Use of ACR method to estimate closure and residual stress free small crack growth data

ASTM Special Technical Publication

Volumn , Issue 1461, 2005, Pages 60-72

  Zonker, H R ^a   Bray, G H ^a   George, K ^b   Garratt, M D ^a  

^a ALCOA TECHNICAL CENTER   (United States)

^b LEHIGH UNIVERSITY   (United States)

Author keywords

Adjusted compliance ratio; Crack closure; Crack propagation; Effective stress intensity; Fatigue; Fatigue threshold; Residual stress

Indexed keywords

CORROSION; DATA ACQUISITION; FATIGUE OF MATERIALS; RESIDUAL STRESSES;

CRACK CLOSURE; EFFECTIVE STRESS INTENSITY; FATIGUE THRESHOLD;

CRACK PROPAGATION;

EID: 33244468363     PISSN: 00660558     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp11486s     Document Type: Conference Paper

References (14)

1. max ΔK-Decreasing Fatigue Crack Growth Procedures," Small-Crack Test Methods, ASTMSTP1149, J. M. Larsen and J. E. Allison, Eds., ASTM International, West Conshohocken, PA, 1992, pp. 197-200.
2. Donald, J. K., "A Procedure for Standardizing Crack Closure Levels," Mechanics of Fatigue Crack Closure, ASTM STP 982, J. C. Newman, Jr. and W. Eiber, Eds., ASTM International, West Conshohocken, PA, 1988, pp. 222-229.
3. th National Symposium on Fatigue and Fracture Mechanics, ASTMSTP 1332, T. L. Panontin and S. D. Sheppard, Eds., ASTM International, West Conshohocken, PA, 1997.
4. th Volume, ASTM STP 1360, P. C. Paris and K. L. Jerina, Eds., ASTM International, West Conshohocken, PA, West Conshohocken, PA, 1999, pp. 388-402.
5. max from Closure-Related Stress Ratio Effects Using the Adjusted Compliance Ratio Technique," Advances in Fatigue Crack Closure Measurements and Analysis: Second Volume, ASTMSTP 1343, R. C. McClung and J. C. Newman, Jr., Eds., ASTM International, West Conshohocken, PA, 1999, pp. 57-78
6. Chen, D. L., Weiss, B., and Stickler, R., "Contribution of the Cyclic Loading Portion Below the Opening Load to Fatigue Crack Growth," Materials Science and Engineering, Vol. A208, 1996, pp. 181-187.
7. Donald, J. K., "Introducing the Compliance Ratio Concept for Determining Effective Stress Intensity," International Journal of Fatigue, Vol. 19, Suppl. No. 1, 1997, pp. 191-195.
8. Donald, J. K. and Phillips, E. P., "Analysis of Second ASTM Round Robin Program on Opening Load Measurement Using the Adjusted Compliance Ratio Technique," Advances in Fatigue Crack Closure Measurement and Analysis: Second Volume, ASTM STP 1343, R. C. McClung and J. C. Newman, Jr., Eds., ASTM International, West Conshohocken, PA, 1997.
9. McClung, R. C., Davidson, D. L., "Near Tip and Remote Characterization of Plasticity Induced Fatigue Crack Closure," Advances in Fatigue Crack Closure Measurement and Analysis, ASTMSTP 1343, R. C. McClung and J. C. Newman, Jr., Eds., ASTM International, West Conshohocken, PA, 1999, pp. 106-127.
10. th Volume, ASTMSTP 1360, K. L. Jerina and P. C. Paris, Eds., ASTM International, West Conshohocken, PA, 1999.
11. George, K., Reemsynder, H. S., Donald, J. K., and Bucci, R. J., "Development of a Corner-Notched, Open Hole Specimen for Material Evaluation," Fatigue Testing and Analysis Under Variable Amplitude Loading Conditions, ASTM STP 1439, P. C. McKeighan and N. Ranganathan, Eds., ASTM International, West Conshohocken, PA, 2002.
12. th Conference), ASTM STP 743, ASTM International, West Conshohocken, PA, 1981, pp. 28-47.
13. Bush, R. W., Bucci, R. J., Magnusen, P. E., and Kuhlman, G. W., "Fatigue Crack Growth Rate Measurements in Aluminum Alloy Forgings: Effects of Residual Stress and Grain Flow," Fracture Mechanics: Twenty-Third Symposium, ASTM STP 1189, Ravinder Chona, Ed., ASTM International, West Conshohocken, PA, 1993, pp. 568-589.
14. Pearson, S., "Initiation of Fatigue Cracks in Commercial Aluminum Alloys and the Subsequent Propagation of Very Short Cracks," Engineering Fracture Mechanics, Vol. 7, No. 2, 1975, pp. 235-247.