Microstructure and fatigue strength of the roller-bearing steel 100Cr6 (SAE 52100) after two-step bainitisation and combined bainitic-martensitic heat treatment

International Journal of Materials Research

Volumn 97, Issue 10, 2006, Pages 1432-1440

  Vetters, Hermann ^a,b,c   Dong, Juan ^a   Bornas, Hubert ^a   Hoffmann, Franz ^a   Zoch, Hans Werner ^a  

^a IWT Bremen   (Germany)

^b UNIVERSITY OF BREMEN   (Germany)

^c NONE   (Germany)

Author keywords

Fatigue strength; Heat treatment; Lower bainite; Microstructure; Roller bearing steel

Indexed keywords

BAINITIC TRANSFORMATIONS; FATIGUE OF MATERIALS; HEAT TREATMENT; MARTENSITIC TRANSFORMATIONS; MICROSTRUCTURE; ROLLER BEARINGS; STRENGTH OF MATERIALS;

BAINITIC MARTENSITIC HEAT TREATMENT; LOWER BAINITE; RETAINED AUSTENITE; ROLLER BEARING STEEL;

STEEL;

EID: 33750512726     PISSN: 18625282     EISSN: None     Source Type: Journal    
DOI: 10.3139/146.101388     Document Type: Article

References (32)

1. O. Schaaber: Härterei-Techn. Mitt. 4 (1950) 9.
2. F. Hengerer, O. Lucas, B. Nyberg: Härterei-Techn. Mitt. 29 (1974) 71.
3. J. Slycke, C. Fajers, J. Volkmuth: Härterei-Techn. Mitt. 57 (2002) 156.
4. E. Macherauch, O. Vöhringer: Härterei-Techn. Mitt. 41 (1986) 71.
5. W. Jellinghaus: Arch. Eisenhüttenw. 23 (1952) 11/12, 459.
6. C. Li, J.L. Wang: Journal of Materials Science 28 (1993) 2112.
7. H.K.D.H. Bhadheshia: Bainite in Steels, Inst. of Materials, London (1992).
8. M. Hillert: Scripta Mat. 43 (2000) 831.
9. H.I. Aaronson, G. Spanos, W.T. Reynolds Jr.: Scripta Mater. 47 (2002) 139.
10. J. Dong, H. Vetters, H.-W. Zoch: Trans. Mat. Heat Treatment 25 (2004) 5, 555.
11. M. Hunkel, Th. Lübben, F. Hoffmann, P. Mayr: Härterei-Techn. Mitt. 54 (1999) 365.
12. H. Bornas, T. Linkewitz, P. Mayr: Fatigue and Fracture of Engineering Materials and Structures 22 (1999) 733.
13. J.W. Christian, D.V. Edmonds: Phase Transformations in Ferrous Alloys; Warrendale, PA (1984) 293.
14. European Patents: EP 0896068 B1; EP 0794262 B1; EP 1248 862 A1.
15. H. Vetters: Steel Research 67 (1996) 408.
16. W.T. Reynolds Jr., S.K. Liu, F.Z. Li, S. Hartfield, H.I. Aaronson: Met. Trans. A 21 (1990) 1433.
17. G. Spanos, H.S. Fang, H.I. Aaronson: Met. Trans. A 21 (1990) 1381.
18. Y. Ohmori: Scripta Mater. 47 (2002) 201.
19. H.S. Fang, J.B. Yang, Z.G. Yang, B.Z. Bai: Scripta Mat. 47 (2002) 157.
20. T.Y. Hsu: Met. Trans A 21 (1990) 811.
21. G.B. Olson, H.K.D.H. Bhadheshia, M. Cohen: Met. Trans. A 21 (1990) 805.
22. R.F. Hehemann: Phase transformations, ASM Ohio (1970) 397.
23. O. Vöhringer, E. Macherauch: Härterei-Techn. Mitt. 32 (1977) 153.
24. H. Schwendemann: Die thermische Restaustenitstabilisierung bei den Stählen 100Cr6 und X210Cr12, Dr.-Ing. Diss.(Thesis), TU Karlsruhe (1981).
25. A. Schrader, F. Wever: Arch. Eisenhüttenwes. 23 (1952) 489.
26. S.J. Matas, R.F. Heheman: Trans TMS AIME 221 (1961) 179.
27. H.K.D.H. Bhadheshia, J.W. Christian: Met. Trans. A 21 (1990) 767.
28. H. Vetters, K. Bullerdiek: Sonderbd. prakt. Metallographie 33 (2002) 41.
29. H. Vetters: Z. Werkstoffe, Wärmebehandlung, Fertigung, Härterei-Techn. Mitt. 57 (2002) 168.
30. C. Razim: Ḧrterei-Techn. Mitt. 23 (1968) 1.
31. S. Laue, C. Thoben, H. Bornas, R. Schröder, R. Kienzier: Z. Werkstoffe, Wärmebehandlung, Fertigung, Härterei-Techn. Mitt. 60 (2005) 271.
32. D. Munz, K. Schwalbe, P. Mayr: Dauerschwingverhalten metallischer Werkstoffe, Braunschweig: Friedr. Vieweg + Sohn GmbH (1971).