Coatings for gas turbine materials and long term stability issues

Materials and Design

Volumn 26, Issue 3, 2005, Pages 223-231

  Pomeroy, Michael J ^a  

^a UNIVERSITY OF LIMERICK   (Ireland)

Author keywords

Aluminide coatings; Gas turbine materials; Interdiffusion; MCrAlY coatings; TBCs

Indexed keywords

CORROSION PREVENTION; HIGH TEMPERATURE EFFECTS; NICKEL ALLOYS; OXIDATION; PROTECTIVE COATINGS; THERMAL BARRIER COATINGS;

BOND COATS; INTERDIFFUSION;

GAS TURBINES;

ALUMINIDE; COATING; CORROSION PREVENTION; GAS TURBINE;

EID: 10444259790     PISSN: 02613069     EISSN: 18734197     Source Type: Journal    
DOI: 10.1016/j.matdes.2004.02.005     Document Type: Article

References (36)

1. Sims C.T. Stoloff N.S. Hagel W.C. Superalloys II 1987 Wiley New York
2. Caron P. Khan T. Evolution of Ni-based superalloys for single crystal gas turbine blade applications Aerospace Sci. Technol. 3 8 1999 513-523
3. Viswanathan R. An investigation of blade failures in combustion turbines Eng. Fail. Anal. 8 5 2001 493-511
4. Nicholls J.R. Simms N.J. Chan W. Evans H.E. Smart overlay coatings-concept and practice Surf. Coat. Technol. 149 2-3 2002 236-244
5. Eliaz N. Shemesh G. Latanision R.M. Hot corrosion in gas turbine components Eng.Fail. Anal. 9 1 2002 31-43
6. Goward G.W. Progress in coatings for gas turbine airfoils Surf. Coat. Technol. 109 1-3 1998 73-79
7. Wood G.C. Stott F.H. Oxidation of alloys Mater. Sci. Technol. 3 7 1987 519-530
8. Mevrel R. Cyclic oxidation of high-temperature alloys Mater. Sci. Technol. 3 7 1987 531-535
9. Pint B.A. Experimental observations in support of the dynamic - segregation theory to explain the reactive-element effect Oxid. Met. 45 1-2 1996 1-37
10. Pichoir R. Hauser J.M. Current status of coatings for high temperature applications. In: Environmental degradation of high temperature materials. Inst. Metall. Spring Residential Conf., Series 3, Number 13, Vol. 1; 1980. p. 6/1-6/21
11. Warnes B.M. Punola D.C. Clean diffusion coatings by chemical vapor deposition Surf. Coat. Technol. 94-95 1-3 1997 1-6
12. Voudouris N. Christoglou C. Angelopoulos G.N. Formation of aluminide coatings on nickel by a fluidised bed CVD process Surf. Coat. Technol. 141 2-3 2001 275-282
13. Squillace A. Bonetti R. Archer N.J. Yeatman J.A. The control of the composition and structure of aluminide layers formed by vapour aluminising Surf. Coat. Technol. 120-121 1999 118-123
14. Stringer J. Role of coatings in energy producing systems: An overview Mater. Sci. Eng. 87 1987 1-10
15. Itoh Y. Tamura M. Reaction diffusion behaviors for interface between Ni-based super alloys and vacuum plasma sprayed MCrAlY coatings J. Eng. Gas. Turb. Power 121 3 1999 476-483
16. Castle A.R. Gabe D.R. Chromium diffusion coatings Int. Mater. Rev. 44 2 1999 37-58
17. Krishna G.R. Das D.K. Singh V. Joshi S.V. Role of Pt content in the microstructural development and oxidation performance of Pt-aluminide coatings produced using a high-activity aluminizing process Mater. Sci. Eng. A 251 1-2 1998 40-47
18. Leyens C. Pint B.A. Wright I.G. Effect of composition on the oxidation and hot corrosion resistance of NiAl doped with precious metals Surf. Coat. Technol. 133 2000 15-22
