Failure mechanisms of laminated composites subjected to static indentation

Composite Structures

Volumn 75, Issue 1-4, 2006, Pages 489-495

  Chen, Puhui ^a   Shen, Zhen ^b   Xiong, Junjie ^a   Yang, Shengchun ^b   Fu, Shaoyun ^c   Ye, Lin ^d  

^a NANJING UNIVERSITY OF AERONAUTICS AND ASTRONAUTICS   (China)

^b AIRCRAFT STRENGTH RESEARCH INSTITUTE OF CHINA   (China)

^c TECHNICAL INSTITUTE OF PHYSICS AND CHEMISTRY   (China)

^d UNIVERSITY OF SYDNEY   (Australia)

Author keywords

Contact force; Damage resistance; Dent depth; Indentation

Indexed keywords

CRACKS; DELAMINATION; FAILURE (MECHANICAL); INDENTATION;

CONTACT FORCE; DAMAGE RESISTANCE; DENT DEPTH;

LAMINATED COMPOSITES;

COMPOSITE; CRACKING; DAMAGE; DELAMINATION; FAILURE ANALYSIS; LOADING (TESTING);

EID: 33745760857     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2006.04.087     Document Type: Article

References (9)

1. Lagace P.A., Williams J.E., and Tsang P.H.W. A preliminary proposition for a test method to measure (impact) damage resistance. J Reinforced Plast Compos 12 (1993) 585-601
2. Lee S.M., and Zahuta P. Instrumented impact and static indentation of composites. J Compos Mater 25 (1991) 204-222
3. Sutherland L.S., and Guedes Soares C. Contact indentation of marine composites. Compos Struct 70 3 (2005) 287-294
4. Shyr T.-W., and Pan Y.-H. Impact resistance and damage characteristics of composite laminates. Compos Struct 62 (2003) 193-203
5. Zhang J.Y., Yu T.X., Kim J.K., and Sui G.X. Static indentation and impact behavior of reformed bamboo/aluminum laminated composites. Compos Struct 50 (2000) 207-216
6. Clarence C. Poe, Jr. Mechanics methodology for textile perform composite materials. NASA-96-28istc-ccp.
7. Zenkert D., Shipsha A., and Persson K. Static indentation and unloading response of sandwich beams. Composites: Part B 35 (2004) 511-522
8. ASTM D 6264-98(04): Standard test fiber-reinforced polymer-matrix composite to concentrated quasi-static indentation force. 2004.
9. Freeman SM. Characterization of lamina and interlaminar damage in graphite-epoxy composites by the deply technique. Composite materials: testing and design (sixth conference), ASTM STP, vol. 787, 1982. p. 50-62.