Shortening the duration of heat treatment in the lower bainitic range

Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment

Volumn 25, Issue 5, 2004, Pages 555-560

  Dong, J ^a   Vetters, H ^a   Zoch, H W ^a  

^a Bremen Institute for Materials Testing   (Germany)

Author keywords

Bainite; Bearing steel; Dilatometry

Indexed keywords

BAINITE; BAINITIC TRANSFORMATIONS; DILATOMETERS; DIMENSIONAL STABILITY; HARDNESS; MARTENSITE; METALLOGRAPHIC MICROSTRUCTURE;

BEARING STEEL; COST REDUCTION; DURATION; ISOTHERMAL BAINITIC TREATMENT; LOWER BAINITIC RANGE; MARTENSITIC HARDENING; POSTQUENCHING; PREQUENCHING; RETAINED AUSTENITE;

HEAT TREATMENT;

EID: 12444336882     PISSN: 10096264     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (15)

1. Macherauch E and Vohringer O. Verformungsverhalten geharteter Stable. Harterei-Technische Mitteilungen, 1986, 41(2): 71-90.
2. Slycke J, Fajers C and Volkmuth J. Berechnung der MaBstabilitat von Walzlagerbauteilen. Harterei-Technische Mitteilungen, 2002, 57(3): 156-163.
3. Hengerer F, Lucas G and Nyberg B. Zwischenstufenumwandlung von Walzlagerstahlen. Harterei-Technische Mitteilungen, 1974, 29(2): 71-79.
4. Jellinghaus W. Anregung der Zwischenstufen-Umwandlung des Stahles durch kleine Mengen von α-Eisen, Archiv fur das Eisenhuttenwesen. 1952, 23(11/12): 459-470.
5. Schaaber O. Uber Einflussfaktoren bei der isothermen Austenitumwandlung in der Zwischenstufe (Bainitgebiet) II. Draht, 1952: 127-137.
6. Li C, Wang J L. Effect on pre-quenching on martensitic-bainitic microstructure and mechanical properties of GCrl5 bearing steel. Journal of Materials Science, 1993, 28: 2112-2118.
7. Hengerer F, Lucas G and Nyberg B. Zwischenstufenumwandlung von Walzlagerstahlen. Harterei-Technische Mitteilungen, 1974, 29(2): 71-79.
8. Christian J W and Edmonds D V. The Bainite Transformation. In: Marder A R, Goldstein J I, Eds. Phase Transformations in Ferrous Alloys. Warrendale, PA, 1984, 293-325.
9. Volkmuth J. Verfahren zur Warmebehandlung von Bauteilen aus Stahl oder Gusseisen. Patent, EP 0 896 068 Bl, SKF GmbH, 1998
10. Maruki M, Ohbayashi K and Suzuki T. A temperature-raising bainite-forming process. Patent, EP 0 794 262 Bl, AISIN AW Co., Ltd, 1997
11. Foerster L, Michalski M, Becht A, Englert K O and Czeringer M. Verfahren zum Bainitisieren von Stahlteilen. Patent, EP 1 248 862 Al, Robert Bosch GmbH, 2000
12. Bhadeshia H K D H and Christian J W. Bainite in Steels. Metallurgical Transactions A. 1990, 21A: 767-797.
13. Jellinghaus W. Einfluss des Kohlenstoffgehaltes auf den Austenitzerfall und dessen Teilreaktionen. Archiv fur das Eisenhuttenwesen. 1957, 28(8): 469-481.
14. Spanos G, Fang H S and Aaronson H I. A Mechanism for the Formation of Lower Bainite. Metallurgical Transactions A. 1990, 21A: 1381-1389.
15. Vetters H. Walzelemente aus 100Cr6, bainitisch umwandeln oder martensitisch harten? Harterei-Technische Mitteilungen, 2002, 57(6): 403-408.