Oxidation of an inward grown aluminide diffusion coating studied using SEM and TEM

Materials at High Temperatures

Volumn 22, Issue 3-4, 2005, Pages 403-410

  Svensson, H ^a   Stiller, K ^a  

^a CHALMERS UNIVERSITY OF TECHNOLOGY   (Sweden)

Author keywords

Al2O3; Diffusion coating; FIB; Isothermal oxidation; NiAl; TEM; Voids

Indexed keywords

DIFFUSION COATINGS; ION BEAMS; METAL FOIL; OXIDATION; SCANNING ELECTRON MICROSCOPY; TRANSMISSION ELECTRON MICROSCOPY;

AL2O3; DIFFUSION COATING; FIB; ISOTHERMAL OXIDATION; NIAL; VOIDS;

ALUMINUM COMPOUNDS;

EID: 33745148967     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.047     Document Type: Article

References (35)

1. Doychak, J., Smialek, J.L. and Mitchell, T.E. Transient oxidation of single-crystal beta -NiAl. Metall. Trans., A 20A(3), 499-518 (1989).
2. Young, E.W.A. and de Wit, J.H.W. An /sup 18/O tracer study on the growth mechanism of alumina scales on NiAl and NiAlY alloys. Oxidat. Met., 26, 351 (1986).
3. 18O tracer and Rutherford backscattering spectrometry to study the oxidation mechanism of NiAl. Solid State Ionics, 16, 39 (1985).
4. 3. Oxidat. Met., 39(3-4), 167-95 (1993).
5. 3 scales using high-resolution imaging secondary ion mass spectrometry. Corrosion (Houston), 50(1), 62 (1994).
6. Svensson, H., Angenete, J. and Stiller, K. Microstructure of oxide scales on aluminide diffusion coatings after short time oxidation at 1050°C. Surf. Coat. Technol., 177-178, 152-157 (2004).
7. Yang, J.C., Schumann, E., Levin, I., Rüble, M. Transient oxidation of NiAl. Acta Mater., 46(6), 2195-201 (1998).
8. Schumann, E., Yang, J.C., Graham, M.J., Rüble, M. The effect of Y and Zr on the oxidation of NiAl. Mater. Corros., 47(11), 631-2 (1996).
9. Smialek, J.L. Oxide morphology and spalling model for NiAl. Metal. Trans., A (Phys. Metal. Mater. Sci.,) 9A(3), 309-20 (1978).
10. 3 on β-NiAl. J. Electrochem. Soc., 127, 1630 (1980).
11. Brumm, M.W. and Grabke, H.J. The oxidation behaviour of NiAl - II. Cavity formation beneath the oxide scale on NiAl of different stoichiometries. Corros. Sci., 34(4), 547-561 (1993).
12. Svensson, H., Stiller, K., and Angenete, J. Investigation of Oxide Formation during Short-Term Oxidation of Model NiAl Alloys. Mater. Sci. For., 461-464, 231-238 (2004).
13. 3 scale adhesion. Metal. Trans., A 22A(3), 739-52 (1991).
14. Funkenbusch, A.W., Smeggil, J.G. and Bornstein, N.S. Reactive element-sulfur interaction and oxide scale adherence. Metal. Trans., A (Phys. Metal. Mater. Sci.,) 16A(6), 1164-6 (1985).
15. Lees, D.G. On the reasons for the effects of dispersions of stable oxides and additions of reactive elements on the adhesion and growth-mechanisms of chromia and alumina scales-the 'sulfur effect'. Oxidat. Met., 27(1-2), 75-81 (1987).
16. Haynes, J.A., Pint, B.A., More, K.L., Zhang, Y. and Wright, I.G. Influence of sulfur, platinum, and hafnium on the oxidation behavior of CVD NiAl bond coatings. Oxidat. Met., 58(5-6), 513-44 (2002).
17. Hou, P.Y. and Priimak, K. Interfacial segregation, pore formation, and scale adhesion on NiAl alloys. Oxidat. Met., 63(1-2), 113 (2005).
18. Grabke, H.J., Wiemer, D. and Viefhaus, H. Segregation of sulfur during growth of oxide scales. Appl. Surf. Sci., 47(3), 243-50 (1991).
19. Angenete, J., Stiller, K. and Svensson, H. Preparation of TEM specimens from fragile oxide films using focused ion beam (FIB). Proc. 15th Int. Cong. Electron Microscopy (ICEM-15), 1, 265-266 (2002).
20. Langford, R.M. and Petford-Long, A.K. Preparation of transmission electron microscopy cross-section specimens using focused ion beam milling. J. Vac. Sci. Technol., Part A: Vac. Surf. Films, 19(5), 2186 (2001).
21. Angenete, J. and Stiller, K. Comparison of inward and outward grown Pt modified aluminide diffusion coatings on a Ni based single crystal superalloy. Surf. Coat. Technol., 150(2-3), 107-118 (2002).
22. Merchant, S.M. and Notis, M.R. A review: Constitution of the Al-Cr-Ni system. Mater. Sci. Engng., 66(1), 47-60 (1984).
23. Angenete, J., Stiller, K. and Bakchinova, E. Microstructural and microchemical development of simple and Pt-modified aluminide diffusion coatings during long term oxidation at 1,050°C. Surf. Coat. Technol., 176(3), 272-283 (2004).
24. 3Al cross sections. Oxidat. Met., 31(5-6), 431-52 (1989).
25. Grabke, H.J. Oxidation of NiAl and FeAl. Intermetallics, 7(10), 1153-8 (1999).
26. Zimmermann, D., Tolpygo, V.K., Rüble, M. ands Clarke, D.R. The role of oxidation-induced cavities on the failure of the thermally grown oxide on binary β-NiAl alloys. Z. Metallk., 94(3), 157-62 (2003).
27. van Manen, P. The mechanism of the oxidation of nickel aluminium coating alloys, TU Delft: Delft (1991).
28. 3 Scales: Void Growth, Grain Growth, and Scale Growth. In: High Temperature Corrosion. San Diego, CA, USA: NACE, Houston, TX, USA (1983).
29. Zhang, Y., Allen Haynes, J., Lee, W.Y., Wright, I.G., Pint, B.A., Cooley, K.M. and Liaw, P.K. Effects of Pt incorporation on the isothermal oxidation behavior of chemical vapor deposition aluminide coatings. Metal. Mater. Trans., A (Phys. Metal. Mater. Sci.) 32A(7), 1727-41 (2001).
30. Allen Haynes, J. Potential influences of bond coat impurities and void growth on premature failure of EB-PVD TBCs. Scr. Mater., 44(7), 1147-52 (2001).
31. 3 Scales Formed on NiCrAl Alloys, in Lewis Research Center Cleveland, Ohio (1981).
32. Zimmermann, D., Bobeth, M., Rühle, M. and Clarke, D.R. Oxidation-induced cavity formation in binary β-NiAl alloys. Z. Metallk., 95(2), 84-90 (2004).
33. Brumm, M.W. and Grabke, H.J. The oxidation behaviour of NiAl-I. Phase transformations in the alumina scale during oxidation of NiAl and NiAlCr alloys. Corros. Sci., 33(11), 1677-1690 (1992).
34. Grabke, H.J., Brumm, M.W. and Wagemann, B. The oxidation of NiAl. Mater. Corros., 47(12), 675-7 (1996).
35. Budnikov, P.P. and Ginstling, A.M. Principles of Solid State Chemistry. Translated from Russian, Gordon and Brech Sci. Pub. (1968).