Aluminium depletion in FeCrAlY steel during transitional alumina formation

Materials at High Temperatures

Volumn 22, Issue 3-4, 2005, Pages 561-566

  Pragnell, W M ^a   Evans, H E ^a   Naumenko, D ^b   Quadakkers, W J ^b  

^a UNIVERSITY OF BIRMINGHAM   (United Kingdom)

^b FORSCHUNGSZENTRUM JÜLICH   (Germany)

Author keywords

Aluminium depletion; FeCrAlY steel; Transitional alumina formation

Indexed keywords

ALUMINA; ALUMINUM; ENERGY DISPERSIVE SPECTROSCOPY; FINITE DIFFERENCE METHOD; REACTION KINETICS; SCANNING ELECTRON MICROSCOPY; THERMOOXIDATION;

ALUMINIUM DEPLETION; FECRALY STEEL; OXIDATION KINETICS; TRANSITIONAL ALUMINA FORMATION;

STEEL;

EID: 33745151957     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.067     Document Type: Article

References (14)

1. Jedlinski, J. The oxidation behaviour of FeCrAl 'alumina forming' alloys at high temperatures. Solid State Ionics, 101-103, 1033-1040 (1997).
2. Whittle, D.P., Evans, D.J. and Scully, D.B. Compositional changes in the underlying alloy during the protective oxidation of alloys. Acta Metall., 15, 1421-1431 (1967).
3. Klöwer, J. Factors affecting the oxidation behaviour of thin FeCr-Al foils part 1: effects of foil dimensions. Mater. Corros., 49, 758-763 (1998).
4. Evans, H.E., Donaldson, A.T. and Gilmour, T.C. Mechanisms of breakaway oxidation and application to a chromia-forming steel. Oxidat. Met., 52(5/6), 379-402 (1999).
5. Gurappa, i., Weinbruch, S., Naumenko, D. and Quadakkers, W.J. Factors governing breakaway oxidation of FeCrAl based alloys. Mater. Corros., 51, 224-235 (2000).
6. Newton, R., Bennett, M.J., Wilber, J.P., Nicholls, J.R., Naumenko, D., Quadakkers, W.J., Al-Badairy, H., Tatlock, G., Strehl, G., Borchardt, G., Kolb-Telieps, A., Jönsson, B., Westerlund, A., Guttmann, V., Maier, M. and Beavan, P. The oxidation lifetime of commercial FeCrAl(RE) alloys. In: Schütze, M. and Quadakkers, W.J. (eds.), Lifetime Modelling of High Temperature Corrosion Processes, pp. 15-36. Maney Publishing, London (2001).
7. Cueff, R., Buscail, H., Caudron, E., Issartel, C. and Riffard, F. Influence of yttrium-alloying addition on the oxidation of alumina formers at 1173 K. Oxidat. Met., 58(5/6), 439-455 (2002).
8. Andrieu, E., Germidis, A. and Molins, R. High temperature oxidation of thin FeCrAl strips. Mater. Sci. Forum, 251-254, 357-364 (1997).
9. Quadakkers, W.J. and Bennett, M.J. Oxidation induced lifetime limits of thin walled, iron based, alumina forming, oxide dispersion strengthened alloy components. Mater. Sci. Technol., 10, 126-131 (1994).
10. Heeseman, A., Schmidtke, E., Faupel, F., Kolb-Telieps, A. and Klöwer, J. Aluminium and silicon diffusion in FeCrAl alloys. Scripta Mater., 40(5), 517-522 (1999).
11. Pragnell, W.M. and Evans, H.E. Predictions of solute depletion under corners and ribs during protective oxidation. In preparation.
12. Grabke, H.J. Oxidation of aluminides. Mater. Sci. Forum, 251-254, 149-162 (1997).
13. Naumenko, D., Quadakkers, W.J., Galerie, A., Wouters, Y. and Jourdain, S. Parameters affecting transient oxide formation on FeCrAl based foil and fibre materials. Mater. High Temp., 20(3), 287-293 (2003).
14. Liu, F., Josefsson, H., Svensson, J-E., Johansson, L-G. and Halversson, M. Microstructure of FeCrAl oxidized at the temperature range from 500 to 900°C. Microscopy of Oxidation 6, in press.