Volumn 49, Issue 8, 2007, Pages 3303-3324

Influence of local stress on initiation behavior of stress corrosion cracking for sensitized 304 stainless steel

Author keywords

A. Stainless steel; B. In situ observation; B. Modeling studies; C. Crack initiation; C. Stress corrosion

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; IMAGE ANALYSIS; STAINLESS STEEL;

EID: 34347208245     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2007.01.011     Document Type: Article
Times cited : (43)

References (26)
  • 1
    • 0036778832 scopus 로고    scopus 로고
    • Influence of interaction between multiple cracks on stress corrosion crack propagation
    • Kamaya M., and Totsuka N. Influence of interaction between multiple cracks on stress corrosion crack propagation. Corrosion Science 44 (2002) 2333-2352
    • (2002) Corrosion Science , vol.44 , pp. 2333-2352
    • Kamaya, M.1    Totsuka, N.2
  • 2
    • 34347239062 scopus 로고    scopus 로고
    • ASME, Boiler and Pressure Vessel Code Section XI 2003 Addenda, ASME, New York, 2003.
  • 3
    • 34347265886 scopus 로고    scopus 로고
    • JSME, Fitness-For-Service Code S NA1-2004, JSME, Tokyo, 2004.
  • 4
    • 0036629595 scopus 로고    scopus 로고
    • Stress intensity factors of interacting parallel surface cracks
    • Kamaya M., and Kitamura T. Stress intensity factors of interacting parallel surface cracks. Transactions of JSME 68 (2002) 1112-1119
    • (2002) Transactions of JSME , vol.68 , pp. 1112-1119
    • Kamaya, M.1    Kitamura, T.2
  • 5
    • 0041826867 scopus 로고    scopus 로고
    • A crack growth evaluation method for multiple interacting cracks
    • Kamaya M. A crack growth evaluation method for multiple interacting cracks. JSME International Journal (Series A) 46 (2003) 15-23
    • (2003) JSME International Journal (Series A) , vol.46 , pp. 15-23
    • Kamaya, M.1
  • 7
    • 0022204214 scopus 로고
    • An experimental and statistical investigation of surface fatigue crack initiation and growth
    • Ochi Y., Ishii A., and Sasaki S.K. An experimental and statistical investigation of surface fatigue crack initiation and growth. Fatigue of Engineering Materials and Structures 8 (1985) 327-339
    • (1985) Fatigue of Engineering Materials and Structures , vol.8 , pp. 327-339
    • Ochi, Y.1    Ishii, A.2    Sasaki, S.K.3
  • 8
    • 0029395258 scopus 로고
    • The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: I - metallography
    • Wang Y.Z., Ebtehaj K., Hardie D., and Parkins R.N. The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: I - metallography. Corrosion Science 37 (1995) 1651-1675
    • (1995) Corrosion Science , vol.37 , pp. 1651-1675
    • Wang, Y.Z.1    Ebtehaj, K.2    Hardie, D.3    Parkins, R.N.4
  • 9
    • 0005156886 scopus 로고
    • An evaluation technique for fatigue life of multiple surface cracks (part I) a problem of multiple series surface cracks
    • Iida K., Ando K., and Hirata T. An evaluation technique for fatigue life of multiple surface cracks (part I) a problem of multiple series surface cracks. Journal of Marine Science and Technology 148 (1980) 284-293
    • (1980) Journal of Marine Science and Technology , vol.148 , pp. 284-293
    • Iida, K.1    Ando, K.2    Hirata, T.3
  • 10
    • 0005213349 scopus 로고
    • An evaluation technique for fatigue life of multiple surface cracks (part II) a problem of multiple parallel surface cracks
    • Ando K., Hirata T., and Iida K. An evaluation technique for fatigue life of multiple surface cracks (part II) a problem of multiple parallel surface cracks. Journal of Marine Science and Technology 153 (1983) 352-363
    • (1983) Journal of Marine Science and Technology , vol.153 , pp. 352-363
    • Ando, K.1    Hirata, T.2    Iida, K.3
  • 11
    • 0028439127 scopus 로고
    • Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near neutral pH
    • Parkins R.N., Blanchard Jr. W.K., and Delanty B.S. Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near neutral pH. Corrosion 50 (1994) 394-408
    • (1994) Corrosion , vol.50 , pp. 394-408
    • Parkins, R.N.1    Blanchard Jr., W.K.2    Delanty, B.S.3
  • 12
    • 0022902184 scopus 로고    scopus 로고
