Fatigue and fracture behaviour of structural Al-alloys up to very long life regimes

International Journal of Fatigue

Volumn 28, Issue 11, 2006, Pages 1572-1576

  Wang, Q Y ^a   Kawagoishi, N ^b   Chen, Q ^b  

^a SICHUAN UNIVERSITY   (China)

^b KAGOSHIMA UNIVERSITY   (Japan)

Author keywords

Aluminium alloys; Fatigue crack growth; Fatigue crack initiation; Fractography; High cycle fatigue; Interfacial voids

Indexed keywords

COALESCENCE; FATIGUE OF MATERIALS; FRACTOGRAPHY; FRACTURE; PIEZOELECTRIC MATERIALS;

FATIGUE CRACK GROWTH; FATIGUE CRACK INITIATION; HIGH CYCLE FATIGUE; INTERFACIAL VOIDS;

ALUMINUM ALLOYS;

EID: 33746327465     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.09.017     Document Type: Article

References (19)

1. Pardoen T., and Hutchinson J.W. Micromechanics-based model for trends in toughness of ductile metals. Acta Mater 51 (2003) 133-148
2. Agarwal H., Gokhale A.M., Graham S., and Horatemeter M.F. Void growth in 6061-aluminium alloy under triaxial stress state. Mater Sci Eng A341 (2003) 35-42
3. Tvergaard V., and Hutchinson J.W. Two mechanisms of ductile fracture: void by void growth versus multiple void interaction. Int J Solids Struct 39 (2002) 3581-3597
4. Bandstra J.P., and Koss D.A. Modeling the ductile fracture process of void coalescence by void-sheet formation. Mater Sci Eng A319-321 (2001) 490-495
5. Sunder R., Porter W.J., and Ashbaugh N.E. Fatigue voids and their significance. Fatigue Fract Eng Mater Struct 25 (2002) 1015-1024
6. Wang Q.Y., Pidaparti R.M., and Palakal M.J. Comparative study of pitting corrosion fatigue in aircraft materials. AIAA J 39 (2001) 325-330
7. Wang Q.Y., Kawagoishi N., Chen Q., and Pidaparti R.M. Evaluation of the probability distribution of pitting corrosion fatigue life in aircraft materials. Acta Mech Sinica 19 (2003) 247-252
8. Wang Q.Y., Kawagoishi N., and Chen Q. Effect of pitting corrosion on the very high cycle life fatigue behaviour. Scripta Mater 49 (2003) 711-716
9. Heuler P., and Birk O. Durability assessment of automotive aluminium parts. Fatigue Fract Eng Mater Struct 25 (2002) 1135-1148
10. Wang Q.Y., Berard J.Y., Dubarre A., Rathery S., and Bathias C. Gigacycle fatigue of ferrous alloys. Fatigue Fract Eng Mater Struct 22 (1999) 667-672
11. Wang Q.Y., Berard J.Y., Rathery S., and Bathias C. High-cycle fatigue crack initiation and propagation behaviour of high-strength spring steel wires. Fatigue Fract Eng Mater Struct 22 (1999) 673-677
12. Wang Q.Y., Bathias C., Kawagoishi N., and Chen Q. Effect of inclusion on subsurface crack initiation and gigacycle fatigue strength. Int J Fatigue 24 (2002) 1269-1274
13. Yan N., Kawagoishi N., Chen Q., and Wang Q.Y. Fatigue properties of Inconel718 in long life region at elevated temperature. Key Eng Mater 243-244 (2003) 321-326
14. Shiozawa K., and Lu L. Very high-cycle fatigue behaviour of shot-peened high-carbon-chromium bearing steel. Fatigue Fract Eng Mater Struct 25 (2002) 813-822
15. Murakami Y., Takada M., and Toriyama T. Super-long life tension-compression fatigue properties of quenched and tempered 0.46% carbon steel. Int J Fatigue 20 (1998) 661-667
16. Bathias C. There is no infinite fatigue life in metallic materials. Fatigue Fract Eng Mater Struct 22 (1999) 559-565
17. Mayer H. Fatigue crack growth and threshold measurements at very high frequencies. Int Mater Rev 44 (1999) 1-34
18. Wang QY. Gigacycle fatigue of ferrous alloys. Ph.D thesis, Ecole Centrale Paris, France, 1998.
19. Srivatsan T.S. The fatigue properties and fracture behaviour of aluminium alloy 7050-T7651. Mater Design 23 (2002) 141-150