19. Zhang Y. Haynes J.A. Lee W.Y. Wright I.G. Pint B.A. Cooley K.M. et al. Synthesis and cyclic oxidation behavior of a (Ni, Pt) Al coating on a desulfurized Ni-base superalloy Metall Mater Trans A 30 10 1999 2679-2687
20. Zhang Y. Haynes J.A. Lee W.Y. Wright I.G. Pint B.A. Cooley K.M. et-al. Effects of Pt incorporation on the isothermal oxidation behavior of chemical vapor deposition aluminide coatings Metall. Mater. Trans. A 32 7 2001 1727-1741
21. Purvis A.L. Warnes B.M. The effects of platinum concentration on the oxidation resistance of superalloys coated with single-phase platinum aluminide Surf. Coat. Technol. 146 2001 1-6
22. Basuki E. Crosky A. Gleeson B. Interdiffusion behaviour in aluminide-coated Rene 80H at 1150 °C Mater. Sci. Eng. A 224 1-2 1997 27-32
23. Chen J.H. Little J.A. Degradation of the platinum aluminide coating on CMSX4 at 1100 °C Surf. Coat. Technol. 92 1-2 1997 69-77
24. Bressers J. Arrell D.J. Ostolaza K. Valles J.L. Effect of an aluminide coating on precipitate rafting in superalloys Mater. Sci. Eng. A 220 1-2 1996 147-154
25. Feng H. Biermann H. Mughrabi H. Microstructure-based 3D finite element modelling of lattice misfit and long-range internal stresses in creep-deformed nickel-base superalloy single crystals Mater. Sci. Eng. A 214 1996 1-16
26. Blavette D. Cadel E. Deconihout B. The role of the atom probe in the study of nickel-based superalloys Mater. Charact. 44 2000 133-137
27. Brindley W.J. Miller R.A. TBCs for better engine efficiency Adv. Mater. Process. 8 1989 29-36
28. Miller RA. Thermal barrier coatings for aicraft engines - history and directions, in: Proceedings of the Thermal Barrier Coating Workshop. NASA as NASA Conference Publication 3312; 1935. p. 17-34
29. Sohn Y.H. Biederman R.R. Sisson R.D.Jr. Microstructural development in physical vapour-deposited partially stabilized zirconia thermal barrier coatings Thin Solid Films 250 1-2 1994 1-7
30. Shillington E.A.G. Clarke D.R. Spalling failure of a thermal barrier coating associated with aluminum depletion in the bond-coat Acta Mater. 47 4 1999 1297-1305 MAR 10 1999
31. Tolpygo V.K. Clarke D.R. Murphy K.S. Oxidation-induced failure of EB-PVD thermal barrier coatings Surf. Coat. Technol. 146 2001 124-131
32. Evans A.G. Mumm D.R. Hutchinson J.W. Meier G.H. Pettit F.S. Mechanisms controlling the durability of thermal barrier coatings Prog. Mater. Sci. 46 5 2001 505-553
33. Yanar N.M. Meier G.H. Pettit F.S. The influence of platinum on the failure of EBPVD YSZ TBCs on NiCoCrAlY bond coats Scr. Mater. 46 4 2002 325-330
34. Clarke D.R. Christensen R.J. Tolpygo V. The evolution of oxidation stresses in zirconia thermal barrier coated superalloy leading to spalling failure Surf. Coat. Technol. 94-95 1-3 1997 89-93
35. Tolpygo V.K. Clarke D.R. Surface rumpling of a (Ni, Pt) Al bond coat induced by cyclic oxidation Acta Mater. 48 13 2000 3283-3293
36. Kim G.M. Yanar N.M. Hewitt E.N. Pettit F.S. Meier G.H. The effect of the type of thermal exposure on the durability of thermal barrier coatings Scr. Mater. 46 7 2002 489-495