Progression markings, striations, and crack-arrest markings on fracture surfaces

Materials Science and Engineering: A

Volumn 468-470, Issue SPEC. ISS., 2007, Pages 74-80

  Lynch, S P ^a  

^a DEFENCE SCIENCE AND TECHNOLOGY ORGANISATION   (Australia)

Author keywords

Crack arrest markings; Environmental effects; Fractography; Fracture mechanisms; Progression markings; Striations

Indexed keywords

CRACKS; EMBRITTLEMENT; FATIGUE OF MATERIALS; FRACTOGRAPHY; FRACTURE; LIQUID METALS; STRESS CORROSION CRACKING;

CRACK-ARREST MARKINGS; PROGRESSION MARKINGS; STRIATIONS;

SURFACES;

CRACKS; EMBRITTLEMENT; FATIGUE OF MATERIALS; FRACTOGRAPHY; FRACTURE; LIQUID METALS; STRESS CORROSION CRACKING; SURFACES;

EID: 34548127960     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2006.09.083     Document Type: Article

References (51)

1. Gough H.J. The Fatigue of Metals (1926), Ernest Benn Ltd., London
2. Forsyth P.J.E. Int. J. Fatigue 5 January (1983) 3-14
3. Hardrath H.F., and McEvily A.J. Proceedings of the Crack Propagation Symposium, Cranfield, September 1961, vol. 1. The College of Aeronautics, Cranfield (1962) 231-270
4. Forsyth P.J.E. Scripta Metall. 10 (1976) 383-386
5. Bowen A.W., and Forsyth P.J.E. Mater. Sci. Eng. 49 (1981) 141-154
6. Lynch S.P., Radtke T.C., Wicks B.J., and Byrnes R.T. Fatigue Fracture Eng. Mater. Struct. 17 (1994) 297-311
7. Wanhill R.J.H. J. Failure Anal. Prev. 4 (2004) 53-61
8. Unpublished Work, DSTO, Australia.
9. Barter S., Molent L., Goldsmith N., and Jones R. Eng. Failure Anal. 12 (2005) 99-128
10. Wanhill R.J.H. Pract. Failure Anal. 3 (2003) 59-69
11. Forsyth P.J.E., and Ryder D.A. Metallurgica 63 (1961) 117-124
12. C.A. Zapffe, C.O. Worden, Preprint 32, ASM, 1950, and Trans. ASM 43 (1951) 958-969.
13. Crussard R. International Conference on Fatigue of Metals (1956), Inst. of Mech. Eng., London p. 748
14. Forsyth P.J.E., and Ryder D.A. Aircraft Eng. April (1960) 96-99
15. Davidson D.L., and Lankford J. Int. Mater. Rev. 37 (1992) 45-76 (and references therein)
16. Meyn D.A. Trans. ASM 61 (1968) 52-61
17. Nix K.J., and Flower H.M. Acta Metall. 30 (1982) 1549-1559
18. Pelloux R.M.N. Eng. Fracture Mech. 1 (1970) 697-704
19. Garrett G.C., and Knott J.F. Acta Metall. 23 (1975) 841-848
20. Grinberg N.M. Int. J. Fatigue 6 (1984) 229-242
21. Riemelmoser F.O., Pippan R., and Stüwe H.P. Acta Mater. 46 (1998) 1793-1799
22. McEvily A.J., and Gonzalez Velazquez J.L. Metal. Trans. 23A (1992) 2211-2221
23. Lynch S.P. Acta Metall. 36 (1988) 2639-2661 (and references therein)
24. Lynch S.P. Metallography 23 (1989) 147-171 (and references therein)
25. Lynch S.P. In: Moody N.R., Thompson A.W., Ricker R.E., Was G.W., and Jones R.H. (Eds). Hydrogen Effects on Materials Behavior and Corrosion Deformation Interactions (2003), TMS, Warrendale, PA 449-466 (and references therein)
26. Chen X., and Gerberich W.W. Metal. Trans. 22A (1991) 59-70
