Relationship between yield strength and near-neutral pH stress corrosion cracking resistance of pipeline steels - An effect of microstructure

Corrosion

Volumn 62, Issue 2, 2006, Pages 129-140

  Lu, B T ^a   Luo, J L ^a  

^a UNIVERSITY OF ALBERTA   (Canada)

Author keywords

Microstructure; Pipeline steel; Stress corrosion cracking; Welding; Yield strength

Indexed keywords

CORROSION RESISTANCE; MICROSTRUCTURE; PH EFFECTS; PIPELINES; STRESS CORROSION CRACKING; WELDING; YIELD STRESS;

PIPELINE STEELS; POLARIZATION RESISTANCE; WELDMENTS;

STEEL STRUCTURES;

CORROSION RESISTANCE; MICROSTRUCTURE; PH EFFECTS; PIPELINES; STEEL STRUCTURES; STRESS CORROSION CRACKING; WELDING; YIELD STRESS;

EID: 33750882524     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278258     Document Type: Article

References (30)

1. M. Elboujdalni, Y.-Z. Wang, R.R. Revie, "Initiation of Stress Corrosion Cracking on X65 Linepipe Steel in Near-Neutral pH Environment," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 967-985.
2. R.N. Parkins, "A Review of Stress Corrosion Cracking of High-Pressure Gas Pipelines," CORROSION/2000, paper no. 363 (Houston, TX: NACE International, 2000).
3. R.N. Parkins, W.K. Blanchard, Jr., B.S. Delanty, Corrosion 50 (1994): p. 304-321.
4. S.D. Liberto, G. Gabetta, Mater. Sci. 33 (1997): p. 411-420.
5. S.X. Mao, B. Gu, N.Q. Wu, L. Qiao, Philos. Mag. A. Phys. Condens. Matter Defects Mech. Prop. 81 (2001): p. 1,813-1,831.
6. M. Elboujdaini, Y.-Z. Wang, R.R. Revie, "Initiation of Stress Corrosion Cracking on X65 Linepipe Steel in Near-Neutral pH Environment," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 967-985.
7. B. Gu, W.Z. Yu, J.L. Luo, X. Mao, Corrosion 55 (1999): p. 312-318.
8. B. Zhang, J. Fan, Y. Gogotsi, A. Chudnovsky, A. Teitsma, "Theoretical and Experimental Study of Stress Corrosion Cracking of Pipeline Steel in Near-Neutral pH Environment," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 1,013-1,020.
9. B.T. Lu, J.L. Luo, B. McCrady, "Near-Neutral pH SCC Initiation and Early Propagation of X70 Pipeline Steel," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 272.
10. M.J. Wilmott, R.L. Sutherby, "The Role of Pressure and Pressure Fluctuation the Growth of Stress Corrosion in Line Pipe Steels," Proc. Int. Pipeline Conf., vol. 1 (New York, NY: ASME International, 1998), p. 409-422.
11. R. Sutherby, T. Jack, G.V. Boven, M. Wilmott, "CEPA Study on Characterization of Pipeline Pressure Fluctuations in Terms Relevant to Stress Corrosion Cracking," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 989-996.
12. N.E. Frost, K.J. Marsh, L.P. Pook, Metal Fatigue (Oxford, U.K.: Clarendon Press, 1974), p. 374.
13. J.A. Beavers, J.T. Jonson, R.L. Sutherby, "Materials Factors Influencing the Initiation of Near-Neutral pH SCC on Underground Pipelines," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 979-988.
14. M. Kimura, T. Kushida, K. Nose, S. Okano, S. Endo, Y. Yashuo, "Effects of Metallurgical Factors and Test Condition on Low-pH Type Stress Corrosion Cracking of Pipeline," ASME Pressure Vessels and Piping Division Publication, vol. 380 (New York, NY: ASME International, 1998), p. 265-272.
15. R. Chu, W. Chen, S.-H. Wang, F. King, R.R. Fessier, Corrosion 60 (2004): p. 275-283.
16. J.G. Gonzalez-Rodriguez, M. Casales, V.M. Salinas-Bravo, J.L. Albarran, L. Martinez, Corrosion 58 (2002): p. 584-590.
17. Y.-Z. Wang, R.W. Revie, R. Shehata, R.N. Parkins, K. Krist, "Initiation of Environment-Induced Cracking In Pipeline Steel, Microstructrual Correlation," Proc. Int. Pipeline Conf., vol. 1 (New York, NY: ASME International, 1998), p. 529-542.
18. W. Chen, S.-H. Wang, R. Chu, F. King, T.R. Jack, R.R. Fessier, Metall. Trans. 34A (2003): p. 2,601-2,608.
19. G. Gabette, S. Di Liberto, A. Bennardo, N. Mancini, Br. Corros. J. 36 (2001): p. 24-28.
20. "Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines," Report of the Inquiry, MH-2-95, National Energy Board, 1996.
21. R.D.K. Misra, J.E. Hartmann, A.J. Boucek, Iron Steel Manufacturing 8 (2000): p. 63-70.
22. A.H. Adelek, J.L. Luo, A.G. Ivey, "Influence of Microstructure on Near-Neutral pH Stress Corrosion Cracking Susceptibility in the Weld Region of X70 Pipeline Steel," Northern Area NACE Conf. (Houston, TX: NACE, 2005).
23. J.T. Bulger, J.L. Luo, "Effect of Microstructure on Near-Neutral-pH SCC," Proc. Int. Pipeline Conf., vol. 2 (New York, NY: ASME International, 2000), p. 974-952.
24. J.T. Bulger, "The Effect of Microstructure on Near-Neutral-pH SCC" (Master's thesis, University of Alberta, 2000).
25. T. Kushida, K. Nose, H. Asahi, Kimura, Y. Yamane, S. Endo, H. Kawano, "Effects of Metallurgical Factors on Near-Neutral pH SCC of Pipeline Steels," CORROSION/2001, paper no. 01213 (Houston, TX: NACE, 2001).
26. H.F. Lopez, R. Bharawaj, J.L. Albarran, L. Martines, Metall. Trans. 30A (1999): p. 1,999-2,419.
27. M. Sakai, Y. Nakano, J. Mater. Res. 17 (2002): p. 2,161-2,173.
28. B. Gu, J.L. Luo, X. Mao, Corrosion 55 (1999): p. 312-318.
29. W. Chen, F. King, T.R. Jack, M.J. Wilmott, Metall. Trans. A. Phys. Metall. Mater. Sci. 33A (2002): p. 1,429-1,436.
30. M. Kimura, T. Kushida, K. Nose, S. Okano, S. Endo, Y. Nishida, "Fitness-for-Service Evaluations in Petroleum and Fossil Power Plants," Pressure Vessels and Piping Division Publication, vol. 380 (New York, NY: ASME International, 1998), p. 265-272.