Alumina scale growth and degradation modes of a TBC system

Materials at High Temperatures

Volumn 20, Issue 4, 2003, Pages 481-485

  Guerre, Catherine ^a   Rémy, Luc ^a   Molins, Régine ^a  

^a CENTRE DES MATÉRIAUX   (France)

Author keywords

Alumina scale growth; Thermal barrier coating

Indexed keywords

ALUMINA; DEGRADATION; DURABILITY; ELECTRON BEAMS; GROWTH (MATERIALS); HEAT TREATMENT; HIGH TEMPERATURE EFFECTS; MICROSTRUCTURE; MORPHOLOGY; PHYSICAL VAPOR DEPOSITION; SCANNING ELECTRON MICROSCOPY; SINGLE CRYSTALS; SUPERALLOYS; THERMAL LOAD; TRANSMISSION ELECTRON MICROSCOPY;

ALUMINA SCALE GROWTH; ELECTRON BEAM PHYSICAL VAPOR DEPOSITION (EB-PVD); THERMAL BARRIER COATINGS (TBC); THERMO MECHANICAL FATIGUE (TMF) TESTS;

THERMAL BARRIER COATINGS;

EID: 10844255951     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2003.056     Document Type: Article

References (21)

1. Remy, L. and Guedou, J.-Y. Thermo-mechanical fatigue problems in aeroengine components. Fatigue 2002, ed. A. F. Blom, EMAS, Cradley Heath , U.K., 1045-1062 (2002).
2. Pint, B.A., Wright, I.G., Lee, W.Y., Zhang, Y., Prussner, K. and Alexander, K.B., Substrate and bond coat compositions: factors affecting alumina scale adhesion. Mater. Sci. Engng. A 245, 201-211, (1998).
3. Haynes, J.A., Zhang, Y., Lee, W.Y. Pint, B.A., Wright I.G. and Cooley, K.M., Effects of platinum additions and sulphur impurities on the microstructure and scale adhesion behavior of single-phase CVD aluminide bond coatings, In: Elevated Temperature Coating: Science und Technology III, Hampikian, J.M. and Dahotre, N.B. (eds), Minerals Metals and Materials Society, 185-196 (1999).
4. Hou, P.Y. Beyond the sulfur effect. Oxid. Met., 52, 337-351 (1999).
5. Smialek, J.L., Jayne, D.T., Schaeffer, J.C. and Murphy, W.H., Effects of hydrogen annealing, sulfur segregation and diffusion on the cyclic oxidation resistance of superalloys. Thin Solid Films, 253, 285-292 (1994).
6. Hsueh, C.H. and Fuller, E.R. Residual stresses in thermal barrier coatings: effects of interface asperity curvature/height and oxide thickness, Mater. Sci. Engng, A 283, 46-55 (2000).
7. Zhang, Y.H., Withers, P.J., Fox, M.D. and Knowles, D.M., Damage mechanisms of coated systems under thermomechanical fatigue. Mater. Sci. Technol., 15, 1031-1036 (1999).
8. Wright, P.K. Influence of cyclic strain on life of a PVD TBC system. Mater. Sci. Engng, A245, 191-200 (1998).
9. Tzimas, E., Mullejans, H., Peteves, S.D., Bressers, J. and Stamm, W., Failure of thermal barrier coating systems under cyclic thermomechanical loading. Acta Mater., 48, 4699-4707 (2000).
10. Baufeld, B., Tzimas, E., Mullejans, H., Peteves, S., Bressers, J. and Stamm, W., Thermal-mechanical fatigue of MAR-M 509 with a thermal barrier coating, Mater. Sci. Engng, A315, 231-239 (2000).
11. Bickard, A. Damage under thermal-mechanical loading of a TBC and a nickel aluminide coating deposited on a single crystal superalloy (in French). Thesis, Ecole des Mines de Paris, (1998).
12. Remy, L., Alam, A. and Bickard. Thermal-mechanical creep-fatigue of coated systems. Thermomechanical Fatigue Behavior of Materials: 4th Volume, ASTM STP 1428, McGaw, M. A., Kalluri, S., Bressers, J. and Peteves, S. D. (eds) American Society for Testing and Materials, West Conshohocken, PA (2002).
13. Guerre, C. Etude des mécanismes d'endommagement d'un système barrière thermique déposé sur un superalliage base nickel. Thesis, Ecole des Mines de Paris, (2002).
14. Guerre, C., Molins, R. and Rémy, L. Study of the coating stability of a TBC system. Mater. High Temp.s. 17 (2), 197-204 (2000).
15. Molins, R., Guerre, C., Rémy, L. and Cartographies, spectrales en EDX, étude d'un système barrière thermique. Matériaux et Microscopie, Colloque SF2M, Saint-Etienne (2001).
16. 3 scales, Oxidat. Met., 48(3/4), 303-328 (1997).
17. Pint, B-A. Characterization of the high temperature oxidation of TBC-coated oxide-dispersed b-NiAl substrates. Mater. High Temp., 14(4), 403-412 (1997).
18. Caliez, M., Feyel, F., Kruch, S. and Chaboche, J.L., Oxidation induced stress fields in an EB-PVD thermal barrier coating. Surface Coatings Technol., 157, 103-110 (2002).
19. Tolpygo, V.K., Clarke, D.R. and Murphy, K.S., The effect of grit blasting on the oxidation behavior of a platinum-modified nickel-aluminide coating. Metall. Mater. Trans. A, 32A, 1467-1478 (2001).
20. Koster, A., Fleury, E., Vasseur, E. and Rémy, L. Thermal-mechanical fatigue testing. In: Automation in fatigue and fracture: testing and analysis. ASTM-STP 1231, ed. Amzallag C., 563-580 (1994).
21. Baufeld, B., Tzimas, E., Hahner, P., Mullejans, H., Peteves, S.D. and Moretto, P. Phase-angle effects on damage mechanisms of thermal barrier coatings under thermomechanical fatigue. Scripta Mater., 45, 859-865 (2001).