Multiple fatigue crack growth in pre-corroded 2024-T3 aluminum

Author keywords

2024 T3 aluminum; Corrosion fatigue; Multiple cracking; Pitting

Indexed keywords

ALUMINUM; CHEMICAL ANALYSIS; CORROSION FATIGUE; FRACTOGRAPHY; FRACTURE MECHANICS; NUCLEATION;

EID: 27144505159     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.06.026     Document Type: Conference Paper
Times cited : (78)

References (24)
  • 3
    • 0035105216 scopus 로고    scopus 로고
    • Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: Modeling and experimental studies
    • K.K. Sankaran, R. Perez, and K.V. Jata Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: modeling and experimental studies Mater Sci Eng A297 2001 223 229
    • (2001) Mater Sci Eng , vol.297 , pp. 223-229
    • Sankaran, K.K.1    Perez, R.2    Jata, K.V.3
  • 4
    • 0037408152 scopus 로고    scopus 로고
    • Fatigue crack growth from corrosion damage in 7075-T6511 aluminum alloy under aircraft loading
    • D.L. DuQuesnay, P.R. Underhill, and H.J. Britt Fatigue crack growth from corrosion damage in 7075-T6511 aluminum alloy under aircraft loading Int J Fatigue 25 2003 371 377
    • (2003) Int J Fatigue , vol.25 , pp. 371-377
    • Duquesnay, D.L.1    Underhill, P.R.2    Britt, H.J.3
  • 5
    • 0242490142 scopus 로고    scopus 로고
    • Corrosion pit size distributions and fatigue lives - A study of the EIFS technique for fatigue design in the presence of corrosion
    • J.J. Medved, M. Breton, and P.E. Irving Corrosion pit size distributions and fatigue lives - a study of the EIFS technique for fatigue design in the presence of corrosion Int J Fatigue 26 2004 71 80
    • (2004) Int J Fatigue , vol.26 , pp. 71-80
    • Medved, J.J.1    Breton, M.2    Irving, P.E.3
  • 6
    • 0031121892 scopus 로고    scopus 로고
    • Effects of prior corrosion on the S/N fatigue performance of aluminum sheet alloys 2024-T3 and 2524-T3
    • W.A. Van Der Sluys R.S. Piascik R. Zawierucha ASTM
    • G.H. Bray, R.J. Bucci, E.L. Colvin, and M. Kulak Effects of prior corrosion on the S/N fatigue performance of aluminum sheet alloys 2024-T3 and 2524-T3 W.A. Van Der Sluys R.S. Piascik R. Zawierucha Effects of the environment on the initiation of crack growth, ASTM STP 1298 1997 ASTM 89 103
    • (1997) Effects of the Environment on the Initiation of Crack Growth, ASTM STP 1298 , pp. 89-103
    • Bray, G.H.1    Bucci, R.J.2    Colvin, E.L.3    Kulak, M.4
  • 8
    • 0034246471 scopus 로고    scopus 로고
    • On fatigue crack initiation from corrosion in 7075-T7351aluminum alloy
    • P.S. Pao, S.J. Gill, and C.R. Feng On fatigue crack initiation from corrosion in 7075-T7351aluminum alloy Scripta Mater 43 2000 391 396
    • (2000) Scripta Mater , vol.43 , pp. 391-396
    • Pao, P.S.1    Gill, S.J.2    Feng, C.R.3
  • 12
    • 0038195283 scopus 로고    scopus 로고
    • Copyright © 1984-2002 by The Mathworks, Inc., Natick, MA, USA
    • ® Version 6.5.0.180913a Release 13, Copyright © 1984-2002 by The Mathworks, Inc., Natick, MA, USA, www.mathworks.com.
    • ® Version 6.5.0.180913a Release 13
  • 15
    • 0033078998 scopus 로고    scopus 로고
    • Fatigue-life prediction methodology using small-crack theory
    • J.C. Newman Jr, E.P. Phillips, and M.H. Swain Fatigue-life prediction methodology using small-crack theory Int J Fatigue 21 2 1999 109 119
    • (1999) Int J Fatigue , vol.21 , Issue.2 , pp. 109-119
    • Newman Jr., J.C.1    Phillips, E.P.2    Swain, M.H.3
  • 21
    • 0034831194 scopus 로고    scopus 로고
    • Variation of the stress intensity factor along the crack front of interacting semi-elliptical surface cracks
    • N.A. Noda, K. Kobayashi, and T. Oohashi Variation of the stress intensity factor along the crack front of interacting semi-elliptical surface cracks Arch Appl Mech 71 2001 43 52
    • (2001) Arch Appl Mech , vol.71 , pp. 43-52
    • Noda, N.A.1    Kobayashi, K.2    Oohashi, T.3
  • 22
    • 0028575028 scopus 로고
    • Estimating the elastic interaction factors of two coplanar surface cracks under mode i load
    • T.H. Leek, and I.C. Howard Estimating the elastic interaction factors of two coplanar surface cracks under mode I load Int J Pressure Vessels Piping 60 1994 307 321
    • (1994) Int J Pressure Vessels Piping , vol.60 , pp. 307-321
    • Leek, T.H.1    Howard, I.C.2
  • 23
    • 0024622758 scopus 로고
    • A numerical investigation of the interaction and coalescence of twin coplanar semi-elliptical fatigue cracks
    • K. Kishimoto, W.O. Soboyejo, R.A. Smith, and J.F. Knott A numerical investigation of the interaction and coalescence of twin coplanar semi-elliptical fatigue cracks Int J Fatigue 11 2 1989 91 96
    • (1989) Int J Fatigue , vol.11 , Issue.2 , pp. 91-96
    • Kishimoto, K.1    Soboyejo, W.O.2    Smith, R.A.3    Knott, J.F.4
  • 24
    • 0040282791 scopus 로고
    • A numerical simulation of fatigue growth of multiple surface initially semicircular defects under tension
    • X.B. Lin, and R.A. Smith A numerical simulation of fatigue growth of multiple surface initially semicircular defects under tension Int J Pressure Vessels Piping 62 1995 281 289
    • (1995) Int J Pressure Vessels Piping , vol.62 , pp. 281-289
    • Lin, X.B.1    Smith, R.A.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.