Stress corrosion cracking of austenitic alloys in supercritical water

Corrosion

Volumn 62, Issue 12, 2006, Pages 1100-1116

  Teysseyre, S ^a   Was, G S ^a  

^a UNIVERSITY OF MICHIGAN   (United States)

Author keywords

Generation IV; Intergranular fracture; Stress corrosion cracking; Supercritical water

Indexed keywords

ACTIVATION ENERGY; AUSTENITIC STAINLESS STEEL; CRACK PROPAGATION; INTERNAL OXIDATION; NICKEL ALLOYS; SUPERCRITICAL FLUIDS; SURFACE ANALYSIS; WATER;

CONSTANT EXTENSION RATE TENSILE MODE; INTERGRANULAR FRACTURE; SUPERCRITICAL WATER; TARNISH RUPTURE MECHANISM;

STRESS CORROSION CRACKING;

ACTIVATION ENERGY; AUSTENITIC STAINLESS STEEL; CRACK PROPAGATION; INTERNAL OXIDATION; NICKEL ALLOYS; STRESS CORROSION CRACKING; SUPERCRITICAL FLUIDS; SURFACE ANALYSIS; WATER;

EID: 33846475566     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278244     Document Type: Article

References (17)

1. R.M. Latanision, R.W. Shaw, "Corrosion in Supercritical Water Oxidation Systems," Workshop held at Massachusetts Institute of Technology, Report no. MIT-EL 93-006, May 6-7, 1993.
2. D.B. Mitton, J.H. Yoon, J.A. Cline, H.S. Kim, N Eliaz, R.M. Latanision, Ind. Eng. Chem. Res. 39 (2000): p. 4,689.
3. D.B. Mitton, J.H. Yoon, R.M. Latanision, Zairyo-to-Kankyo (Corros. Eng.) 49, 3 (2000): p. 130-137.
4. U. S. Department of Energy (DOE), "A Technology Roadmap, for Generation IV Nuclear Energy Systems," U.S. DOE Nuclear Energy Research Advisory Committee and the Generation IV International Forum (NERAC/GIV), Washington DC, http://gif.inel.gov/roadmap/pdfs/ gen_iv_roadmap.pdf, 2002.
5. G. Was, S. Teysseyre, "Challenges and Recent Progress in Corrosion and Stress Corrosion Cracking of Alloys for Supercritical Water Reactor Core Compounds," Proc. 12th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale. PA: TMS, 2005), p. 1,343.
6. W.K. Boyd, H.A. Pray, Corrosion 13 (1957): p. 375.
7. L. Fournier, D. Delafosse, C. Bosch, Th. Magnin, "Stress Corrosion Cracking of Nickel Base Superalloys in Aerated Supercritical Water," CORROSION/2001, paper no. 01361 (Houston, TX: NACE International, 2001).
8. Y. Tsuchiya, F. Kano, N. Saito, A. Shioiri, K. Moriya, S. Kasahara, "SCC Properties of Metals Under Supercritical-Water Cooled Power Reactor Conditions," CORROSION/2004, paper no. 04485 (Houston, TX: NACE, 2004).
9. Y. Watanabe, H. Abe, Y. Daigo, "Environmentally Assisted Cracking of Sensitized Stainless Steel In Supercritical Water: Effects of Physical Property of Water," GENES4/ANP2003, paper no. 1183, held Sept. 15-19 (Tokyo. Japan: Atomic Energy Society of Japan, 2003).
10. K. Chihab, Y. Estrin, L.P. Kubin, J. Vergnol, Scr. Metall. 21 (1987): p. 203.
11. J.A. Begley, "Strain-Rate Damage Model for Alloy 600 in Primary Water," Electric Power Research Institute, report no. NP-7008s, 1990.
12. P.L. Andresen, Stress Corrosion Cracking, ed. R.H. Jones [Materials Park, OH: ASM International, 1992], p. 183.
13. G. Santarini, Corrosion 45 (1989): p. 389.
14. G.S. Was, S. Teysseyre, J. McKinley, Z. Jiao, "Corrosion of Alloys in Supercritical Water," CORROSION/2005, paper no. 05397 (Houston, TX: NACE, 2005).
15. R.W. Staehle, J.A. Gorman, "Progress in Understanding and Mitigating Corrosion on the Secondary Side of PWR Steam Generators," Proc. 10th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, eds. P. Ford, G.S. Was, L. Nelson (Houston, TX: NACE, 2001).
16. P.M. Scott, "An Overview of Internal Oxidation as a Possible Explanation of Intergranular Stress Corrosion Cracking of Alloy 600 in PWRs," 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, eds. S. Bruemmer, P. Ford, G.S. Was (Warrendale: PA: The Minerals, Metals, and Materials Society, 1999), p. 3.
17. R.H. Bricknell, D.A. Woodford, Scr. Metall. 16 (1982): p. 761-763.