Influence of grain boundaries on short crack growth behaviour of IGSCC

Fatigue and Fracture of Engineering Materials and Structures

Volumn 27, Issue 6, 2004, Pages 513-521

  Kamaya, M ^a  

^a INSTITUTE OF NUCLEAR SAFETY SYSTEM   (Japan)

Author keywords

Crack growth simulation; Grain boundary; IGSCC; Short crack; Weibull distribution

Indexed keywords

BIFURCATION (MATHEMATICS); COMPUTER SIMULATION; CRACK PROPAGATION; GRAIN BOUNDARIES; WEIBULL DISTRIBUTION;

CRACK KINK; INTERGRANULAR STRESS CORROSION CRACKING; MECHANICAL EFFECT;

STRESS CORROSION CRACKING;

EID: 2442690662     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2004.00799.x     Document Type: Article

References (13)

1. Tanaka, K. (1989) Mechanics and micromechanics of fatigue crack propagation. In: Fracture Mechanics: Perspectives and Directions, ASTM STP 1020 (Edited by R. P. Wei and R. P. Gangloff). ASTM, Philadelphia, pp. 151-183.
2. Navarro, A. and Rios, E. R. (1988) A microstructurally-short fatigue crack growth equation. Fatigue Fract. Engng Mater. Struct. 11, 383-396.
3. Tada, N. (1992) Initiation and propagation of creep fatigue small cracks in a type 304 stainless steel. Ph.D. dissertation, Kyoto University, Kyoto.
4. Wang, Y. Z., Ebtehaj, K., Hardie, D. and Parkins, R. N. (1995) The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: 1 - Metallography. Corros. Sci. 37, 1651-1675.
5. Suh, C. M. F., Lee, J. J. and Kang, Y. G. (1990) Fatigue microcracks in type 304 stainless at elevated temperature. Fatigue Fract. Engng Mater. Struct. 13, 487-496.
6. Wang, Y. Z., Ebtehaj, K., Hardie, D. and Parkins, R. N. (1995) The behaviour of multiple stress corrosion cracks in a Mn-Cr and a Ni-Cr-Mo-V steel: 2 - Statistical characterisation. Corros. Sci. 37, 1677-1703.
7. Sakai, S., Totsuka, N., Kamaya, M. and Nakajima, N. (2001) A study of evaluation method for life time of alloy 600 on primary water stress corrosion cracking. In: Proceedings of the Corrosion/2001, NACE, Houston, No. 01134.
8. Kamaya, M., Sakai, S., Totsuka, N., and Nakajima, N. (1999) Short crack growth behavior on PWSCC of mill annealed alloy 600. Zairyo-to-Kankyo (Corros. Engng) 48, 790-795.
9. Kamaya, M. and Totsuka, N. (2002) Influence of interaction between multiple cracks on stress corrosion crack propagation. Corros. Sci. 44, 2333-2352.
10. Nishitani, H. and Murakami, Y. (1974) Stress intensity factors of an elliptical crack or a semi-elliptical crack subject to tension. Int. J. Fract. 10, 353-368.
11. Murakami, Y. and Nemat-Nasser, S. (1983) Growth and stability of interacting surface flaws of arbitrary shape. Engng Fract. Mech. 17, 193-210.
12. Konda, N., Tokimasa, K., Yamanaka, K. and Inoue, M. (1995) Dynamic SCC threshold evaluation and life prediction for SG tubing materials. In: Proceedings of the International Symposium in Plant Aging and Life Predictions of Corrodible Structures (Edited by T. Shoji and T. Shibata). NACE and JSCE, Sapporo, pp. 265-272.
13. Shen, C. H. and Shewmon, P. G. (1990) A mechanism for hydrogen-induced intergranular stress corrosion cracking in alloy 600. Metall. Trans. 21A, 1261-1271.