An oxidation study of an MCrAlY overlay coating

Materials at High Temperatures

Volumn 22, Issue 3-4, 2005, Pages 433-436

  Taylor, M P ^a  

^a UNIVERSITY OF BIRMINGHAM   (United Kingdom)

Author keywords

CM186LC alloy; LPPS MCrAlY coating; Oxidation behaviour

Indexed keywords

ALUMINUM ALLOYS; COATING TECHNIQUES; OXIDATION RESISTANCE; POWER PLANTS; REACTION KINETICS; THERMAL EFFECTS;

CM186LC ALLOYS; DUPLEX STRUCTURE; LPPS MCRALY COATING; OXIDATION BEHAVIOUR;

CHROMIUM ALLOYS;

EID: 33745152315     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.051     Document Type: Article

References (14)

1. 3-forming alloys and coatings. Mater. Sci. Engng., 87, 267-274 (1987).
2. Prescott, R. and Graham, M.J. The formation of aluminium oxide scales on high-temperature alloys. Oxidat. Met., 38(3-4), 233-254 (1992).
3. 3 Scales on Fe-Al and Ni-Al Alloys at 1100°C. Solid State Ionics, 53-6, 229-237, Part 1 Jul-Aug (1992).
4. Chevalier, S., Strehl, G., Favergeon, J., Desserrey, F., Weber, S., Heintz, O., Borchardt, G. and Larpin, J.P. Use of oxygen isotope to study the transport mechanism during high temperature oxide scale growth. Mater. High Temp., 20(3), 253-259 (2003).
5. Guerre, C., Rémy, L. and Molins, R. Alumina scale growth and degradation modes of a TBC system. Mater. High Temp., 20(4), 481-485 (2003).
6. Yanar, N.M., Kim, G., Hamano, S., Pettit, F.S. and Meier, G.H. Microstructural characterisation of the failures of thermal barrier coatings on ni-base superalloys. Mater. High Temp., 20(4), 495-506 (2003).
7. Bouhanek, K., Adesanya, O.A., Stott, F.H., Skeldon, P., Lees, D.G. and Wood, G.C. Isothermal and thermal cyclic oxidation behaviour of thermal barrier coatings: Pt aluminide bond coats. Mater. High Temp., 17(1/2), 185-196 (2000).
8. Evans, A.G., Mumm, D.R., Hutchinson J.R., Meier, G.H. and Pettit, F.S. Mechanisms Controlling the Durability of Thermal Barrier Coatings. Prog. Mater. Sci., 46, 505-553 (2001).
9. Taylor, M.P. and Evans, H.E. Formation of diffusion cells in LPPS MCrAlY coatings. Mater. High Temp., 20(4), 461-465 (2003).
10. Gray, S., Taylor, M.P., Chau, E. and Evans, H.E. Oxide thickness to initiate spallation from a LPPS CoNiCrAlY coating. JCSE, 6 (2003).
11. Taylor, M.P., Pragnell, W.M. and Evans, H.E. Evidence for the formation of Al-rich reservoir phases resulting from interdiffusion between MCrAlY coating and Ni-based substrate. Mater. Sci. For., 461-464, 239-246 (2004).
12. Strawbridge, A. and Evans, H.E. Mechanical failure of thin brittle coatings. Eng. Failure Anal., 2, 85 (1995).
13. Hindum, H. and Whittle, D.P. Oxidat. Met., 18, 245-284 (1983).
14. Tolpygo, V. and Clarke, D.R. Microstructural evidence for counter-diffusion of aluminium and oxygen during the growth of alumina scales. Mater. High Temp., 20(3), 261-272 (2003).