Contact strength of ceramic laminates

Composites Science and Technology

Volumn 68, Issue 1, 2008, Pages 209-214

  Ceseracciu, Luca ^a   Jiménez Piqué, Emilio ^a   Fett, Theo ^b   Anglada, Marc ^a  

^a UNIVERSITAT POLITÈCNICA DE CATALUNYA   (Spain)

^b UNIVERSITY OF KARLSRUHE   (Germany)

Author keywords

A. Layered structures; B. Contact strength; C. Finite element analysis (FEA); C. Residual stresses

Indexed keywords

BRITTLENESS; CERAMIC MATERIALS; COMPOSITE STRUCTURES; FINITE ELEMENT METHOD; FRACTURE TOUGHNESS; RESIDUAL STRESSES; STRENGTH OF MATERIALS;

CERAMIC LAMINATES; CONTACT STRENGTH; HERTZIAN-LIKE STRESS STATE; LAYERED STRUCTURES;

LAMINATES;

CERAMICS; FAILURE ANALYSIS; FINITE ELEMENT ANALYSIS; FRACTURE; LAMINATE; STRENGTH; STRESS; TESTING; TOUGHNESS;

EID: 35448937152     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compscitech.2007.04.020     Document Type: Article

References (16)

1. Chan H.M. Layered ceramics: processing and mechanical behavior. Ann Rev Mater Sci 27 (1997) 249-282
2. Prakash O., Sarkar P., and Nicholson P.S. Crack deflection in ceramic/ceramic laminates with strong interfaces. J Am Ceram Soc 78 4 (1995) 1125-1127
3. Bermejo R., Torres Y., Sanchez-Herencia A.J., Baudin C., Anglada M., and Llanes L. Residual stresses, strength and toughness of laminates with different layer thickness ratios. Acta Mater 54 18 (2006) 4745-4757
4. Clegg W.J., Kendall K., Alford N.McN., Button T.W., and Birchall J.D. Simple way to make tough ceramics. Nature 347 6292 (1990) 445-457
5. de Portu G., Micele L., and Pezzotti G. Laminated ceramic structures from oxide systems. Composites Part B 37 (2006) 556-567
6. 2 composites strengthened by transformation-induced residual stresses. J Am Ceram Soc 71 12 (1988) C501-C505
7. Chen C.R., Pascual J., Fischer F.D., Kolednik O., and Danzer R. Prediction of the fracture toughness of a ceramic multilayer composite - modeling and experiments. Acta Mater 55 2 (2007) 409-421
8. Pavon J., Jiménez-Piqué E., Anglada M., Saiz E., and Tomsia A.P. Monotonic and cyclic Hertzian fracture of a glass coating on titanium-based implants. Acta Mater 54 13 (2006) 3593-3603
9. Toschi F., Melandri C., Pinasco P., Roncari E., Guicciardi S., and de Portu G. Influence of residual stresses on the wear behavior of alumina/alumina-zirconia laminated composites. J Am Ceram Soc 86 9 (2003) 1547-1553
10. Jiménez-Piqué E., Ceseracciu L., Chalvet F., Anglada M., and de Portu G. Hertzian contact fatigue on alumina/alumina-zirconia laminated composites. J Eur Ceram Soc 25 15 (2005) 3393-3401
11. Ceseracciu L., Chalvet F., de Portu G., Anglada M., and Jiménez-Piqué E. Surface contact degradation of multilayer ceramics under cyclic subcritical loads and high number of cycles. Int J Refr Hard Mater 23 4-6 (2005) 375-381
12. Fett T., Munz D., and Thun G. Test devices for strength measurements of bars under contact loading. J Test Eval 29 1 (2001) 1-10
13. Fett T., and Munz D. Influence of stress gradients on failure in contact strength tests with cylinder loading. Engng Fract Mech 69 (2002) 1353-1361
14. Fett T., Creek D., Badenheim D., and Oberacker R. Crack growth data from dynamic tests under contact loading. J Eur Ceram Soc 24 (2004) 2049-2054
15. Hillman C., Suo Z., and Lange F.F. Cracking of laminates subjected to biaxial tensile stress. J Am Ceram Soc 78 8 (1996) 2127-2133
16. Nagl M.M., Llanes L., Fernández R., and Anglada M. The fatigue behaviour of Mg-PSZ and ZTA ceramics. Fracture of Mechanics 12 (1996), Plenum Press p. 61-76