27. Birnbaum H.K., and Sofronis P. Mater. Sci. Eng. A176 (1994) 191-202
28. McEvily Jr. A.J., and Bond A.P. J. Electrochem. Soc. 112 (1965) 131-137
29. Scamans G.M. Metal. Trans. 11A (1980) 846-850
30. Flanagan W.F., and Lichter B.D. Int. J. Fracture 79 (1996) 121-135
31. Sieradzki K., and Newman R.C. Phil. Mag. A 51 (1985) 95-132
32. Brozova A., and Lynch S. CD-Rom of Proceedings of Second Int. Conf. on Environmental Degradation of Engineering Materials (EDEM 2003), Paper KN1-2-1. European Federation of Corrosion (2003)
33. Lukowswki J.T., Kasul D.B., Heldt L.A., and White C.A. Scripta Metall. Mater. 24 (1990) 1959-1964
34. Lynch S.P. In: Magnin T. (Ed). Second International Conference on Corrosion Deformation Interactions (CDI'96). Institute of Materials, London (1997) 206-219
35. Newman R.C., Shahrabi T., and Sieradzki K. Scripta Metall. 23 (1989) 71-74
36. Gangloff R.P. In: Milne I., Ritchie R.O., and Karihaloo B. (Eds). Comprehensive Structural Integrity vol. 6 (2003), Elsevier 31-101
37. Bika D., and McMahon Jr. C.J. Acta Mater. 43 (1995) 1909-1916
38. Krupp U. Int. Mater. Rev. 50 (2005) 83-97
39. Bertocci U., Pugh E.N., and Ricker R.E. In: Gangloff R.P., and Ives M.B. (Eds). Environment-Induced Cracking of Metals, NACE-10 (1990), NACE, Houston, TX 273-285
40. Smith E. Eng. Fracture Mech. 19 (1984) 601-604
41. Tetelman A.S., and Robertson W.D. Trans. Met. Soc. AIME 224 (1962) 775-783
42. Stringer J. Corros. Sci. 10 (1970) 513-543
43. Guo X., Gao K., Qiao L., and Chu W. Metall. Mater. Trans. 32A (2001) 1309-1312
44. Newman R.C., and Sieradzki K. Scripta Metall. 17 (1983) 621-624
45. Dickson J.I., Shiqiong Li., Bailon J.-P., and Tromans D. In: Bruemmer S.M., Meletis E.I., Jones R.H., Gerberich W.W., Ford F.P., and Staehle R.W. (Eds). Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, TMS. Warrendale, PA (1992) 303-322
46. Meletis E.I., Lian K., and Huang W. In: Magnin T., and Gras J.M. (Eds). Corrosion-Deformation Interactions (CDI'92). Les Editions de Physique Les Ulis, France (1993) 69-81
47. Aaltonen P., Saario T., Ehrnstén U., Itäaho M., and Hänninen H. In: Magnin T. (Ed). Second International Conference on Corrosion Deformation Interactions (CDI'96). Institute of Materials, London (1997) 35-44
48. Galvale J.R. In: Jones R.H. (Ed). Chemistry and Electrochemistry of Stress Corrosion Cracking: a Symposium Honoring the Contributions of R.W. Staehle, TMS. Warrendale, PA (2001) 27-44
49. Lynch S.P., Moutsos S., Gable B., Edwards D.P., and Muddle B.C. ECF-16. Alexandroupolis, Greece, July 3-7 (2006). 1-4020-4971-4 (E.E. Gdoutos (Ed.), Failure Analysis of Nano and Engineering Materials Structures, Springer Science)
50. Magnin T., Chambreuil A., and Bayle B. Acta Mater. 44 (1996) 1457-1470
51. Hintz M.B., Blanchard W.K., Brindley P.K., and Heldt L.A. Metall. Trans. 17A (1986) 1081-1086