Hydrogen Accumulation and Hydrogen-Induced Cracking of API C90 Tubular Steel

Corrosion (Houston)

Volumn 53, Issue 10, 1997, Pages 762-769

  Yu, G H ^a   Cheng, Y H ^a   Chen, L ^a   Qiao, L J ^a   Wang, Y B ^a   Chu, W Y ^a  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

API C90 tubular steel; Blistering; Grain boundary; Hydrogen induced cracking; Inclusions; SM90 steel SM95 steel; Stress; Stress intensity; Sulfide stress cracking; Tubular steel

Indexed keywords

EID: 0001318853     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3290260     Document Type: Article

References (13)

1. G.J. Biefer, MP 21 (1982): p. 19.
2. J.P. Hirth, Metall. Trans. 11A (1980): p. 861.
3. R.N. Merrick, MP 28 (1989): p. 53.
4. R.W. Revie, V.S. Sastri, G.R. Hoey, R.R. Ramsingh, D.K. Mak, M.T. Shehata, Corrosion 49 (1993): p. 17.
5. S. Ochiai, S. Yoshinaga, Y. Kikuta, Trans. ISIJ 15 (1975): p. 503.
6. S. Wu, L. Chen, Acta. Metall. Sin. 3A (1990): p. 312.
7. M. Smialowski, Hydrogen in Steel (New York, NY: Pergamon Press, 1962), p. 64.
8. M.A.V. Devanathan, Z. Stachursky, Proc. Roy. Soc. 270A (1962): p. 90.
9. M. Creager, P.C. Paris, Int. J. Fract. Mech. 4 (1967): p. 247.
10. W.Y. Chu, J. Yao, C.M. Hsiao, Metall. Trans. 15A (1984): p. 729.
11. W.Y. Chu, C.M. Hsiao, J.W. Wang, Metall. Trans. 16A (1985): p. 1,663.
12. T.Y. Zhang, W.Y. Chu, C.M. Hsiao, Metall. Trans. 16A (1985): p. 1,665
13. W.W. Gerberich, J. Garry, J.F. Lessar, "Grain Size and Concentration Effects In Internal and External Hydrogen Embrittlement," in Effect of Hydrogen on Behavior of Materials, eds. I.M. Bernstein, A.W. Thompson (New York, NY: AIME, 1986), p. 70.