Stress corrosion cracking of stainless steels and nickel alloys in high-temperature water

Corrosion

Volumn 64, Issue 1, 2008, Pages 15-29

  Andresen, P L ^a   Morra, M M ^a  

^a GE GLOBAL RESEARCH   (United States)

Author keywords

Corrosion potential; Crack growth rates; High temperature water; Mechanisms; Nickel; Stainless steel; Stress corrosion cracking; Stress intensity factor; Water chemistry

Indexed keywords

CORROSION RATE; CRACK PROPAGATION; NICKEL ALLOYS; STAINLESS STEEL; STRESS INTENSITY FACTORS; YIELD STRESS;

CORROSION POTENTIAL; CRACK GROWTH RATE; HIGH-TEMPERATURE WATER;

STRESS CORROSION CRACKING;

CORROSION RATE; CRACK PROPAGATION; NICKEL ALLOYS; STAINLESS STEEL; STRESS CORROSION CRACKING; STRESS INTENSITY FACTORS; YIELD STRESS;

EID: 38049037442     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278457     Document Type: Article

References (31)

1. F.P. Ford, P.L. Andresen, "Corrosion in Nuclear Systems: Environmentally Assisted Cracking in Light Water Reactors," in Corrosion Mechanisms, eds. P. Marcus, J. Ouder (New York, NY: Marcel Dekker, 1994), p. 501-546.
2. P.L. Andresen, F.P. Ford, Mater. Sci. Eng. A103 (1988): p. 167-183.
3. F.P. Ford, D.F. Taylor, P.L. Andresen, R.G. Ballinger, "Corrosion-Assisted Cracking of Stainless and Low-Alloy Steels in LWR Environments," EPRI Contract RP2006-6, Report NP5064M, February 1987.
4. P.L. Andresen, "Conceptual Similarities and Common Predictive Approaches for SCC in High-Temperature Water Systems," CORROSION/96, paper no. 258 (Houston, TX: NACE International, 1996).
5. P.L. Andresen, F.P. Ford, S.M. Murphy, J.M. Perks, "State of Knowledge of Radiation Effects on Environmental Cracking in Light Water Reactor Core Materials," Proc. 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 1990), p. 1-83 to 1-121.
6. P.L. Andresen, L.M. Young, "Characterization of the Roles of Electrochemistry, Convection, and Crack Chemistry in Stress Corrosion Cracking," Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 1995), p. 579-596.
7. P.L. Andresen, F.P. Ford, Corros. Sci. 38 (1996): p. 1,011-1,016.
8. G.R. Engelhardt, D.D. Macdonald, M. Urquidi-Macdonald, Corros. Sci. 41 (1999): p. 2,267-2,302 (see p. 2,288).
9. P.L. Andresen, P.W. Emigh, M.M. Morra, J. Hickling, "Effects of PWR Primary Water Chemistry and Deaerated Water on SCC," Proc. 12th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: The Minerals, Metals, and Materials Society [TMS], 2005).
10. P.L. Andresen, C.L. Briant, Corrosion 45 (1989): p. 448-463.
11. P.L. Andresen, C.L. Briant, "Role of S, P, and N Segregation on Intergranular Environmental Cracking of Stainless Steels in High-Temperature Water," Proc. 3rd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (New York, NY: American Institute of Mining, Metallurgical, and Petroleum Engineers [AIME], 1988), p. 371-382.
12. P.L. Andresen, Corrosion 44, 7 (1988): p. 450.
13. P.L. Andresen, "The Effects of Aqueous Impurities on Intergranular Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel," Final Report NP3384, Contract T115-3, EPRI, 1983.
14. L.W. Niedrach, J. Electrochem. Soc. 127 (1980): p. 2,122.
15. P.L. Andresen, T.M. Angeliu, L.M. Young. "Immunity, Thresholds, and Other SCC Fiction," Proc. Staehle Symp. on Chemistry and Electrochemistry of Corrosion and SCC Warrendale, PA: The Minerals, Metals, and Materials Society [TMS], 2001).
