Characterization and modeling of fracture and damage behavior of notched woven fabric GFRP laminates under three-point bending at cryogenic temperatures

Author keywords

Composite materials; Cryomechanics; Damage mechanics; Finite element method; Fracture mechanics; Fracture toughness; Material testing; Single edge notched bend specimen; Superconducting magnet

Indexed keywords

COMPOSITE MATERIALS; FINITE ELEMENT METHOD; FRACTURE MECHANICS; FRACTURE TOUGHNESS; SUPERCONDUCTING MAGNETS;

EID: 34548524989     PISSN: 07316844     EISSN: 15307964     Source Type: Journal    
DOI: 10.1177/0731684407079775     Document Type: Article
Times cited : (9)

References (21)
  • 1
    • 0029409899 scopus 로고
    • Initial Results from the Testing of Potential ITER Insulation Materials
    • Broadbent, A.J., Crozier, J., Smith, K.D., Street, A.J. and Wiatrzyk, J.M. (1995). Initial Results from the Testing of Potential ITER Insulation Materials, Cryogenics, 35 (11). 701 - 703.
    • (1995) Cryogenics , vol.35 , Issue.11 , pp. 701-703
    • Broadbent, A.J.1    Crozier, J.2    Smith, K.D.3    Street, A.J.4    Wiatrzyk, J.M.5
  • 4
    • 0021973341 scopus 로고
    • Fracture Behavior of Cross-Ply Graphite/Epoxy Laminates
    • Garg, A. (1985). Fracture Behavior of Cross-Ply Graphite/Epoxy Laminates, Engineering Fracture Mechanics, 22 (6). 1035 - 1048.
    • (1985) Engineering Fracture Mechanics , vol.22 , Issue.6 , pp. 1035-1048
    • Garg, A.1
  • 5
    • 7044235938 scopus 로고    scopus 로고
    • Mode-I Fracture Toughness Testing of Thick Section FRP Composites using the ESE(T) Specimen
    • El-Hajjar, R. and Haj-Ali, R. (2005). Mode-I Fracture Toughness Testing of Thick Section FRP Composites using the ESE(T) Specimen, Engineering Fracture Mechanics, 72 (4). 631 - 643.
    • (2005) Engineering Fracture Mechanics , vol.72 , Issue.4 , pp. 631-643
    • El-Hajjar, R.1    Haj-Ali, R.2
  • 6
    • 13444275996 scopus 로고    scopus 로고
    • Fracture Behavior of G-10 Woven Glass-Epoxy Laminates at Low Temperatures
    • Shindo, Y., Sanada, K. and Horiguchi, K. (1996). Fracture Behavior of G-10 Woven Glass-Epoxy Laminates at Low Temperatures, Advances in Cryogenic Engineering, 42 (A). 129 - 136.
    • (1996) Advances in Cryogenic Engineering , vol.42 , Issue.A , pp. 129-136
    • Shindo, Y.1    Sanada, K.2    Horiguchi, K.3
  • 7
    • 0029657071 scopus 로고    scopus 로고
    • Effect of Various Approximations on Predicted Progressive Failure in Plain Weave Composites
    • Whitcomb, J. and Srirengan, K. (1996). Effect of Various Approximations on Predicted Progressive Failure in Plain Weave Composites, Composite Structure, 34 (1). 13 - 20.
    • (1996) Composite Structure , vol.34 , Issue.1 , pp. 13-20
    • Whitcomb, J.1    Srirengan, K.2
  • 9
    • 28544444261 scopus 로고    scopus 로고
    • Finite Element Continuum Damage Modeling of Plain Weave Reinforced Composites
    • Barbero, E.J., Lonetti, P. and Sikkil, K.K. (2006). Finite Element Continuum Damage Modeling of Plain Weave Reinforced Composites, Composites: Part B, 37 (2 - 3). 137 - 147.
    • (2006) Composites , vol.37 , Issue.2-3 , pp. 137-147
    • Barbero, E.J.1    Lonetti, P.2    Sikkil, K.K.3
  • 10
    • 21244478155 scopus 로고    scopus 로고
    • Cryogenic Damage and Fracture Behaviors of G-11 Woven Glass-Epoxy Laminates
    • Sanada, K. and Shindo, Y. (2005). Cryogenic Damage and Fracture Behaviors of G-11 Woven Glass-Epoxy Laminates, JSME International Journal, Series A, 48 (2). 91 - 99.
    • (2005) JSME International Journal , vol.48 , Issue.2 , pp. 91-99
    • Sanada, K.1    Shindo, Y.2
  • 11
    • 21744432832 scopus 로고    scopus 로고
    • Deformation and Progressive Failure Behavior of Woven-Fabric-Reinforced Glass/Epoxy Composite Laminates under Tensile Loading at Cryogenic Temperatures
