Stress corrosion crack growth rate behavior of Ni alloys 182 and 600 in high temperature water

NACE - International Corrosion Conference Series

Volumn 2002-April, Issue , 2002, Pages

  Andresen, Peter L ^a   Young, Lisa M ^a   Emigh, Paul W ^a   Horn, Ron M ^a,b  

^a GE GLOBAL RESEARCH   (United States)

^b GE ENERGY   (United States)

Author keywords

Alloy 182; Alloy 600; Cold work; Crack growth rate corrosion potential; High temperature water; Sensitization; Stress corrosion cracking; Stress intensity factor; Water purity; Weld metal

Indexed keywords

BOILING WATER REACTORS; COLD WORKING; CORROSIVE EFFECTS; CRACKING (CHEMICAL); DYNAMIC LOADS; GROWTH RATE; HIGH TEMPERATURE CORROSION; NICKEL ALLOYS; PRESSURIZED WATER REACTORS; RESIDUAL STRESSES; SOFTWARE TESTING; STRESS ANALYSIS; STRESS INTENSITY FACTORS; TESTING; WELD DECAY; WELDS;

ALLOY 182; ALLOY 600; CORROSION POTENTIALS; HIGH-TEMPERATURE WATER; SENSITIZATION; WELD METAL;

STRESS CORROSION CRACKING;

EID: 85039430833     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (37)

