048
21. Yüzer N. The investigation of chloride effect on reinforced concrete members with silica fume by using accelerated corrosion test, Ph.D. Thesis, Department of Civil Engineering, Yi{dotless}ldi{dotless}z Technical University, 1998.