Impact resistance and damage characteristics of composite laminates

Composite Structures

Volumn 62, Issue 2, 2003, Pages 193-203

  Shyr, Tien Wei ^a   Pan, Yu Hao ^a  

^a FENG CHIA UNIVERSITY   (Taiwan)

Author keywords

Composite laminate; Impact damage; Low velocity impact

Indexed keywords

BENDING (DEFORMATION); CRACK INITIATION; DELAMINATION; FABRICS; FAILURE (MECHANICAL); FRACTOGRAPHY; IMPACT RESISTANCE; IMPACT TESTING; METALLOGRAPHY; MICROSCOPIC EXAMINATION; REINFORCEMENT; STRENGTH OF MATERIALS; STRESSES;

FIBER BREAKAGE;

LAMINATED COMPOSITES;

DAMAGE; GLASS FIBER FABRIC; IMPACT RESISTANCE; LAMINATE; MAT; NONWOVEN FABRIC; STRENGTH;

EID: 0042326566     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0263-8223(03)00114-4     Document Type: Article

References (41)

1. de Freitas M. Reis L. Failure mechanisms on composite specimens subjected to compression after impact Compos. Struct. 42 1998 365-373
2. Hitchen S.A. Kemp R.M.J. The effect of staking sequence on impact damage in a carbon fibre/epoxy composite Composite 26 1995 207-214
3. de Freitas M. Silva A. Reis L. Numerical evaluation of failure mechanisms on composite specimens subjected to impact loading Composites: Part B 31 2000 199-207
4. Cantwell W.J. Morton J. Comparison of the low and high velocity impact response of CFRP Composites 20 6 1989 545-551
5. Cantwell W.J. Morton J. Detection of impact damage in CFRP laminates Compos. Struct. 3 1985 241-257
6. Davies G.A.O. Zhang X. Zhou G. Watson S. Numerical modeling of impact damage Composites 25 5 1994 342-350
7. Davies G.A.O. Zhang X. Impact damage prediction in carbon composite structure Int. J. Impact Eng. 16 1 1994 149-170
8. Zhang X. Impact damage in composite aircraft structures-experimental; testing and numerical simulation Proc. Inst. Mech. Eng. 212 1998 245-259
9. Schoeppner G.A. Abrate S. Delamination threshold loads for low velocity impact on composite laminates Composites: part A 31 2000 903-915
10. Belingardi G. Vadori R. Low velocity impact tests of laminate glass-fiber-epoxy matrix composite material plates Int. J. Impact Eng. 27 2002 213-229
11. Davies G.A.O. Hitchings D. Zhou G. Impact damage and residual strengths of woven fabric glass/polyester laminates Composites: Part A 27A 1996 1147-1156
12. Matemilola S.A. Stronge W.J. Low speed impact damage in filament-wound CFRP composite pressure vessels J. Pressure Vessel Technol. 119 4 1997 435-443
13. Alderson K.L. Evans K.E. Failure mechanisms during the transverse loading of filament-wound pipes under static and low velocity impact conditions Composites 23 3 1992 167-173
14. Hirai Y. Hamada H. Kim J.K. Impact response of woven glass-fabric composites. I. Effect of fiber surface treatment Compos. Sci. Technol. 58 1 1998 91-105
15. Zhou G. The use of experimentally-determined impact force as a damage measure in impact damage resistance and tolerance of composite structures Compos. Struct. 42 1998 375-382
16. Cartie D.D.R. Irving P.E. Effect of resin and fibre properties on impact and compression after impact performance of CFRP Composites: Part A 33 2002 483-493
17. Sjöblom P. Simple design approach against low velocity impact damage. In: Proceeding of 32nd SAMPE Symposium, Anaheim, CA, 1987, p. 529-39
18. Olsson R. A review of impact experiments at FFA during 1986 to 1998. The Aeronautical research Institute of Sweden. FFA TN 1999-08, 1999
19. Dorey G. Impact damage in composites-development, consequences, and prevention. In: Proc. 6th Int. Conf. on Composite Materials and 2nd European Conf. on Composite materials. London: Imperial College, vol. 3, 1988, p. 3.1-3.26
20. Zhou G. Prediction of impact damage thresholds of glass fiber reinforced laminates Compos. Struct. 31 1995 185-193
21. Zhou G. Effect of impact damage on residual compressive strength of glass-fiber reinforced polyester (GFRP) laminates Compos. Struct. 35 1995 171-181
22. Zhou G. Compressive behaviour of large undamaged and damaged thick laminated panels Compos. Struct. 38 1997 588-597
23. Scardino F. An introduction to textile structures and their behavior. In: Chou TW, Ko FK, editors. Composite material series, 3: Textile structural composites. Amsterdam: Elsevier; 1989, p. 1-22
24. Bibo G.A. Hogg P.J. Influence of reinforcement architecture on damage mechanisms and residual strength of glass-epoxy/epoxy composite systems Compos. Sci. Technol. 58 1998 803-813
25. Shyr TW, Ouyang C, Pan YH. Impact damage and residual strength of multiaxial warp knitted glass fabric reinforced polyester laminate. In: Proceedings of the 12th International Conference on Composite Materials (ICCM/12), Paris, 5-9 July 1998, Paper ID 944
26. Kang T.J. Kim C. Energy-absorption mechanisms in Kevlar multiaxial warp-knit fabric composite under impact loading Compos. Sci. Technol. 60 2000 184-773
27. Bibo G.A. Hogg P.J. Backhouse R. Mills A. Carbon-fibre non-crimp fabric laminates for cost-effective damage-tolerant structures Compos. Sci. Technol. 58 1998 129-143
28. Morii T. Hamada H. Desaeger M. Gotoh A. Yokoyama A. Verpoest I. Maekawa Z.I. Damage tolerance of glass mat/epoxy laminates hybridized with flexible resin under static and impact loading Compos. Struct. 32 1995 133-139
29. Cantwell W.J. Morton J. The impact resistance of composite materials-a review Composites 22 5 1991 347-362
30. Cantwell W.J. Morton J. The significance of damage and defects and their detection in composite materials: A review J. Strain Anal. 27 1 1992 29-42
31. Abrate S. Impact on laminated composite materials Appl. Mech. Rev. 44 4 1991 155-190
32. Abrate S. Impact on laminated composites: Recent advances Appl. Mech. Rev. 47 11 1994 517-544
33. Abrate S. Impact on composite structures 1998 Cambridge university press Cambridge
34. Richardson M.O.W. Wisheart M.J. Review of low-velocity impact properties of composite materials Composites: Part A 27A 1996 1123-1131
35. Lesser A.J. Effect of resin crosslink density on the impact damage resistance of laminated composites Polymer Compos. 18 1997 16-27
36. Liu D. Impact-induced delamination-a view of bending stiffness mismatching J. Compos. Mater. 22 1988 674-691
37. Abrate S. Impact on composite structures 1998 Cambridge university press Cambridge p. 161-62
38. Davies GAO, Robinson P. Predicting failure by debonding/delamination. 'AGARD: 74th Structures and Materials Meeting 1992
39. Chaudhri M.M. Chen L. The orientation of the Hertzian cone crack in soda-lime glass formed by oblique dynamic and qusi-static loading with a hard sphere J. Mater. Sci. 24 1989 3441-3448
40. Hirai Y. Hamada H. Kim J.K. Impact response of woven glass-fabric composites. II. Effect of temperature Compos. Sci. Technol. 58 1 1998 119-128
41. Delfosse D. Poursartip A. Energy-based approach to impact damage in CFRP laminates Composites: Part A 28A 1997 647-655