Stress corrosion cracking and hydrogen-induced cracking of an alumina ceramic

Journal of the American Ceramic Society

Volumn 88, Issue 2, 2005, Pages 353-356

  Shi, B ^a   Chu, W Y ^a   Su, Y J ^a   Gao, K W ^a   Qiao, L J ^a  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINA; CERAMIC MATERIALS; HYDROGEN; STRESS INTENSITY FACTORS;

ALUMINA CERAMIC; HYDROGEN-INDUCED CRACKING (HIC); THRESHOLD STRESS INTENSITY;

STRESS CORROSION CRACKING;

EID: 29744465867     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1551-2916.2005.00052.x     Document Type: Article

References (11)

1. C. P. Chen and W. J. Knapp, "Delayed Fracture of an Alumina Ceramic," J. Am. Ceram. Soc., 60, 87 (1977).
2. J. E. Ritter and J. N. Humenik, "Static and Dynamic Fatigue of Polycrystalline Alumina," J. Mater. Sci., 14, 626-32 (1979).
3. T. Okabe, M. Kido, and T. Miyahara, "Fatigue Fracture Behavior of Oxide Ceramics in Water," Eng. Fract. Mech., 48, 1373-46 (1994).
4. T. A. Michalske and S. W. Freiman, "A Molecular Mechanism for Stress Corrosion in Vitreous Silica," J. Am. Ceram. Soc., 66, 284-8 (1983).
5. H. H. Yu and Z. Suo, "Delayed Fracture of Ceramics Caused by Stress-Dependent Surface Reaction," Acta Mater., 47, 77-86 (1999).
6. C. Chen, "The Stress Intensity Factor for Some Samples," Novel Metal Mater. (Chinese), 11, 145-56 (1975).
7. G. W. Yu, L. J. Qiao, Y. B. Wang, and W. Y. Chu, "Hydrogen Accumulation and Hydrogen-Induced Cracking of API C90 Tubular Steel," Corrosion. 53, 762-9 (1997).
8. 3-Based Semiconducting Ceramics," J. Mater. Sci. Lett., 17, 899-900 (1998).
9. W. Chen, L. Li, Y. Wang, and Z. Gui, "Effect of Electrochemical Hydrogen Charging on Lead-Based Relaxor Ferroelectric Multilayer Ceramic Capacitors," J. Mater. Res., 13, 1110-2 (1998).
10. W. Y. Chu, C. M. Hsiao, and Y. Z. Zhao, "Corrosion Fatigue Crack Initiation in a Mode II Notch Specimen," Metall. Trans. A, 19A, 1067-73 (1988).
11. W. Y. Chu, L. J. Qiao, Y. B. Wang, and Y. W. Zheng, "Quantitative Study for Sulfide Stress Corrosion Cracking of Tubular Steel," Corrosion, 55, 667-73 (1999).