Crack initiation and early propagation of X70 steel in simulated near-neutral pH groundwater

Corrosion

Volumn 62, Issue 8, 2006, Pages 723-731

  Lu, B T ^a   Luo, J L ^a  

^a UNIVERSITY OF ALBERTA   (Canada)

Author keywords

Crack initiation; Crack propagation; Environmentally assisted cracking; Microstructure; Pipeline steel

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; GROUNDWATER; MICROSTRUCTURE; PH EFFECTS;

ENVIRONMENTALLY ASSISTED CRACKING; NONMETALLIC INCLUSIONS; PIPELINE STEEL; PIT CRACKS;

STEEL;

CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; GROUNDWATER; MICROSTRUCTURE; PH EFFECTS; STEEL;

EID: 33750887354     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278297     Document Type: Article

References (31)

1. National Energy Board, Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines. Report of the Inquiry, MH-2-95, 1996.
2. R.N. Parkins, "A Review of Stress Corrosion Cracking of High Pressure Gas Pipelines," CORROSION/2000, paper no. 363 (Houston, TX: NACE International. 2000).
3. R.N. Parkins, W.K. Blanchard, Jr. D.S. Delany, Corrosion 50 (1994): p. 304.
4. S.D. Liberto, G. Gabetta, Mater. Sci. 33 (1997): p. 411.
5. S.X. Mao, B. Gu, N.Q. Wu, L. Qiao, Philos. Mag. A. Phys. Condens. Matter Defects Mech. Prop. 81 (2001): p. 1,813.
6. B.T. Lu, J.L. Luo, "A Mechanistic Study on Near-Neutral pH Stress Corrosion Cracking of Pipeline Steel," Proc. 2nd Int. Conf. of Environment-Induced Cracking of Metals, held August 2004 (Houston, TX: NACE, 2004).
7. M. Elboujdaini, Y.-Z. Wang. R.W. Revie, "Initiation of Stress Corrosion Cracking on X65 Linepipe Steel in Near-Neutral pH Environment," Proc. Int. Pipeline Conf. (IPC2000), vol. 2 (New York, NY: ASME International, 2000), p. 967.
8. R. Sutherby, T. Jack, G.V. Boven, M. Wilmott, "CEPA Study on Characterization of Pipeline Pressure Fluctuations in Terms Relevant to Stress Corrosion Cracking." Proc. Int. Pipeline Conf. (IPC2000), vol. 2 (New York. NY: ASME International, 2000), p. 989.
9. M.J. Wilmott, R.L. Sutherby, "The Role of Pressure and Pressure Fluctuation the Growth of Stress Corrosion in Line Pipe Steels," Proc. Int. Pipeline Conf. (IPC1998), vol. 1 (New York, NY: ASME International, 1998). p. 409.
10. B.W. Williams, S.B. Lambert, R. Sutherby, A. Plumtree, Corrosion 60 (2004): p. 95.
11. M. Elboujdaini, Y.-Z. Wang, R.W. Revie, R.N. Parkins, M.T. Schhata, "Stress Corrosion Crack Initiation Processes: Pitting and Microcrack Coalescence." CORROSION/2000, paper no. 379 (Houston, TX: NACE, 2000).
12. Y.-Z. Wang, R.W. Revie, R. Shehata, R.N. Parkins, K. Krist, "Stress Corrosion Crack Initiation Processes: Pitting and Microcrack Coalescence," Proc. Int. Pipeline Conf. (IPC1998), vol. 1 (New York, NY: ASME International, 1998), p. 529.
13. T. Kushida, K. Nose, H. Asahi, Kimura, Y. Yamane, S. Endo, H. Kawano, "Effect of Metallurgical Factors on Near-Neutral pH SCC of Pipeline Steels," CORROSION/2001, paper no. 01213 (Houston, TX: NACE, 2001).
14. R.D.K. Misra, J.E. Hartmann, A.J. Boucek, Iron Steel Manufacture 8 (2000): p. 63.
15. W.D. Pikey, Peterson's Stress Concentration Factors, 2nd ed. (New York. NY: Wiley. 1997).
16. Y.X. Zhao, Q. Gao, J.N. Wang, Fatigue Fract. Eng. Mater. Struct 23 (2000): p. 926.
17. N.E. Frost, K.J. Marsh. L.P. Pook, Metal Fatigue (Oxford, U.K.: Clarendon Press, 1974), p. 371.
18. D.A. Jones, Corrosion 52 (1996): p. 356.
19. D.J. Duqeutte, Corrosion 46 (1990): p. 434.
20. RN. Parkins, Corrosion 46 (1990): p. 178.
21. I.I. Dykyi, I.M. Protsov, Mater. Sci. 29 (1993): p. 569.
22. G.M. Gutman, Mechanochemistry of Materials (London, England: Cambridge International Science Publishing, 1998). p. 252.
23. Y.Z. Wang. R. Akid, K.J. Miller, J. Eng. Mater. Struct. 18 (1995): p. 293.
24. X.-Y. Zhang, S.B. Lambert, R Sutherby, A. Plumtree, Corrosion 55 (1999): p. 297.
25. B.T. Lu, X.L. Zheng, Eng. Fract. Mech. 42 (1992): p. 1,001.
26. K.J. Miller, Fatigue Fract. Eng. Mater. Struct. 16 (1993): p. 931.
27. T.V. Duggan, J. Byrne, Fatigue as a Design Criterion (London, England: Macmillan, 1977), p. 11.
28. J.T. Bulger, The Effect of Microstructure on Near-Neutral-pH SCC" (Master's thesis, University of Alberta, 2000).
29. T. Magnin, A. Chambreuil, B. Bayle, Acta Mater. 44 (1996): p. 1,457.
30. B.T. Lu, J.L. Luo, Corrosion 62, 2 (2006): p. 129.
31. R. Chu, W. Chen, S.-H. Wang, F. King, RR Fessier, Corrosion 60 (2004): p. 275.