Analytical electron microscopy of the mixed zone in NiCoCrAlY-based EB-PVD thermal barrier coatings: As-coated condition versus late stages of TBC lifetime

Materials at High Temperatures

Volumn 22, Issue 3-4, 2005, Pages 393-401

  Braue, W ^a   Schulz, U ^a   Fritscher, K ^a   Leyens, C ^a,b   Wirth, R ^c  

^a GERMAN AEROSPACE CENTER DLR   (Germany)

^b BRANDENBURG UNIVERSITY OF TECHNOLOGY   (Germany)

^c GFZ GERMAN RESEARCH CENTRE FOR GEOSCIENCES   (Germany)

Author keywords

Analytical transmission electron microscopy; EB PVD TBC systems; Mixed zone; NiCoCrAlY bond coat; TGO TBC reaction zone

Indexed keywords

CHROMIUM ALLOYS; ELECTRONS; MICROSTRUCTURE; PHYSICAL VAPOR DEPOSITION; THERMAL BARRIER COATINGS; TRANSMISSION ELECTRON MICROSCOPY; ZIRCONIA;

ANALYTICAL TRANSMISSION ELECTRON MICROSCOPY; EB-PVD TBC SYSTEMS; MIXED ZONE; NICOCRALY BOND COAT; TGO/TBC REACTION ZONE;

NICKEL ALLOYS;

EID: 33745172118     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.046     Document Type: Article

References (38)

