Nondestructive impedance spectroscopy evaluation of the bond coat oxidation in thermal barrier coatings

Surface Review and Letters

Volumn 14, Issue 5, 2007, Pages 935-943

  Yang, L ^a   Zhou, Y C ^a   Mao, W G ^a   Liu, Q X ^a  

^a XIANGTAN UNIVERSITY   (China)

Author keywords

Air plasma sprayed thermal barrier coatings; Impedance spectroscopy; NiCrAIY bond coat; Oxidation

Indexed keywords

ALUMINA; ENERGY DISPERSIVE SPECTROSCOPY; EQUIVALENT CIRCUITS; OXIDATION; SCANNING ELECTRON MICROSCOPY;

AIR PLASMA SPRAYED (APS); IMPEDANCE MEASUREMENTS; IMPEDANCE SPECTROSCOPY; ISOTHERMAL OXIDATION; THERMALLY GROWN OXIDE (TGO);

THERMAL BARRIER COATINGS;

EID: 35448979826     PISSN: 0218625X     EISSN: None     Source Type: Journal    
DOI: 10.1142/S0218625X07010494     Document Type: Article

References (26)

1. R. A. Miller, Current status of thermal barrier coatings -An overview, Surf. Coat. Technol. 88 (1987) 321-330.
2. J. W. Vogan, L. Hsu and A. R. Stetson, Thermal barrier coatings for thermal insulation and corrosion resistance in industrial gas turbine engines, Thin Solid Films 84(1) (1981) 75-87.
3. Y. C. Zhou, T. Tonomori, A. Yoshida, G. Bignall and T. Hashida, Fracture characteristics of thermal barrier coatings after tensile and bending tests, Surf. Coat. Technol. 157 (2002) 118-127.
4. S. Sridharana, L. Xiea, E. H. Jordanb, M. Gella and K. S. Murphyc, Damage evolution in an electron beam physical vapor deposited thermal barrier coating as a function of cycle temperature and time, Mater. Sei. Eng. A 393 (2005) 51-62.
5. J. Liu, J. W. Byeon and Y. H. Sohn, Effects of phase constituents/ microstructure of thermally grown oxide on the failure of EB-PVD thermal barrier coating with NiCoCrAIY bond coat, Surf. Coat. Technol. 200(20-21) (2006) 5869-5876.
6. V. K. Tolpygo, D. R. Clarke and K. S. Murphy, Evaluation of interface degradation during cyclic oxidation of EB-PVD thermal barrier coatings and correlation with TGO luminescence, Surf. Coat. Technol. 188-189 (2004) 62-70.
7. W. R. Chen, X. Wu, B. R. Marple and P. C. Patnaik, Modification of oxide layer in plasma-sprayed thermal barrier coating, Surf. Coat. Technol 201(2-4) (2006) 5863-5868.
8. M. J. Pomeroy, Coatings for gas turbine materials and long term stability issues, Mater. Design 26 (2005) 223-231.
9. R. A. Miller and C. E. Lowell, Failure mechanisms of thermal barrier coatings exposed to elevated temperatures, Thin Solid Films 95(3) (1982) 265-273.
10. X. Wang, J. Mei and P. Xiao, Non-destructive evaluation of thermal barrier coatings using impedance spectroscopy, Surf. Coat. Technol. 21 (2001) 855-859.
11. B. Jayaraj, S. Vishweswaraiah, V. H. Desai and Y. H. Sohn, Electrochemical impedance spectroscopy of thermal barrier coatings as a function of isothermal and cyclic thermal exposure, Surf. Coat. Technol. 177-178 (2004) 140-151.
12. M. S. Ali, S. Song and P. Xiao, Evaluation of degradation of thermal barrier coatings using impedance spectroscopy, J. Eur. Ceram. Soc. 22 (2002) 101-107.
13. N. Q. Wu, K. Ogawa, M. Chyu and S. X. Mao, Failure detection of thermal barrier coatings using impedance spectroscopy, Thin Solid Films 457 (2004) 301-306.
14. C. X. Zhang, C. G. Zhou, S. K. Gong, H. F. Li and H. B. Xu, Evaluation of thermal barrier coating exposed to different oxygen partial pressure environments by impedance spectroscopy, Surf. Coat. Technol. 13(3-4) (2005) 315-322.
15. H. Brodin and M. Eskner, The influence of oxidation on mechanical and fracture behaviour of an airplasma-sprayed NiCoCrAIY bondcoat, Surf. Coat. Technol. 187 (2004) 113-121.
16. D. StoÈver and C. Funkel, Directions of the development of thermal barrier coatings in energyapplications, J. Mater. Process. Technol. 92-93 (1999) 195-202.
17. P. Scardi, L. Lutterotti and E. Galvanetto, Microstructural characterization of plasma-sprayed zirconia thermal barrier coatings by X-ray diffraction full pattern analysis, Surf. Coat. Technol. 61(1-3) (1993) 52-59.
18. 3 compositions for potential thermal barrier coating applications, Acta Materialia 54(6) (2006) 1615-1621.
19. T. Hilpert and E. Ivers-Tiffee, Correlation of electrical and mechanical properties of zirconia based thermal barrier coatings, Solid State Ionics 175 (2004) 471-476.
20. H. Brodin and M. Eskner, The influence of oxidation on mechanical and fracture behaviour of an air plasma-sprayed NiCoCrAIY bondcoat, Surf. Coat. Technol. 187 (2004) 113-121.
21. L. D. Xie, E. H. Jordan, N. P. Padture and M. Gell, Phase and microstructural stability ofsolution precursor plasma sprayed thermal barrier coatings, Mater. Sei. Eng. A 381 (2004) 189-195.
22. J. P Zhou, Matlab 6.5 Graph and Image Processing and Application Illustration (Science Press, Beijing, 2003) (in Chinese).
23. S. H. Song and P. Xiao, An impedance spectroscopy study of high-temperature oxidation of thermal barrier coatings, Mater. Sei. Eng. B 97 (2003) 46-53.
24. 3 and thermally grown oxide on nickel aluminide, Mater. Sei. Eng. A 372 (2004) 278-286.
25. J. W. Byeon, B. Jayaraj, S. Vishweswaraiah, S. Rhee, V. H. Desai and Y. H. Sohn, Non-destructive evaluation of degradation in multi-layered thermal barrier coatings by electrochemical impedance spectroscopy, Mater. Sei. Eng. A 407 (2005) 213-225.
26. Lassia, Electrochemical impedance spectroscopy and its applications, in Modern Aspects of Electrochemistry, eds. B. E. Conway, J. O' M. Bockris and R. E. White, Vol. 32 (Kluwer Academic/Plenum Publishers, New York, 1999), Ch. 2A.