    • Takeda, T., Takano, S., Shindo, Y. and Narita, F. (2005). Deformation and Progressive Failure Behavior of Woven-Fabric-Reinforced Glass/Epoxy Composite Laminates Under Tensile Loading at Cryogenic Temperatures, Composites Science Technology, 65 (11 - 12). 1691 - 1702.
    • (2005) Composites Science Technology , vol.65 , Issue.11-12 , pp. 1691-1702
    • Takeda, T.1    Takano, S.2    Shindo, Y.3    Narita, F.4
  • 13
    • 0032900211 scopus 로고    scopus 로고
    • Damage Accumulation in Woven-Fabric CFRP Laminates under Tensile Loading: Part 1. Observations of Damage Accumulation, Composites
    • Gao, F., Boniface, L., Ogin, S.L., Smith, P.A. and Greaves, R.P. (1999). Damage Accumulation in Woven-Fabric CFRP Laminates under Tensile Loading: Part 1. Observations of Damage Accumulation, Composites Science and Technology, 59 (1). 123 - 136.
    • (1999) Science and Technology , vol.59 , Issue.1 , pp. 123-136
    • Gao, F.1    Boniface, L.2    Ogin, S.L.3    Smith, P.A.4    Greaves, R.P.5
  • 14
    • 20344379423 scopus 로고    scopus 로고
    • Acoustic Emission and Fracture Behavior of GFRP Woven Laminates at Cryogenic Temperatures
    • Shindo, Y., Sumikawa, M., Narita, F. and Sanada, K. (2005). Acoustic Emission and Fracture Behavior of GFRP Woven Laminates at Cryogenic Temperatures, Cryogenics, 45 (6). 439 - 449.
    • (2005) Cryogenics , vol.45 , Issue.6 , pp. 439-449
    • Shindo, Y.1    Sumikawa, M.2    Narita, F.3    Sanada, K.4
  • 17
    • 0028528498 scopus 로고
    • A Micromechanics Model for Thermoelastic Properties of Plain Weave Fabric Composites
    • Hahn, H.T. and Pandey, R. (1994). A Micromechanics Model for Thermoelastic Properties of Plain Weave Fabric Composites, ASME Journal of Engineering Materials and Technology, 116 (4). 517 - 523.
    • (1994) ASME Journal of Engineering Materials and Technology , vol.116 , Issue.4 , pp. 517-523
    • Hahn, H.T.1    Pandey, R.2
  • 18
    • 0034781961 scopus 로고    scopus 로고
    • Analytical and Experimental Studies of Short-Beam Interlaminar Shear Strength of G-10CR Glass-Cloth/Epoxy Laminates at Cryogenic Temperatures
    • Shindo, Y., Wang, R. and Horiguchi, K. (2001). Analytical and Experimental Studies of Short-Beam Interlaminar Shear Strength of G-10CR Glass-Cloth/Epoxy Laminates at Cryogenic Temperatures, ASME Journal of Engineering Materials and Technology, 123 (1). 112 - 118.
    • (2001) ASME Journal of Engineering Materials and Technology , vol.123 , Issue.1 , pp. 112-118
    • Shindo, Y.1    Wang, R.2    Horiguchi, K.3
  • 19
    • 0001546191 scopus 로고
    • The Brittle Strength of Orthotropic Materials
    • Hoffman, O. (1967). The Brittle Strength of Orthotropic Materials, Journal of Composite Materials, 1 (2). 200 - 206.
    • (1967) Journal of Composite Materials , vol.1 , Issue.2 , pp. 200-206
    • Hoffman, O.1
  • 20
    • 84980287971 scopus 로고
    • A Path Independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks
    • Rice, J.R. (1968). A Path Independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks, ASME Journal of Applied Mechanics, 35: 379 - 386.
    • (1968) ASME Journal of Applied Mechanics , vol.35 , pp. 379-386
    • Rice, J.R.1
  • 21
    • 28144434727 scopus 로고    scopus 로고
    • Analysis of Mode i interlaminar fracture and damage behavior of GFRP woven laminates at cryogenic temperatures
    • Sumikawa, M., Shindo, Y., Takeda, T., Narita, F., Takano, S. and Sanada, K. (2005). Analysis of Mode I interlaminar fracture and damage behavior of GFRP woven laminates at cryogenic temperatures, Journal of Composite Materials, 39 (22). 2053 - 2066.
    • (2005) Journal of Composite Materials , vol.39 , Issue.22 , pp. 2053-2066
    • Sumikawa, M.1    Shindo, Y.2    Takeda, T.3    Narita, F.4    Takano, S.5    Sanada, K.6


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.