SCC behavior in the transitiion region of an alloy 182-SA 508 Cl.2 dissimilar weld joint under simulated BWR-NWC conditions

Proceedings of the Twelfth International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors

Volumn , Issue , 2005, Pages 589-599

  Peng, Qunjia ^a,c   Shoji, Tetsuo ^a   Ritter, Stefan ^b   Seifert, Hans Peter ^b  

^a TOHOKU UNIVERSITY   (Japan)

^b PAUL SCHERRER INSTITUTE   (Switzerland)

^c UNIVERSITY OF MICHIGAN   (United States)

Author keywords

Alloy 182; Boiling Water Reactor; Crack Growth Rate; Dissimilar Weld Joint; Low Alloy Steel; Stress Corrosion Cracking

Indexed keywords

BOILING WATER REACTORS; CHARACTERIZATION; MICROSTRUCTURE; STRESS CORROSION CRACKING; WELDABILITY;

ALLOY 182; CRACK GROWTH RATE; DISSIMILAR WELD JOINT; LOW ALLOY STEEL; NORMAL WATER CHEMISTRY (NWC);

TRANSITION METAL ALLOYS;

EID: 33745223255     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (28)

1. th Int. Symp. on Contribution of Materials Investigation to the Resolution of Problems Encountered in Pressurized Water Reactors (Fontevraud 5), Fontevraud, France, September 23-27, 2002, CD-ROM.
2. th Int. Symp. on Contribution of Materials Investigation to the Resolution of Problems Encountered in Pressurized Water Reactors (Fontevraud 5), Fontevraud, France, September 23-27, 2002, CD-ROM.
3. P. Andresen, "Observation and Prediction of the Effects of Water Chemsitry and Mechanics on Environmentally Assited Cracking of Inconels 182 Weld Metal and 600," Corrosion, 44 (1988), 376-385.
4. M. Itow et al., "Crack Growth Rates of Alloy 182 in High Temperature Water," Proc. 7th Inter. Sym. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Houston, TX: NACE International, 1995), 541-551.
5. th Int. Sym. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL: ANS, 1997), 712-719.
6. P.L. Andresen et al., "Stress Corroison Crack Growth rate Behavior of Ni Alloys 182 and 600 in High Temperature Water," NACE Corrosion 2002 (Houston, TX: NACE International, 2002), Paper No. 02510, CD-ROM.
7. th Int. Sym. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL: ANS, 1997), 422-429.
8. th Int. Sym. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: TMS, 1999), 279-295.
9. th Int. Sym. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: TMS, 1999), 217-224.
10. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 2001), CD-ROM.
11. Q. J. Peng, H. Yamauchi, and T. Shoji, Metall. Mater. Trans. A, 34A(9) (2003), 1891-1899.
12. H.P. Seifert, S. Ritter, and J. Hickling, "Research and Service Experience with Environmentally Assisted Cracking of Low-Alloy Steel Pressure-Boundary Components under LWR Conditions," Power Plant Chemistry, 6 (2004), 111-123.
13. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL: ANS, 2003), CD-ROM.
14. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL: ANS, 2003), CD-ROM.
15. th Int. Sym. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: TMS, 1999), 331 -337.
16. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL: ANS, 1997), 704-711.
17. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Warrendale, PA: TMS, 1993), 379-4.
18. P. L. Andresen, "Fracture mechanics Data and Modeling of Environmentally cracking of Nickel-Base Alloys in High-Temperature Water," Corrosion, 47 (12) (1991), 917-938.
19. A. McMinn, and R. A. Page, "Stress Corrosion Cracking of Inconel Alloys and Weldments in High Temperature Water -The Effect of Sulfuric Acid Addition," Corrosion, 44 (1988) 239-247.
20. P. Andresen, "Effects of Dissolved Oxygen, Solution Conductivity and Stress Intensity on the Interdendritic Stress Corrosion Cracking of Alloy 182 Weld Metal," NACE Corrosion /87 (Houston, TX: NACE International, 1987), Paper No. 85.
21. R. A. Page, "Stress Corrosion of Alloys 600 and 690 and Nos. 82 and 182 Weld Metals in High Temperature Water," Corrosion, 39 (1983) 409-421.
22. th International Conference on Nuclear Engineering, Shinjuku, Tokyo, Japan, April 20-23, 2003, Paper ICONE11-36056.
23. th International Conference on Nuclear Engineering, April 8-12, 2001, Nice, France, Paper ICONE 9-66.
24. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 2001), CD-ROM.
25. G.F. Li, and J. Congleton, "Stress Corrosion Cracking of Low Alloy Steel to Stainless Steel Transition Weld in PWR Primary Water at 292°C," Corrosion Science, 42 (2000), 1005-1021.
26. th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange Park, IL : ANS, 1999), 430-438.
27. M. Ruscak et al., "Structural Aspects of the Environmentally Assisted Cracking of WWER 440 Dissimilar Weld Joints," Int. J. Pres. Ves. And Piping, 68 (1996) 23-37.
28. R. Page, "Stress Corrosion of 1-182 Weld Metal in High Temperature Water - The Effect of a Carbon Steel Couple," Corrosion, 41 (1985) 338-344.