SEM in-situ investigation on fatigue cracking behavior of P/M Rene95 alloy with surface inclusions

Journal of University of Science and Technology Beijing: Mineral Metallurgy Materials (Eng Ed)

Volumn 13, Issue 3, 2006, Pages 244-249

  Wang, Xishu ^a   Zhang, Lina ^a,b   Zeng, Yanping ^b   Xie, Xishan ^b  

^a TSINGHUA UNIVERSITY   (China)

^b UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

Fatigue behavior; In situ observation; Inclusion; P M Rene95 alloy; Powder metallurgy; SEM

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; INCLUSIONS; POWDER METALLURGY; SCANNING ELECTRON MICROSCOPY;

FATIGUE CRACK; IN-SITU OBSERVATION; RENE95 ALLOY; SURFACE INCLUSIONS;

ALLOYS;

EID: 33747422790     PISSN: 10058850     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1005-8850(06)60052-2     Document Type: Article

References (27)

1. R. Baccino, F. Moret, F. Pellerin, et al., High performance and high complexity net shape parts for gas turbines: the ISOPREC powder metallurgy process, Mater. Des., 21 (2000), p. 345.
2. A. Fujiki, Present state and future prospects of powder metallurgy parts for automotive applications, Mater. Chem. Phys., 67 (2001), p. 298.
3. Y. Murakami, S. Kodama, and S. Konuma, Quantitative evaluation of defects of non-metallic inclusions on fatigue strength of high strength steels. I: Basic fatigue mechanism and evaluation of correlation between the fatigue fracture stress and size and location of non-metallic inclusions, Int. J. Fatigue, 11 (1989), p. 291.
4. A. Melander, M. Rolfsson, A. Nordgren, et al., Influence of inclusion content on fatigue properties of SAE 52100 bearing steels, Scand. J. Metall, 20 (1991), p. 229.
5. J. Monnot, B. Heritier, and J.Y. Cogne, Relationship of meting practice, inclusion type and size with fatigue resistance of bearing steels, ASTM STP, 987 (1988), p. 149.
6. T. Lund, S.A. Johansson, and L.J.P. Olund, Nucleation of fatigue in very low oxygen bearing steels, ASTM STP, 1327 (1998), p. 124.
7. M. Larsson, A. Melander, and A. Nordgren, The Effect of Inclusions on the Fatigue Behavior of Hardened Spring Steel-An Experimental and Theoretical Study, Sweden, 1992, p. 1.
8. Y. Bergengren, M. Larsson, and A. Melander, The influence of machining defects and inclusions on the fatigue of a hardened spring steel, Fatigue Fract. Eng. Mater. Struct., 18 (1995), p. 1071.
9. Y. Murakami, M. Takada, and T. Toriyama, Super-long life tension-compression fatigue properties of quenched and tempered 0.46% carbon steel, Int. J. Fatigue, 16 (1998), No. 9, p. 661.
10. X.S. Wang, F. Liang, Y.P. Zeng, et al, SEM in-situ observations to investigate the effects of inclusions on the low cyclic fatigue crack initiation and propagation of super strength steel, Acta Metall. Sin., 41 (2005), No. 12, p. 1272.
11. X.S. Wang and Y.Q. Li, Characterization of the fatigue surface microcrack growth in vicinal inclusion for powder metallurgy alloys, Acta Mech. Solid. Sin., 16 (2003), No. 4, p. 327.
12. T. Billaudeau, Y. Nadot, and G. Bezine, Multiaxial fatigue limit for defective materials: mechanisms and experiments, Acta Mater., 52 (2004), p. 3911.
13. P.J. Laz, and B.M. Hillberry, Fatigue life predication from inclusion initiated cracks, Int. J. Fatigue, 20 (1998), No. 4, p. 263.
14. M. Jono, SEM and AFM observation and mechanism of fatigue crack growth, [in] Proc. Fatigue'99, Proceedings of the 7th International Fatigue Conference, Beijing, 1999, p. 57.
15. X.S. Wang and J.H. Fan, SEM online investigation of fatigue crack initiation and propagation in notched cast magnesium specimens, J. Mater. Sci., 39 (2004), No. 7, p. 2617.
16. X.S. Wang, X. Lu, and H.D. Wang, Investigation of surface fatigue microcrack growth behavior of cast Mg-Al alloy, Mater. Sci. Eng. A, 364 (2004), p. 11.
17. X.S. Wang, Y. Xu, and X.Q. Xu, Direct observations of microcracking in the fuel plate using the scanning electron microscope, J. Appl. Compos. Mater., 11 (2004), No. 3, p. 145.
18. X.S. Wang, B.S. Wu, and Q.Y. Wang, Online SEM investigation of microfracture characteristics of concretes at various temperature values, Cem. Concr. Res., 35 (2005), No. 7, p. 1385.
19. X.S. Wang and J.H. Fan, An evaluation the growth rate of small fatigue cracks in cast AM50 magnesium alloy at different temperature in vacuum environment, Int. J. Fatigue, 28 (2006), No. 1, p. 79.
20. X.S. Wang and Y. Xu, Experiments, characterizations and analyses of dispersion U3S12-Al fuel plate with sandwich structure, J. Nucl. Mater., 328 (2004), No. (2-3), p. 243.
21. I.S. Raju and J.C. Newman, Stress-intensity factors for a wide range of semi-elliptical surface cracks in finitethickness plates, Eng. Fract. Mech., 11 (1979), p. 817.
22. A.E. Green and I.N. Sneddon, The distribution of stress in the neighborhood of a flat elliptic crack in an elastic solid, [in] Proc. Cambrige Phil. Soc., London, 1976, p. 46.
23. X.S. Wang and N. Kawagoishi, A simple predicting method of fatigue crack growth rate based on a tensile strength of carbon steel, J. Iron Steel Res. Int., 10 (2003), No. 2, p. 58.
24. X.S. Wang, Y.Q. Li, and S.W. Yu, Evaluation of the thermal-mechanical fatigue behavior for 62Sn38Pb bulk solder, J. Exp. Tech., 27 (2003), No. 2, p. 31.
25. H. Nisitani, M. Goto, and N. Kawagoishi, A small crack growth law and its related phenomena, J. Eng. Fract. Mech., 41 (1992), No. 4, p. 499.
26. X.Q. Feng and S.W. Yu, An upper bound on damage of elastic-plastic structures at shakedown, J. Damage Mech., 3 (1994), p. 277.
27. M. Carpurso, Some upper bound principles to plastic strains in dynamic shakedown of elastic-plastic structures, J. Struct. Mech., 7 (1979), No. 1, p. 1.