16. P.L. Andresen, "Perspective and Direction of Stress Corrosion Cracking in Hot Water," Proc. 10th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 2001).
17. P.L. Andresen, T.M. Angeliu. L.M. Young, W.R. Catlin, R.M. Horn, "Mechanisms and Kinetics of SCC in Stainless Steels," Proc. 10th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 2001).
18. P.L. Andresen, K. Gott, J.L. Nelson, "Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel in 288°C Water: A Five Laboratory Round Robin," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (New York, NY: American Institute of Mining, Metallurgical, and Petroleum Enigneers [AIME], 1999).
19. P.L. Andresen, T.M. Angeliu, W.R. Catlin, L.M. Young, R.M. Horn, "Effect of Deformation on SCC of Unsensitized Stainless Steel," CORROSION/2000, paper no. 203 (Houston, TX: NACE, 2000).
20. P.L. Andresen, T.M. Angeliu, L.M. Young, "Effect of Martensite and Hydrogen on SCC of Stainless Steels," CORROSION/2001, paper no. 01228 (Houston, TX: NACE, 2001).
21. P.L. Andresen, L.M. Young, P.W. Emigh, R.M. Horn, "Stress Corrosion Crack Growth Rate Behavior of Ni Alloys 182 and 600 in High-Temperature Water," CORROSION/2002, paper no. 02510 (Houston, TX: NACE, 2002).
22. P.L. Andresen, "SCC Testing and Data Quality Considerations," 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (New York, N Y: American Institute of Mining, Metallurgical, and Petroleum Enigneers [AIME], 1999).
23. D.S. Morton, S.A. Attanasio, J.S. Fish, M.K. Schurman, "Influence of Dissolved Hydrogen on Nickel Alloy SCC in High-Temperature Water," CORROSION/99, paper no. 447 (Houston, TX: NACE, 1999).
24. D.S. Morton, S.A. Attanasio, G.A. Young, P.L. Andresen, T.M. Angeliu, "The Influence of Dissolved Hydrogen on Nickel Alloy SCC: A Window to Fundamental Insight," CORROSION/2001, paper no. 117 (Houston, TX: NACE, 2001).
25. 2 Permeation in Alloy 600 and Stainless Steel, April 2001.
26. P.L. Andresen, "Irradiation-Assisted Stress Corrosion Cracking," in Stress Corrosion Cracking: Materials Performance and Evaluation, ed. R.H. Jones (Materials Park, OH: ASM International, 1992), p. 181-210.
27. A.J. Jacobs, "Hydrogen Buildup in Irradiated Type 304 Stainless Steel," 13th Symp. Radiation Induced Changes in Microstructure, eds. F.A. Garner, N.H. Packan, A.S. Kumar, STP 956, vol. 2 (West Conshohocken, PA: ASTM International, 1985), p. 239.
28. T. M. Karlsen, E. Hauso, "Qualification and Application of Instrumented Specimens for In-Core Studies on Cracking Behavior or Austenitic Stainless Steels," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (New York, NY: American Institute of Mining, Metallurgical, and Petroleum Engineers [AIME], 1999), p. 951-961.
29. T.M. Angeliu, P.L. Andresen, J.A. Sutliff, R.M. Horn, "Intergranular Stress Corrosion Cracking of Unsensitized Stainless Steels in BWR Environments," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (New York, NY: American Institute of Mining, Metallurgical, and Petroleum Engineers [AIME], 1999), p. 311-318.
30. T.M. Angeliu, P.L. Andresen, E. Hall, J.A. Sutliff, S. Sitzman, "Strain and Microstructure Characterization of Austenitic Stainless Steel Weld HAZs," CORROSION/2000, paper no. 186 (Houston, TX: NACE, 2000).
31. P. L. Andresen, "Similarity of Cold Work and Radiation Hardening in Enhancing Yield Strength and SCC Growth of Stainless Steel in Hot Water," CORROSION/2002, paper no. 02509 (Houston, TX: NACE, 2002).