Initiation and shape development of corrosion-nucleated fatigue cracking

International Journal of Fatigue

Volumn 29, Issue 7, 2007, Pages 1269-1281

  van der Walde, K ^a   Hillberry, B M ^a  

^a Purdue University   (United States)

Author keywords

2024 T3 Aluminum; Corrosion fatigue; Initiation; Pitting

Indexed keywords

AIRCRAFT; ALUMINUM SHEET; CRACK INITIATION; FATIGUE CRACK PROPAGATION; NUCLEATION; PITTING;

2024-T3 ALUMINUM; BREAKING INITIATION; CORROSION-NUCLEATED FATIGUE; SPECIMEN ORIENTATIONS;

CORROSION FATIGUE;

EID: 33947257908     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2006.10.010     Document Type: Article

References (29)

1. Dolley E.J., Lee B., and Wei R.P. The effect of pitting corrosion on fatigue life. Fatigue Fract Eng Mater Struct 23 (2000) 555-560
2. Pao P.S., Gill S.J., and Feng C.R. On fatigue crack initiation from corrosion in 7075-T7351 aluminum alloy. Scripta Mater 43 (2000) 391-396
3. Sankaran K.K., Perez R., and Jata K.V. Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: modeling and experimental studies. Mater Sci Eng A297 (2001) 223-229
4. Harmsworth CL. ASD-TR-61-121, Wright-Patterson Air Force Base, Ohio. July 1961.
5. Clark PN. The transition of corrosion pitting to surface racks in 2024-T3 aluminum alloy, Ph.D. Dissertation, University of Utah, 2001.
6. Kacmar C., and Blackshire J.L. In situ measurements of stress-corrosion crack growth using laser ultrasonics. Proc SPIE 5045 (2003) 213-222
7. Koch GH, Hagerdorn EL, Berens AP. Effect of corrosion on fatigue cracking of aluminum alloys 2024-T3 and 7075-T6, Report R215-04, Prepared for Flight Dynamics Directorate Wright Laboratory Materiel Command, Wright-Patterson Air Force Base, Ohio, 1995.
8. Rokhlin S.I., Kim J.Y., Nagy H., and Zoofan B. Effect of pitting corrosion on fatigue crack initiation and fatigue life. Eng Fract Mech 62 (1999) 425-444
9. Bray G.H., Bucci R.J., Colvin E.L., and Kulak M. Effects of prior corrosion on the S/N fatigue performance of aluminum sheet alloys 2024-T3 and 2524-T3. In: Van Der Sluys W.A., Piascik R.S., and Zawierucha R. (Eds). Effects of the environment on the initiation of crack growth. ASTM STP 1298 (1997), ASTM 89-103
10. Perez R. Corrosion/fatigue metrics. In: ICAF97 Symposium on fatigue in new and ageing aircraft. Springer, Scotland, 1996; p. 215-229.
11. Lankford J. The growth of small fatigue cracks in 7075-T6 aluminum. Fatigue Eng Mater Struct 5 (1982) 233-248
12. Turnbull A., and de los Rios E.R. The effect of grain size on the fatigue of commercially pure aluminum. Fatigue Fract Eng Mater Struct 18 (1995) 1455-1467
13. Ravichandran K.S. Effect of crack shape on crack growth. ASM Fatigue Fract 13 (1987) 159-167
14. Ludwig W., Buffiere J.-Y., Savelli S., and Cloetens P. Study of the interaction of a short fatigue crack with grain boundaries in a cast Al alloy using X-ray microtomography. Acta Mater 51 (2003) 585-598
15. Zamber JE. A Probabilistic approach to predicting fatigue lives of corroded 2024-T3 aluminum, M.S. Thesis, Purdue University, 1997.
16. Medved J.J., Breton M., and Irving P.E. Corrosion pit size distributions and fatigue lives - a study of the EIFS technique for fatigue design in the presence of corrosion. Int J Fatigue 26 (2004) 71-80
17. Tuegel EJ. Investigation of the effect of corrosion pitting on fatigue life of aluminum structure, Report AFRL-VA-WP-TR-2003-3088, Air Force Research Laboratory, Air Force Materiel Command, Wright-Patterson Air Force Base, Ohio, 2003.
18. van der Walde K., Brockenbrough J.R., Craig B.A., and Hillberry B.M. Multiple fatigue crack growth in pre-corroded 2024-T3 aluminum. Int J Fatigue 27 (2005) 1509-1518
19. Gruenberg KM. A method for predicting the fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests, Ph.D. Dissertation, Purdue University, 2001.
20. ASTM G110-92, Standard practice for evaluating intergranular corrosion resistance of heat treatable aluminum alloys by immersion in sodium chloride + hydrogen peroxide solution, 1997.
21. Chen G.S., Liao C.M., Wan K.C., Gao M., and Wei R.P. Pitting corrosion and fatigue crack nucleation. In: Van Der Sluys W.A., Piascik R.S., and Zawierucha R. (Eds). Effects of the environment on the initiation of crack growth. ASTM STP 1298 (1997), ASTM
22. ASTM E112-96, Standard test for determining average grain size, 1996.
23. ® Version 6.5.0.180913a Release 13, Copyright © 1984-2002 by The Mathworks, Inc., Natick, MA, USA, www.mathworks.com.
24. Montgomery D.C. Design and analysis of experiments. fifth ed. (2001), John Wiley & Sons, New York
25. DuQuesnay D.L., Underhill P.R., and Britt H.J. Fatigue crack growth from corrosion damage in 7075-T6511 aluminum alloy under aircraft loading. Int J Fatigue 25 (2003) 371-377
26. Iesulauro E, Ingraffea A, Heber G, Wawrzynek PA. A multiscale modeling approach to crack initiation in metallic polycrystals. In: Proceeding of the 44th AIAA/ASME/ASCE/ AHS/ASC structures, structural dynamics, and materials conference, Norfolk, VA, USA, 7-10 Apr 2003.
27. van der Walde K. Corrosion-nucleated fatigue crack growth. Ph.D. Dissertation, Purdue University, May 2005.
28. Trantina G.G., and Barishpolsky M. Elastic-plastic analysis of small defects-voids and inclusions. Eng Fract Mech 20 (1984) 1-10
29. Kishimoto K., Soboyejo W.O., Smith R.A., and Knott J.F. A numerical investigation of the interaction and coalescence of twin coplanar semi-elliptical fatigue cracks. Int J Fatigue 11 2 (1989) 91-96