1. th Int. Symp. on Env. Degr. of Materials in Nuclear Power Systems - Water Reactors, NACE, 2001.
2. th Int. Symp. on Env. Degr. of Materials in Nuclear Power Systems - Water Reactors, AIME, 1999.
3. th Int. Symp. on Env. Degr. of Materials in Nuclear Power Systems - Water Reactors, ANS, 1997.
4. F.P. Ford and P.L. Andresen, "Corrosion in Nuclear Systems: Environmentally Assisted Cracking in Light Water Reactors", in "Corrosion Mechanisms", Ed. P. Marcus and J. Ouder, Marcel Dekker, p.501-546, 1994.
5. P.L. Andresen, T.M. Angeliu, P.W. Emigh, L.M. Young and R.M Horn, "Crack Growth Rate Behavior of Ni Alloys", Corrosion/2000, Paper 00202, NACE, 2000.
6. P.L. Andresen, "Conceptual Similarities and Common Predictive Approaches for SCC in High Temperature Water Systems", Paper 96258, Corrosion/96, NACE, 1996.
7. P.L. Andresen, "Fracture Mechanics Data & Modeling of Environmental Cracking of Nickel-Base Alloys in High Temperature Water", Corrosion 47, December 1991, p. 917-938.
8. L. G. Ljungberg, D. Cubicciotti, and M. Trolle, "Crack Propagation in Alloys 600 and 182 in Simulated BWR Environment", Eighth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ANS, p.226, 1997.
9. See also L. G. Ljungberg, "Stress Corrosion Cracking of Alloys 600 and 182 in BWRs, Volume 1," SD 94-1103, ABB Atom Interim Report, September 1994.
10. "Integrity Evaluation for Future Operation: Virgil C. Summer Nuclear Plant Reactor Vessel Nozzle to Pipe Weld Regions", WCAP-15617, Rev. 0 (non-proprietary, from S. Carolina E&G to NRC), Dec 26, 2000.
11. Outlet Nozzle Cracking at Ringhals 4 PWR, Swedish Nuclear Inspectorate, 2001.
12. SCC of Alloy 182 weld metal in shroud support of Tsuruga-1 BWR, Japan, 1999.
13. P.L. Andresen, "SCC Testing and Data Quality Consideration", Proc. Ninth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, AIME, 1999.
14. P.L. Andresen, K. Gott and J.L. Nelson, "Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel in 288C Water: A Five Laboratory Round Robin", Proc. Ninth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, AIME, 1999.
15. P.L. Andresen, "IGSCC Crack Propagation Rate Measurement in BWR Environments: Executive Summary of a Round Robin Study", Report 98:27 ISSN 1104-1374, ISRN SKI-R-98/27-SE, SKI, Stockholm, 1999.
16. P.L. Andresen, "Experimental Quality Guidelines for SCC Testing", GE CRD, Schenectady, NY, Jan. 1998.
17. Y.J. Kim and P.L. Andresen, "Data Quality, Issues and Guidelines for ECP Measurements in High Temperature Water", Corrosion/2001, Paper 01137, NACE, 2001.
18. Int. Cooperative Group on Environmentally Assisted Cracking, Dr. John Hickling, Executive Secretary.
19. P.L. Andresen and C.L. Briant, "Environmentally Assisted Cracking of Types 304L/316L/316NG Stainless Steel in 288 C Water," Corrosion, Vol. 45, pp. 448-463, 1989.
20. P.L. Andresen and C.L. Briant, "Role of S, P and N Segregation on Intergranular Environmental Cracking of Stainless Steels in High Temperature Water," Proc. 3rd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, AIME, pp. 371-382, 1988.
21. P.L. Andresen, "Environmentally Assisted Growth Rate Response of Nonsensitized AISI 316 Grade Stainless Steels in High Temperature Water," Corrosion 44, 7, p. 450, 1988.
22. P.L. Andresen, "The Effects of Aqueous Impurities on Intergranular Stress Corrosion Cracking of Sensitized Type 304 Stainless Steel," Final Report NP3384 Contract T115-3, EPRI, 1983.
23. See also, "Innovations in Experimental Techniques for Testing in High Temperature Aqueous Environments," Report No. 81CRD088, GE-CRD, Schenectady, New York, 1981.
24. L.W. Niedrach, "A New Membrane Type pH Sensor for Use in High Temperature High Pressure Water", J Electrochem Soc 127, p. 2122, 1980.
25. P.L. Andresen, et al, "In-Reactor Monitoring for Component Life Prediction", Interim Technical Progress Report #2, EPRI project RP2006-17, August 1988.
26. P.L. Andresen, "Specific Anion and Corrosion Potential Effects on Environmentally Assisted Cracking in 288 °C Water", GE CRD Report 93CRD215, December 1993.
27. -8 m/cycle", E647-95a, 1997 Annual Book of ASTM Standards, Volume 03.01, ASTM, 1997.
28. P.L. Andresen, "Probabilistic Interpretation of SCC Initiation & Growth", Paper #99446, Corrosion/98, NACE, 1999.
29. P.L. Andresen, T.M. Angeliu, L.M. Young, W.R. Catlin, and R.M. Horn, "Mechanisms and Kinetics of SCC in Stainless Steels", Proc. Tenth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 2001.
30. P.L. Andresen, "Perspective and Direction of Stress Corrosion Cracking in Hot Water", Proc. Tenth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 2001.
31. T.M. Angeliu, P.L. Andresen, and M.L. Pollick, "Repassivation and Crack Propagation of Alloy 600 in 288C Water", Corrosion 53, p.114, 1997.
32. D.S. Morton, S.A. Attanasio, J.S. Fish, and M.K. Schurman, "Influence of Dissolved Hydrogen on Nickel Alloy SCC in High Temperature Water", Corrosion/99, Paper 99447, NACE, 1999.
33. C.D. Thompson, D.M. Carey, and N.L. Perazzo, "Effects of Hydrogen on Electropotential Monitoring of Stress Corrosion Crack Growth", Eighth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ANS, p. 366, 1997.
34. P.L. Andresen, Unpublished results on hydrogen permeation in Ni alloys in hot water, GE Corporate R&D Center, Schenectady, NY, 1999.
35. 2 on Nickel Alloy SCC: A Window to Fundamental Insight", Corrosion/2001, #01117, NACE, 2001.
36. P.L. Andresen, T.M. Angeliu and L.M. Young, "Immunity, Thresholds, and Other SCC Fiction", Proc. Staehle Symp. on Chemistry and Electrochemistry of Corrosion and SCC, TMS, Feb. 2001.
37. S.A. Attanasio, D.S. Morton, M.A. Ando, N.F. Panayotou, C.D. Thompson, "Measurement of the Ni/NiO Phase Transition in High Temperature Hydrogenated Water Using the Contact Electric Resistance (CER) Technique", Proc. Tenth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 2001.