High temperature crack initiation and defect assessment of P22 steel weldments using time dependent failure assessment method

Engineering Fracture Mechanics

Volumn 74, Issue 6, 2007, Pages 839-852

  Dogan, B ^a   Ceyhan, U ^a   Petrovski, B ^a  

^a INSTITUTE OF MATERIALS RESEARCH   (Germany)

Author keywords

Crack initiation; Creep crack growth; Failure assessment diagram; Steels; Welds metals

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; CREEP; DEFECTS; DUCTILITY; FAILURE ANALYSIS; HIGH TEMPERATURE EFFECTS; MICROSTRUCTURE; STEEL; WELDS;

CREEP CRACK GROWTH; CREEP CRACK INITIATION; FAILURE ASSESSMENT; WELD METALS;

FRACTURE MECHANICS;

CRACK INITIATION; CRACK PROPAGATION; CREEP; DEFECTS; DUCTILITY; FAILURE ANALYSIS; FRACTURE MECHANICS; HIGH TEMPERATURE EFFECTS; MICROSTRUCTURE; STEEL; WELDS;

EID: 33846413233     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2006.08.018     Document Type: Article

References (28)

1. Steen WM, Shannon GJ. Laser welding - the most adaptable technique available. In: Vitek JM et.al., editors. International conference on trends in welding research, Georgia: ASM International; 1998. p. 423-30.
2. Nikbin KM. The role of defect assessment in elevated temperature component design and remaining life estimation codes. In: Y.Asada, editor. CREEP 7. Tsukuba, 2001. p. 123-30.
3. Dogan B. High temperature defect assessment procedures. Int J Pres Vessels Piping 80 3 (2003) 149-156
4. Dogan B, Ainsworth RA. Defect assessment procedures for low to high temperature. In: ASME conference PVP2003-2032, 2003;463:105-111.
5. British Standard BS7910. Guidance on methods for assessing the acceptability of flaws in metallic structures (2000), British Standards Institution
6. ASME Section III. Rules for construction of nuclear power plant components, Division 1, Sub-section NH. Class 1 components in elevated temperature service (1995), ASME
7. R5. Assessment procedure for the high temperature response of structures. Issue 2. Goodall IW, editor. British Energy-UK; 1998.
8. A16. Guide for leak before break analysis and defect assessment. RCC-MR. Appendix A16. Edition; 2002. AFCEN No: 94-2002.
9. Drubay B, Moulin D, Faidy C, Poette C, Bhandari S. Defect assessment procedure: a French approach. ASME PVP;1993. vol. 266: p. 113-8.
10. Jaske C.E. In: Amzallag C. (Ed). Materials data needs for fatigue design of pressure vessel systems, in STP 770, Low cycle fatigue and life prediction (1982), ASTM, Philadelphia 600-611
11. ASTM E1457-00. Standard test method for measurement of creep crack growth rates in metals. ASTM 03.01. Philadelphia: ASTM 2000, PA 19103, USA.
12. Saxena A, Liaw PK. Remaining life assessment of boiler pressure parts-crack growth studies, In: EPRI CS 4688, Electric Power Research Institute. Palo Alto, CA, 1986.
13. Dogan B., Saxena A., and Schwalbe K.-H. Creep xrack behaviour of Ti6262. Mater High Temp 10 2 (1992) 138-143
14. Dogan B, Petrovski B. High temperature behaviour of P91 steel welds. In: Parker JD, editors. 9th international conference on CFMS. Swansea, UK, 2001. p. 763-75.
15. Leung C.-P., McDowell D.L., and Saxena A. Consideration of primary creep at a stationary crack tip: Implications for the C t parameter. Int J Fracture 36 4 (1988) 275-289
16. Hawk D.E., and Bassani J.L. Transient crack growth under creep conditions. J Mech Phys Solids 34 3 (1986) 191-212
17. Dean DW, Hooton DG. A review of creep toughness data for austenitic type 316 steels. BEGL Report E/REP/GEN/0024/00. 2003.
18. Ainsworth R.A., Hooton D.G., and Green D. Failure assessment diagrams for high temperature defect assessment. Engng Fracture Mech 62 (1999) 95-109
19. Riedel H, Rice JR. Tensile crack in creeping solids. In: ASTM STP 700; 1980. p.112-130.
20. Holdsworth S.R. Initiation and early growth of creep cracks from pre-existing defects. Mater High Temp 10 2 (1992) 127-137
21. Dogan B, Petrovski B, Ceyhan U. Significance of creep crack initiation for defect assessment. In: Veivo J, Auerkari P, editors. Int. Conf. BALTICA VI, VTT Symposium 234, Vol.2. Helsinki-Stockholm-Helsinki; 2004, p. 595-607.
22. Ainsworth R.A., and Budden P.J. Design and assessment of components subjected to creep. J Strain Anal 29 (1994) 201-208
23. R6. Assessment of integrity of structures containing defects; Procedure R6, Revision 3. British Energy, Gloucester, UK, 1997.
24. Ainsworth R.A. The use of a failure assessment diagram for initiation and propagation of defects at high temperatures. Fatigue Fract Engng Mater Struct 16 (1993) 1091-1108
25. Müller F, Gengenbach T, Klenk A. ECCC CCI (WG 1.2); 3(4) Draft 3. 2003.
26. Pique R, Bensussan P, Pineau A. Crack initiation and growth under creep and fatigue loading of an austenitic stainless steel. In: Proc. MECAMAT, Int. Seminar on High Temperature Fracture Mechanisms and Mechanics. Dourdan; 1987. p. 53-70.
27. Dogan B, Petrovski B, Ceyhan U. In: Shibli IA, Holdsworth SR, Merckling G. editors. ECCC Int. Conf. on Creep and Fracture in High Temperature Components - Design and Life Assessment Issues. London; 2005. p.724-743.
28. Davies C.M., O'Dowd N.P., Dean D.W., Nikbin K.M., and Ainsworth R.A. Failure assessment diagram analysis of creep crack initiation in 316H stainless steel. Int J Pres Vessels Piping 80 7-8 (2003) 541-551