Volumn 13, Issue 7, 2006, Pages 1057-1064

Comparison on the cracking susceptibility of different low alloy steel weldments exposed to the environment containing wet H2S

Author keywords

Environmental cracking; HIC; SSCC; SSRT; Wet H2S

Indexed keywords

BRITTLE FRACTURE; FRACTURE TOUGHNESS; OPTICAL MICROSCOPY; SCANNING ELECTRON MICROSCOPY; STEEL; STRAIN RATE; TENSILE TESTING;

EID: 33646566529     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2005.07.009     Document Type: Article
Times cited : (30)

References (15)
  • 1
    • 0001029973 scopus 로고
    • Occurrence and prevention of hydrogen induced stepwise cracking and stress corrosion cracking of low alloy pipeline steels
    • Herbsleb G., Poepperling R.K., and Schwenk W. Occurrence and prevention of hydrogen induced stepwise cracking and stress corrosion cracking of low alloy pipeline steels. Corrosion 36 5 (1981) 247-256
    • (1981) Corrosion , vol.36 , Issue.5 , pp. 247-256
    • Herbsleb, G.1    Poepperling, R.K.2    Schwenk, W.3
  • 2
    • 0021231035 scopus 로고
    • Hydrogen induced cracking in pipeline steels
    • Brown A., and Jones C.L. Hydrogen induced cracking in pipeline steels. Corrosion 40 7 (1984) 330-336
    • (1984) Corrosion , vol.40 , Issue.7 , pp. 330-336
    • Brown, A.1    Jones, C.L.2
  • 3
    • 0024088426 scopus 로고
    • LPG storage vessel cracking experience
    • Cantwell J.E. LPG storage vessel cracking experience. Mater Perf 10 (1988) 79-82
    • (1988) Mater Perf , vol.10 , pp. 79-82
    • Cantwell, J.E.1
  • 5
    • 84996260632 scopus 로고
    • Role of elonged MnS inclusions in hydrogen embrittlement of high-strength steel
    • Venkatasubramanian T.V., and Baker T.J. Role of elonged MnS inclusions in hydrogen embrittlement of high-strength steel. Met Sci 116 12 (1982) 543-554
    • (1982) Met Sci , vol.116 , Issue.12 , pp. 543-554
    • Venkatasubramanian, T.V.1    Baker, T.J.2
  • 6
    • 0021494415 scopus 로고
    • Resistance of line pipe steels to wet sour gas
    • Taira T., Kobayashi Y., Matsumoto K., et al. Resistance of line pipe steels to wet sour gas. Corrosion 40 9 (1984) 478-486
    • (1984) Corrosion , vol.40 , Issue.9 , pp. 478-486
    • Taira, T.1    Kobayashi, Y.2    Matsumoto, K.3
  • 7
    • 0035241897 scopus 로고    scopus 로고
    • Influence of sulphur content and inclusion distribution on hydrogen induced blister cracking in pressure vessel and pipeline steels
    • Domizzi G., Anteri G., and Ovejero-García J. Influence of sulphur content and inclusion distribution on hydrogen induced blister cracking in pressure vessel and pipeline steels. Corros Sci 43 (2001) 325-339
    • (2001) Corros Sci , vol.43 , pp. 325-339
    • Domizzi, G.1    Anteri, G.2    Ovejero-García, J.3
  • 8
    • 0023597169 scopus 로고
    • The application of the slow strain rate test method for the development of linepipe steels resistant to sulphide stress cracking
    • Margot-Marette H., Bardou G., and Charbonnier J.C. The application of the slow strain rate test method for the development of linepipe steels resistant to sulphide stress cracking. Corros Sci 27 10/11 (1987) 1009-1026
    • (1987) Corros Sci , vol.27 , Issue.10-11 , pp. 1009-1026
    • Margot-Marette, H.1    Bardou, G.2    Charbonnier, J.C.3
  • 9
    • 0037997609 scopus 로고    scopus 로고
    • Performance of welded high-strength low-alloy steels in sour environments
    • Omweg G.M., Frankel G.S., Bruce W.A., et al. Performance of welded high-strength low-alloy steels in sour environments. Corrosion 59 7 (2003) 640-653
    • (2003) Corrosion , vol.59 , Issue.7 , pp. 640-653
    • Omweg, G.M.1    Frankel, G.S.2    Bruce, W.A.3
  • 11
    • 0023534749 scopus 로고
    • The resistance of welded linepipes to sulfide stress cracking
    • Kobayashi Y., Ume K., Hyodo T., et al. The resistance of welded linepipes to sulfide stress cracking. Corros Sci 27 10/11 (1987) 1117-1135
    • (1987) Corros Sci , vol.27 , Issue.10-11 , pp. 1117-1135
    • Kobayashi, Y.1    Ume, K.2    Hyodo, T.3
  • 12
    • 0028448821 scopus 로고
    • The influences of microstructure and composition on the electrochemical behavior of A516 steel weldment
    • Huang H.-H., Tsai W.-T., and Lee J.-T. The influences of microstructure and composition on the electrochemical behavior of A516 steel weldment. Corros Sci 36 6 (1994) 1027-1038
    • (1994) Corros Sci , vol.36 , Issue.6 , pp. 1027-1038
    • Huang, H.-H.1    Tsai, W.-T.2    Lee, J.-T.3
  • 13
    • 0023535193 scopus 로고
    • On the evaluation method of sulfide stress cracking susceptibility of carbon and low alloy steels
    • Ikeda A., Kaneko T., and Ando Y. On the evaluation method of sulfide stress cracking susceptibility of carbon and low alloy steels. Corros Sci 27 10/11 (1987) 1099-1115
    • (1987) Corros Sci , vol.27 , Issue.10-11 , pp. 1099-1115
    • Ikeda, A.1    Kaneko, T.2    Ando, Y.3
  • 14
    • 33646549161 scopus 로고
    • Susceptibility of conventional pressure vessel steel to hydrogen-induced cracking and stress-oriented hydrogen-induced cracking in hydrogen sulfide-containing diglycolamine solutions
    • Al-Anezi M.A., Frankel G.S., and Agrawal A.K. Susceptibility of conventional pressure vessel steel to hydrogen-induced cracking and stress-oriented hydrogen-induced cracking in hydrogen sulfide-containing diglycolamine solutions. Corrosion 50 11 (1994) 1101-1109
    • (1994) Corrosion , vol.50 , Issue.11 , pp. 1101-1109
    • Al-Anezi, M.A.1    Frankel, G.S.2    Agrawal, A.K.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.