1. Evans, A.G., Mumm, D.R., Hutchison, J.W., Meier, G.H. and Pettit, F.S. Mechanisms controlling the durability of thermal barrier coatings. Prog. Mater. Sci., 46, 505-553 (2001).
2. Leyens, C., Schulz, U., Fritscher, K., Bartsch, M., Peters, M. and Kaysser, W.A. Contemporary materials issues for advanced EB-PVD thermal barrier coatings. Z Metallkd., 92, 762-772 (2001).
3. Yanar, N.M., Kim, G., Hamano, S., Pettit, F.S. and Meier, G.H. Microstructural characterization of the failures of thermal barrier coatings on Ni-base superalloys. Mater. High Temp., 20, 495-506 (2003).
4. Stiger, M.J., Yanar, N.M., Topping, M.G., Pettit, F.S. and Meier, G.H. Thermal barrier coatings for the 21st century. Z. Metallkd., 90, 1069-1078 (1999).
5. Sohn, Y.H., Kim, J.H., Jordan, E.H. and Gell, M. Thermal cycling of EB-PVD/MCrAlY thermal barrier coatings: I. Microstructural development and spallation mechanisms. Surf. Coat. Technol, 146-147, 70-78 (2001).
6. Kim, G.M., Yanar, N.M., Hewitt, E.N., Pettit, F.S. and Meier, G.H. The effect of the type of thermal exposure on the durability of thermal barrier coatings. Scripta Mater., 46, 489-495 (2002).
7. Levi, C.G., Sommer, E., Terry, S.G., Catanoiu, A. and Rühle, M. Alumina grown during deposition of thermal barrier coatings. J. Am. Ceram. Soc., 86, 676-685 (2003).
8. Leyens, C., Yang, Y.Q. and Schulz, U. Formation of the alumina-zirconia bonding zone in EB-PVD thermal barrier coatings. In: McNallum, M. and Opila, E. (eds) High Temperature Corrosion and Materials Chemistry III, pp. 28-37. The Electrochemical Society, Pennington, NJ (2001).
9. 2 Electron Beam-Physical Vapor Deposition Coatings on Ni-Base Superalloys. J. Am. Ceram. Soc., 77, 984 (1994).
10. Murphy, K.S., More, K.L. and Lance, M.J. As-deposited mixed zone in thermally grown oxide beneath a thermal barrier coating. Surf. Coat. Technol., 146-147, 152-161 (2001).
11. Lakiza, S.N. and Lopato, L.M. Stable and metastable phase relations in the system alumina- zirconia-yttria. J. Am. Ceram. Soc., 80(4), 893-902 (1997).
12. Levin, I. and Brandon, D. Metastable Alumina Polymorphs: Crystal Structures and Transition Sequences. J. Am. Ceram. Soc., 81, 1995-2012 (1998).
13. Levi, C.G. Metastability and microstructure evolution in the synthesis of inorganics from precursors. Acta Mater., 46, 787-800 (1998).
14. Yang, J.C., Schumann, E. and Rühle, M. Transient Oxidation of NiAl. Acta Mater., 46, 2195-2201 (1998).
15. Brickey, M.R. and Lee, J.L. Structural and chemical analyses of thermally grown oxide scales in thermal barrier coatings containing a platinum-nickel-aluminide bondcoat. Oxid. Metals, 54, 237-254 (2000).
16. Ragan, D.D., Mates, T. and Clarke, D.R. Effect of yttrium and erbium ions on epitaxial phase transformations in alumina. J. Am. Ceram. Soc., 86, 541-545 (2003).
17. 3. Z. Metallkd., 95, 27-39 (2004).
18. Braue, W., Fritscher, K., Schulz, U., Leyens, C. and Wirth, R. Nucleation and growth of oxide constituents on NiCoCrAlY bond coats during the different stages of EB-PVD TBC deposition and upon thermal loading. Mater. Sci. Forum, 461-464, 899-906 (2004).
19. Laxman, S., Franke, B., Kempshall, B.W., Sohn, Y.H., Giannuzzi, L.A. and Murphy, K.S. Phase transformation of thermally grown oxide on (Ni,Pt)Al bondcoat during electron beam physical vapor deposition and subsequent oxidation. Surf. Coat. Technol., 177-178, 121-130 (2004).
20. Schulz, U., Menzebach, M., Leyens, C. and Yang, Y.Q. Influence of substrate material on oxidation behavior and cyclic lifetime of EB-PVD TBC systems. Surf. Coat. Technol., 146-147, 117-123 (2001).
21. Burns, A.J., Subramanian, R., Kempshall, B.W. and Sohn, Y.H. Microstructure of as-coated thermal barrier coatings with varying lifetimes. Surf. Coat. Technol., 177-178, 89-96 (2004).
22. Wirth, R. Focused-Ion-Beam (FIB): A novel technology for advanced application of micro- and nanoanalysis in geosciences and applied mineralogy. Eur. J. Mineral., 16, 863-876 (2004).
23. Schulz, U., Fritscher, K. and Kaysser, W.A. Cyclic lifetime of PYSZ and CeSZ EB-PVD TBC systems on various Ni-superalloy substrates. In: Lecomte-Beckers, J., Carton, M., Schubert, F. and Ennis, P.J. (eds.) COST 2002, Liege: Vol. 21-1, pp. 483-492 (2002).
24. Brumm, W.M. and Grabke, H.J. The oxidation behavior of NiAl, I. Phase transformations in the alumina scale during oxidation of NiAl and Ni-Al-Cr alloys. Corros. Sci., 33, 1677-1690 (1992).
25. Quadakkers, W.J., Shemet, V., Sebold, D., Anton, R., Wessel, E. and Singheiser, L. Oxidation characteristics of a platinized MCrAlY bond coat for TBC systems during cyclic oxidation at 1000°C. Surf. Coat. Technol., 199, 77-82 (2005).
26. (2-x/2) materials synthesized with liquid precursors. J. Am. Ceram. Soc., 77, 2069-2075 (1994).
27. Svensson, H., Stiller, K. and Angenete, J. Investigation of oxide formation during short-term oxidation of model NiAl alloys. Mater. Sci. Forum, 461-464, 231-238 (2004).
28. Shillington, E.A.G. and Clarke, D.R. Spalling failure of a thermal barrier coating associated with aluminum depletion in the bond coat. Acta Mater., 47, 1297-1305 (1999).
29. 3 growth upon high-temperature oxidation of NiCrAl alloys: experiment versus model predictions. Acta Mater., 53, 1643-1653 (2005).
30. Kofstad, P. High Temperature Corrosion. Elsevier Applied Science, London, 1988.
31. Schütze, M. Fundamentals of high temperature corrosion. In: Schütze, M. (ed.) Corrosion and Environmental Degradation, Wiley, 2000.
32. Hou, P. Impurity effects on alumina scale growth. J. Am. Ceram. Soc., 86, 660-668 (2003).
33. Lelait, L., Alpérine, S. and Mévrel, R. Alumina scale growth at zirconia/MCrAlY Interface: a microstructural study. In: Bennett, M.J. and Lorimer, G.W. (eds) Proc. 1st International Conference on Microscopy of Oxidation, pp. 161-168. University of Cambridge, March 26-28, 1990, The Institute of Metals, 1991.
34. Schilbe, J.E. Substrate alloy element diffusion in thermal barrier coatings. Surf. Coat. Technol., 133-134, 35-39 (2000).
35. 2 system. Mater. Sci. Eng., A145, 113-118 (1991).
36. Bloss, F.D. Crystallography and crystal chemistry. Holt, Rinehart and Winston, (1971).
37. 3 at 1600°C in Air. J. Am. Ceram. Soc., 65, C166-168 (1982).
38. 1.5 in Air. J. Am. Ceram. Soc., 67, C240-242 (1984).