    • A.F. Grandt Jr., A.B. Thakker, D.E. Tritsch, An experimental and numerical investigation of the growth and coalescence of multiple fatigue cracks at notches, in: J.H. Underwood, R. Chait, C.W. Smith, D.P. Wilhem, W.A. Andrews, J.C. Newman (Eds.), Fracture Mechanics, vol. 17, ASTM STP 905, Philadelphia, 1986, pp. 239-252.
  • 14
    • 0024622758 scopus 로고
    • A numerical investigation of the interaction and coalescence of twin coplanar semi-elliptical fatigue cracks
    • Kishimoto K., Soboyejo W.O., Smith R.A., and Knott J.F. A numerical investigation of the interaction and coalescence of twin coplanar semi-elliptical fatigue cracks. International Journal of Fracture 11 (1989) 91-96
    • (1989) International Journal of Fracture , vol.11 , pp. 91-96
    • Kishimoto, K.1    Soboyejo, W.O.2    Smith, R.A.3    Knott, J.F.4
  • 15
    • 0029395255 scopus 로고
    • The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: III - Monte Carlo simulation
    • Wang Y.Z., Hardie D., and Parkins R.N. The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: III - Monte Carlo simulation. Corrosion Science 37 (1995) 1705-1720
    • (1995) Corrosion Science , vol.37 , pp. 1705-1720
    • Wang, Y.Z.1    Hardie, D.2    Parkins, R.N.3
  • 16
    • 0542397043 scopus 로고
    • Evaluation of creep fatigue damage based on initiation and growth of small cracks
    • Ainsworth R.A., and Skelton R.P. (Eds), Mechanical Engineering Publications, London
    • Kitamura T., Tada N., and Ohtani R. Evaluation of creep fatigue damage based on initiation and growth of small cracks. In: Ainsworth R.A., and Skelton R.P. (Eds). Behavior of Defects at High Temperatures, ESIS 15 (1993), Mechanical Engineering Publications, London 47-49
    • (1993) Behavior of Defects at High Temperatures, ESIS 15 , pp. 47-49
    • Kitamura, T.1    Tada, N.2    Ohtani, R.3
  • 17
    • 0017915918 scopus 로고    scopus 로고
    • H. Kitagawa, T. Fujita, K. Miyazawa, Small randomly distributed cracks in corrosion fatigue, in: Corrosion Fatigue Technology, ASTM STP 642, American Society for Testing and Materials, 1978, pp. 98-114.
  • 19
    • 84938291113 scopus 로고    scopus 로고
    • M. Kamaya, G. Chiba, N. Totsuka, N. Nakajima, Multiple Crack Initiation and Propagation Behavior of Stainless Steel in High Temperature Water Environment and Examination by a Simulation, CORROSION/2001, NACE International, Houston, 2001, paper no. 219.
  • 20
    • 11144310183 scopus 로고    scopus 로고
    • A simulation on growth of multiple small cracks under stress corrosion
    • Kamaya M., and Kitamura T. A simulation on growth of multiple small cracks under stress corrosion. International Journal of Fracture 130 (2004) 787-801
    • (2004) International Journal of Fracture , vol.130 , pp. 787-801
    • Kamaya, M.1    Kitamura, T.2
  • 21
    • 33747181928 scopus 로고    scopus 로고
    • Crack initiation model for sensitized 304 stainless steel in high temperature water
    • Kamaya M., and Haruna T. Crack initiation model for sensitized 304 stainless steel in high temperature water. Corrosion Science 48 (2006) 2442-2456
    • (2006) Corrosion Science , vol.48 , pp. 2442-2456
    • Kamaya, M.1    Haruna, T.2
  • 22
    • 34347208789 scopus 로고    scopus 로고
    • JIS, JIS-G0580, Japan Industrial Standards, 1986.
  • 23
    • 0042162137 scopus 로고
    • In situ observation of stress corrosion crack during slow strain rate test and estimation of the crack behavior by fracture mechanics and statistics
    • Shibata T., and Haruna T. In situ observation of stress corrosion crack during slow strain rate test and estimation of the crack behavior by fracture mechanics and statistics. Corrosion Engineering 41 (1992) 977-987
    • (1992) Corrosion Engineering , vol.41 , pp. 977-987
    • Shibata, T.1    Haruna, T.2
  • 24
    • 0034098584 scopus 로고    scopus 로고
    • A HSAB concept applied to inhibition effect of anions on IGSCC of sensitized type 304 stainless steel
    • Zhang S., Shibata T., and Haruna T. A HSAB concept applied to inhibition effect of anions on IGSCC of sensitized type 304 stainless steel. Corrosion Science 42 (2000) 1071-1081
    • (2000) Corrosion Science , vol.42 , pp. 1071-1081
    • Zhang, S.1    Shibata, T.2    Haruna, T.3
  • 26
    • 34347246782 scopus 로고    scopus 로고
    • ABAQUS Inc., ABAQUS/Standard User's Manual Ver. 6.5, (2005) ABAQUS Inc., USA.


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.