Crack-healing behaviour and resultant high-temperature fatigue strength of machined Si3N4/SiC composite ceramic

Fatigue and Fracture of Engineering Materials and Structures

Volumn 31, Issue 1, 2008, Pages 2-11

  Jung, Y S ^a   Guo, Y ^a   Nakao, W ^a   Takahashi, K ^a   Ando, Koto ^a   Saito, S ^b  

^a YOKOHAMA NATIONAL UNIVERSITY   (Japan)

^b Dept NHK SPRING Co   (Japan)

Author keywords

Crack healing; Fatigue; High temperature strength; Machining; Si3N4; SiC; Structural ceramic

Indexed keywords

BENDING STRENGTH; COMPOSITE MATERIALS; CRACKS; FATIGUE OF MATERIALS; SILICON COMPOUNDS; STRENGTH OF MATERIALS; TEMPERATURE;

COMPOSITE CERAMIC; CRACK-HEALING BEHAVIOUR; MACHINING CRACKS;

CERAMIC MATERIALS;

EID: 38349077236     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2007.01196.x     Document Type: Article

References (34)

1. Riley, F. L. (2000) Silicon nitride and related materials. J. Am. Ceram. Soc. 83, 245-265.
2. Munz, D. and Fett, T. (1999) Ceramics: Mechanical Properties, Failure Behaviour, Materials Selction. Springer Verlag, Berlin, Germany.
3. Quinn, G. D., Ives, L. K. and Jahanmir, S. (2005) On the nature of machining cracks in ground ceramics: Part I: SRBSN strengths and fractographic analysis. Mach. Sci. Technol. 9, 169-210.
4. Quinn, G. D., Ives, L. K. and Jahanmir, S. (2005) On the nature of machining cracks in ground ceramics: Part II: Comparison to other silicon nitrides and damage maps. Mach. Sci. Technol. 9, 211-237.
5. Liu, T., Latella, B. A. and Zhang, L. (2001) Grinding of ceramics: Strength, surface features and grinding conditions. Key Eng. Mater. 196, 53-60.
6. Zhang, B. and Peng, X. (2000) Grinding damage prediction for ceramics via CDM model. J. Manuf. Sci. Eng. 122, 51-58.
7. Bandyopadhyay, B. P. (1995) The effect of grinding parameters on the strength and surface finish of two silicon nitride ceramics. J. Mater. Process. Technol. 53, 533-543.
8. 3 composites and its application to the highest structural integrity of machined components. J. Eur. Ceram. Soc. 25, 3495-3502.
9. 3/SiC nano-composite ceramics by crack-healing. J. Eur. Ceram. Soc. 27, 3261-3267.
10. Choi, S. R. and Tikare, V. (1992) Crack healing behavior of hot pressed silicon nitride due to oxidation. Scripta Metal. Mater. 26, 1263-1268.
11. Matsuo, Y., Ogasawara, T., Kimura, S., Sato, S. and Yasuda, E. (1991) The effects of annealing on surface machining damage of alumina ceramics. J. Ceram. Soc. Jpn. 99, 384-389 (in Japanese).
12. Liu, M., Takagi, J. and Tsukuda, A. (2002) Strength recovery of ground ceramics via electric furnace heating. J. Mater. Process. Tech. 127, 107-114.
13. Ando, K., Chu, M. C., Sato, S., Yao, F. and Kobayashi, Y. (1998) The study on crack healing behaviour of silicon nitride ceramics. J. Jpn. Soc. Mech. Eng. A 64, 1936-1942 (in Japanese).
14. 3-SiC nanocomposites. J. Am. Ceram. Soc. 78, 567-571.
15. Chou, I. A., Chan, H. M. and Harmer, M. P. (1998) Effect of annealing environment on the crack healing and mechanical behavior of silicon carbide reinforced alumina nanocomposites. J. Am. Ceram. Soc. 81, 1203-1208.
16. 4/SiC composite ceramics. Fatigue Fract. Eng. Mater. Struct. 21, 119-122.
17. 4/SiC composite ceramics. Fatigue Fract. Eng. Mater. Struct. 22, 897-903.
18. 4/SiC ceramics under cyclic stress and resultant fatigue strength at the healing temperature. J. Am. Ceram. Soc. 85, 2268-2272.
19. Kim, Y. W., Ando, K. and Chu, M. C. (2003) Crack healing behavior of liquid-phase-sintered silicon carbide ceramics. J. Am. Ceram. Soc. 86, 465-470.
20. 3/SiC composite using crack healing and a proof test. Fatigue Fract. Eng. Mater. Struct. 30, 599-607.
21. Ono, M., Ishida, W., Nakao, W., Ando, K., Mori, S. and Yokouchi, M. (2005) Crack healing behavior under stress, strength and fracture toughness of Mullite/SiC whisker composite ceramic. J. Soc. Mat. Sci. Jpn. 54, 207-214 (in Japanese).
22. 4/SiC and resultant cyclic fatigue strength at the healing temperature. J. Am. Ceram. Soc. 88, 645-651.
23. Nakao, W., Ono, M., Lee, S. K., Takahashi, K. and Ando, K. (2005) Critical crack-healing condition for SiC whisker reinforced alumina under stress. J. Eur. Ceram. Soc. 25, 3649-3655.
24. 4 from 300 K to 1673 K, In: The 6th International Conference on Durability and Fatigue, Fatigue 2007 (Edited by Bache, M. R., Blackmore, P. A., Cawte, E.R., Roberts, P. and Yates, J.R.). Engineering Integrity Society, UK, p. 11.2.
25. Yao, F., Ando, K., Chu, M. C. and Sato, S. (2000) Crack-healing behavior, high temperature and fatigue strength of SiC-reinforced silicon nitride composite. J. Mater. Sci. Lett. 19, 1081-1083.
26. Chase, M., Davies, C., Downey, J., Frurip, D., Mcdonald R. and Syverud, A. (1986) JANAF Thermodynamic Tables, 3rd Edition. American Chemical Society, American Institute of Physics, New York.
27. Japan Industrial Standard R1601. (1993) Testing Methods for Flexural Strength of High Performance Ceramics. Japan Standard Association, Tokyo, Japan.
28. Nishida, M. (1967) Stress Concentration. Morikita Publishing Co. Ltd., Tokyo, Japan (in Japanese)
29. Houjou, K., Ando, K., Liu, S. P. and Sato, S. (2004) Crack-healing and oxidation behavior of silicon nitride ceramics. J. Eur. Ceram. Soc. 24, 2329-2338.
30. Japan Industrial Standard R1625. (1996) Weibull Statistics of Strength Data for Fine Ceramics. Japan Standard Association, Tokyo, Japan.
31. Walpole, R. E. and Myers, R. H. (1993) Probability and Statistics for Engineers and Scientists, 5th Edition. Macmillan Publishing Co., New York, NY, USA.
32. Lee, S. K., Ishida, W. and Ando, K. (2003) Strength properties of crack-healed silicon-carbide ceramics. J. Soc. Mat. Sci. Jpn. 52, 674-680 (in Japanese).
33. 4/SiC crack-healed under cyclic stress. J. Eur. Ceram. Soc. 25, 1953-1959.
34. Quinn, G. D. (1990) Fracture mechanism maps for advanced structural ceramics. J. Mater. Sci. 25, 4361-4376.