Preparation, structures, and multiferroic properties of single phase Bi1-xLaxFeO3 (x=0-0.40) ceramics

Journal of Applied Physics

Volumn 100, Issue 11, 2006, Pages

  Zhang, Shan Tao ^a   Pang, Ling Hua ^b   Zhang, Yi ^b   Lu, Ming Hui ^b   Chen, Yan Feng ^b  

^a NANJING UNIVERSITY   (China)

^b NONE

Author keywords

[No Author keywords available]

Indexed keywords

BISMUTH COMPOUNDS; FERROELECTRICITY; SOLID SOLUTIONS; SYNTHESIS (CHEMICAL); X RAY DIFFRACTION ANALYSIS; X RAY PHOTOELECTRON SPECTROSCOPY;

MAGNETOELECTRIC INTERACTION; MULTIFERROIC PROPERTIES; ORTHORHOMBIC PHASE;

CERAMIC MATERIALS;

EID: 33845761009     PISSN: 00218979     EISSN: None     Source Type: Journal    
DOI: 10.1063/1.2390625     Document Type: Article

References (35)

1. M. Fiebig, J. Phys. D 38, R123 (2005).
2. G. Catalan, Appl. Phys. Lett. 88, 102902 (2006).
3. N. A. Hill, J. Phys. Chem. B 104, 6694 (2000).
4. O. P. Vajk, M. Kenzelmann, J. W. Lynn, S. B. Kim, and S.-W. Cheong, Phys. Rev. Lett. 94, 087601 (2005).
5. B. B. Van Aken, T. T. M. Plastra, A. Filippetti, and N. A. Spaldin, Nat. Mater. 3, 164 (2004).
6. J. Wang, Science 299, 1719 (2003).
7. M. Fiebig, M. T. Lottermoser, D. Fröhlich, A. V. Goltsev, and R. V. Pisarev, Nature (London) 419, 818 (2002).
8. J. R. Cheng, N. Li, and L. E. Cross, J. Appl. Phys. 94, 5153 (2003).
9. Y. P. Wang, L. Zhou, M. F. Zhang, X. Y. Chen, J. M. Liu, and Z. G. Liu, Appl. Phys. Lett. 84, 1731 (2004).
10. A. K. Pradhan, J. Appl. Phys. 97, 093903 (2005).
11. W. Eerenstein, F. D. Morrison, J. Dho, M. G. Blamire, J. F. Scott, and N. D. Mathur, Science 307, 1203a (2005).
12. J. B. Neaton, C. Ederer, U. V. Waghmare, N. A. Spaldin, and K. M. Rabe, Phys. Rev. B 71, 014113 (2005).
13. K. Y. Yun, M. Noda, M. Okuyama, H. Saeki, H. Tabata, and K. Saito, J. Appl. Phys. 96, 3399 (2004).
14. F. Bai, Appl. Phys. Lett. 86, 032511 (2005).
15. J. Li, Appl. Phys. Lett. 84, 5261 (2004).
16. G. Xu, H. Hiraka, G. Shirane, J. Li, J. Wang, and D. Viehland, Appl. Phys. Lett. 86, 182905 (2005).
17. A. V. Zalesskii, A. K. Zvezdin, A. A. Frolov, and A. A. Bush, JETP Lett. 71, 465 (2000).
18. J. S. Kim, C. I. Cheon, C. H. Lee, and P. W. Jang, J. Appl. Phys. 96, 468 (2004).
19. J. S. Kim, C. I. Cheon, Y. N. Choi, and P. W. Jang, J. Appl. Phys. 93, 9263 (2003).
20. N. Wang, J. Cheng, A. Pyatakov, A. K. Zvezdin, J. F. Li, L. E. Cross, and D. Viehland, Phys. Rev. B 72, 104434 (2005).
21. M. M. Kumar, V. R. Palkar, K. Srinivas, and S. V. Suryanarayana, Appl. Phys. Lett. 76, 2764 (2000).
22. J. Lüning, F. Nolting, A. Scholl, H. Ohldag, J. W. Seo, J. Fompeyrine, J.-P. Locquet, and J. Stöhr, Phys. Rev. B 67, 214433 (2003).
23. D. Lee, M. G. Kim, S. Ryu, H. M. Jang, and S. G. Lee, Appl. Phys. Lett. 86, 222903 (2005).
24. Y. H. Lee, J. M. Wu, and C. H. Lai, Appl. Phys. Lett. 88, 042903 (2006).
25. Z. V. Gabbasova, M. D. Kuz'min, A. K. Zvezdin, I. S. Dubenko, V. A. Murashov, D. N. Rakov, and I. B. Krynetsky, Phys. Lett. A 158, 491 (1991).
26. A. V. Zalesskii, A. A. Frolov, T. A. Khimich, and A. A. Bush, Phys. Solid State 45, 141 (2003).
27. B. Ruette, S. Zvyagin, A. P. Pyatakov, A. A. Bush, J. F. Li, V. I. Belotelov, A. K. Zvezdin, and D. Viehland, Phys. Rev. B 69, 064114 (2004).
28. C. Ederer and N. A. Spaldin, Phys. Rev. B 71, 060401 (R) (2005).
29. Y. F. Popov, A. M. Kadomtseva, S. S. Drotov, D. V. Belov, G. P. Worob'ev, P. N. Makhov, and A. K. Zvezdin, Low Temp. Phys. 27, 478 (2001).
30. I. Sosnowska, W. Schäfer, W. Kockelmann, K. H. Andersen, and I. O. Troyanchuk, Appl. Phys. A: Mater. Sci. Process. A74, S1040 (2002).
31. S. T. Zhang, M. H. Lu, D. Wu, Y. F. Chen, and N. B. Ming, Appl. Phys. Lett. 87, 262907 (2005).
32. S. T. Zhang, Appl. Phys. Lett. 88, 162901 (2006).
33. T. Kanai, K. Ohkoshi, A. Nakajima, T. Watanabe, and K. Hashimoto, Adv. Mater. (Weinheim, Ger.) 13, 487 (2001).
34. P. Baettig and A. Spaldin, Appl. Phys. Lett. 86, 012505 (2005).
35. J. Yu, N. Koshikawa, Y. Arai, S. Yoda, and H. Saitou, J. Cryst. Growth 231, 568 (2001).