Stress corrosion cracking of nickel base superalloys in aerated supercritical water

NACE - International Corrosion Conference Series

Volumn 2001-March, Issue , 2001, Pages

  Fournier, L ^a,b   Delafosse, D ^a   Bosch, C ^a   Magnin, T ^a  

^a CENTRE SMS   (France)

^b UNIVERSITY OF MICHIGAN   (United States)

Author keywords

Alloy 690; Alloy 718; Nickel base superalloy; Oxygen embrittlement; Stress corrosion cracking; Supercritical water oxidation (SCWO)

Indexed keywords

CRACKS; EMBRITTLEMENT; INTERGRANULAR CORROSION; NICKEL; NICKEL ALLOYS; OXIDATION; RESIDUAL STRESSES; SUPERALLOYS; WATER AERATION;

ALLOY 690; ALLOY 718; NICKEL BASE SUPERALLOY; OXYGEN EMBRITTLEMENT; SUPERCRITICAL WATER OXIDATION;

STRESS CORROSION CRACKING;

EID: 85042182771     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (22)

1. R.M. Latanision, Corrosion Science, 51 (1995): p. 270.
2. P. Kritzer, N. Boukis, E. Dinjus, Materials and Corrosion, 49 (1998): p. 831.
3. R.M. Latanision, R. W. Shaw, "Corrosion in supercritical water oxidation systems, " Workshop Summary, The Energy Laboratory, MIT, 6-7 May, 1993.
4. L.B. Kriksunov, D. D. Macdonald, Journal of the Electrochemical Society, 142 (1995): p. 4069.
5. R.H. Bricknell, D. A. Woodford, Metallurgical Transactions, 12 (1981): p.425.
6. M.C. Pandey, D. M. R. Taplin, A. K. Mukherjee, Metallurgical Transactions, 15 (1984): p.1763.
7. L. Fournier, PhD thesis, Ecole Nationale Superieure des Mines de St-Etienne, France (2000).
8. R. Molins, G. Hochstetter, J. C. Chassaigne, E. Andrieu, Acta Materialia, 2 (1997): p. 663.
9. M. Clavel, A. Pineau, Materials Science and Engineering, 55 (1982): p.157.
10. A. Diboine, A. Pineau, Fatigue and Fracture of Engineering Material Structure, 10 (1987): p.141.
11. S. Fox, J. W. Brooks, M. H. Loretto, R. E. Smallman, "Influence of carbides on the mechanical properties on inconel 718, " Seventh International Conference on Strength of Metals and Alloys, (Pergamon Press, 1986).
12. M. Sundararaman, P. Mukhopadhyay, High Temperature Materials and Processes, 11 (1993): p.351.
13. A. Harabasz, K. Wolski, T. Magnin, M. Biscondi, Materials Science Forum, 294-296 (1999): p.677.
14. K. Chihab, Y. Estrin, L.P. Kubin, J. Vergnol, Scripta Metal. 21 (1987): p 203.
15. T. Magnin, Advances in Corrosion-Deformation Interactions (Zurich: Trans Tech. Publications Ltd, 1996).
16. D. Delafosse, J. P. Chateau, A. Chambreuil, T. Magnin, Materials Science and Engineering, 234-236 (1997): p.889.
17. T. Magnin, F. Foct, O. de B, "i-lydrogen effects on PWR SCC mechanisms in monocrystalline and polycrystalline alloy 600, " Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, (The Minerals, Metals and Materials Society, 1999).
18. P. Hancock, "Influence of vacancies produced by oxidation on the mechanical properties of Ni and Ni-Cr alloys, " Vacancies 1976, (Met. Soc., 1977).
19. P.M. Scott, M. Le Calvar, "Some possible mechanisms of intergranular stress corrosion cracking of alloy 600 in PWR primary water, " Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, (The Minerals, Metals and Materials Society, 1993).
20. L. E. Thomas, S. M. Bruemmer, "Insights into environmental degradation mechanisms from analytical transmission electron microscopy of SCC cracks, " Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, (The Minerals, Metals and Materials Society, 1999).
21. R.C. Newman, T. S. Gendron, P. M. Scott, "Internal oxidation and embrittlement of alloy 600, " Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems- Water Reactors, (The Minerals, Metals and Materials Society, 1999).
22. M.O. Speidel, R. Magdowski, "Stress corrosion cracking of nickel base alloys in high temperature water, " Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, (The Minerals, Metals and Materials Society, 1993).