Corrosion of reinforcement in relation to presence of defects at the interface between steel and concrete

Journal of Materials in Civil Engineering

Volumn 17, Issue 4, 2005, Pages 447-455

  Soylev T A ^a   Francois R ^b  

^a ISTANBUL KULTUR UNIVERSITY   (Turkey)

^b INSA   (France)

Author keywords

Compaction; Concrete; Corrosion; Interfaces; Reinforcement; Steel

Indexed keywords

BARS (METAL); COMPACTION; CONCRETE REINFORCEMENTS; CONCRETES; DEFECTS; INSPECTION; INTERFACES (MATERIALS); POROSITY; STEEL;

BLEEDING; INDUCE CORROSION; INTERFACE QUALITY; MACRODEFECTS; MICRODEFECTS; SETTLEMENT; STEEL-CONCRETE INTERFACE DEFECTS;

STEEL CORROSION;

CORROSION;

EID: 25444510056     PISSN: 08991561     EISSN: None     Source Type: Journal    
DOI: 10.1061/(ASCE)0899-1561(2005)17:4(447)     Document Type: Article

References (27)

1. Andrade, C., and Alonso, C. (1996). "Corrosion rate monitoring in the laboratory and on-site." Constr. Build. Mater., 10(5), 315-328.
2. Arya, C., and Xu, Y. (1995). "Effect of cement type on chloride binding and corrosion of steel in concrete." Cem. Concr. Res., 25(4), 893-902.
3. Cao, H. T., and Sirivivatnanon, V. (1991). "Corrosion of steel in concrete with and without silica fume." Cem. Concr. Res., 21(2-3), 316-324.
4. Cao, J., and Chung, D. D. L. (2001). "Degradation of the bond between concrete and steel under cyclic shear loading, monitored by contact electrical measurement." Cem. Concr. Res., 31, 669-671.
5. Castel, A., François, R., and Arliguie, G. (2000). "Factors other than chloride level influencing corrosion rate of reinforcement." Proc., CANMET/ACI Durability of Concrete, V. M. Malhotra, ed., American Concrete Institute, Detroit, 629-644.
6. Gjorv, O. E., Monteiro, P. J. M., and Mehta, P. K. (1990). "Effect of condensed silica fume on the steel-concrete bond." ACI Mater. J., 87(6), 573-580.
7. Glass, G. K., Reddy, B., and Buenfeld, N. R. (2000). "Corrosion inhibition in concrete arising from its acid neutralization capacity." Corros. Sci., 42, 1587-1598.
8. Hamad, B. S., and Itani, M. S. (1998). "Bond strength of reinforcement in high-performance concrete: The role of silica fume, casting position, and superplasticizer dosage." ACI Mater. J., 95(5), 499-511.
9. Khayat, K. H. (1998a). "Viscosity-enhancing admixtures for cement-based materials - an overview." Cem. Concr. Compos., 20, 171-188.
10. Khayat, K. H. (1998b). "Use of viscosity-modifying admixture to reduce top-bar effect of anchored bars cast with fluid concrete." ACI Mater. J., 95(2), 158-167.
11. Khayat, K. H. (1999). "Workability, testing, and performance of self-consolidating concrete." ACI Mater. J., 96, 346-353.
12. Khayat, K. H., Vachon, M., and Lanctot, M. C. (1997). "Use of blended silica fume in commercial concrete mixtures." ACI Mater. J., 94(3), 119-131.
13. Kosmatka, S. H. (1994). "Bleeding, significance of tests, and properties of concrete and concrete making material." Proc., Special Publication STP 169 C, ASTM, West Conshohocken, Pa., 88-111.
14. Lambert, P. L., Page, C. L., and Vassie, P. R. W. (1991). "Investigations of reinforcement corrosion. 2: Electrochemical monitoring of steel in chloride-contaminated concrete." Mater. Struct., 24, 351-358.
15. Lorentz, T., and French, C. (1995). "Corrosion of reinforcing steel in concrete: Effects of materials, mix composition, and cracking." ACI Mater. J., 92(2), 181-190.
16. Millard, S. G., Law, D., Bungey J. H., and Cairns, J. (2001). "Environmental influences on linear polarization corrosion rate in reinforced concrete." NDT & E Int., 34, 409-417.
17. Mohammed, T. U., and Hamada, H. (2001). "Discussion of 'Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar,' by C. Alonso, C. Andrade, M. Castellote, and P. Castro." Cem. Concr. Res., 31, 835-838.
18. Mohammed, T. U., Otsuki, N., Hamada, H., and Yamaji, T. (2002). "Chloride-induced corrosion of steeel bars in concrete with presence of gap at the steel-concrete interface." ACI Mater. J., 99(2), 149-156.
19. Mohammed, T. U., Otsuki, N., and Hisada, M. (1999). "Corrosion of steel bars with respect to orientation in concrete." ACI Mater. J., 96(2), 154-159.
20. Nilsson, L. O., Poulsen, E., Sandberg, P., Sørensen, H. E., and Klinghoffer, O. (1996). "Chloride penetration into concrete state of art." HETEK Rep. No. 53, Danish Road Directorate, Copenhagen, Denmark.
21. Page, C. L. (1975). "Mechanism of corrosion protection in reinforced concrete marine structures." Nature (London), 258(11), 514-515.
22. Page, C. L., Al Khalaf, M. N., and Ritchie, A. G. B. (1978). "Steel/ mortar interfaces: Mechanical characteristics and electrocapillarity." Cem. Concr. Res., 8, 481-490.
23. Page, C. L., and Treadaway, K. W. J. (1982). "Aspects of the electrochemistry of steel in concrete." Nature (London), 297, 109-115.
24. Page, C. L., and Vennesland, Ø. (1983). "Pore solution composition and chloride binding capacity of silica-fume cement pastes." Mater. Struct., 16(91), 19-25.
25. Petrov, N. (1998). "Etude des propriétés d'un béton autonivelant in situ et de leurs influences sur I'interface béton-armature." MS thesis, Université de Sherbrooke, Sherbrooke, Canada.
26. Suryavanshi, A. K., Scantlebury, J. D., and Lyon, S. B. (1988). "Corrosion of reinforcement steel embedded in high water-cement ration concrete contaminated with chloride." Cem. Concr. Compos., 20, 263-281.
27. Yonezawa, T., Ashworth, V., and Procter, R. P. M. (1988). "Pore solution composition and chloride effects on the corrosion of steel in concrete." Corros. Eng., 44(7), 489-499.